Fibrous Structure Formation in Cold-Drawing of Polyethylene

Abstract

Rods of spherulitic, linear polyethylene were cold-drawn at 60 and 100°C and the morphology of the drawn material, particularly the necked portion, was characterized by light and electron microscopy and by wide- and small-angle x-ray scattering. The drawing proceeded by neck formation and propagation at a draw ratio of 10. Further extension or creep beyond the neck produced draw ratios up to 20. Neck formation was characterized by spherulites deforming essentially in concert with the macroscopic deformation, becoming elongated and oriented and, thereby, defining a gross fibrous structure.

Very early in the process of neck formation, small disruptions appeared within the spherulites. Similar to crazes in amorphous materials, these disruptions measured a few microns long, perpendicular to the direction of deformation, and a fraction of a micron thick. The disruptions increased in size and number as drawing progressed, dominated the structure at the higher draw ratios, and oriented to define a fine, fibrillar structure. These observations are contrasted with the rather different results obtained in an earlier, similar study of the cold-drawing of nylon 66.

Keywords

Marlex 6050(TN)polyethylene. Crystallized polyethylene. Temperature pressure time draw ratio load length extension rate. Spherulites neck formation neck propagation disruptions macroscopic deformation. Fibrous structure. Instron tensile tester crystallization cold-drawing light microscopy electron microscopy.

Get full access to this article

View all access options for this article.

References

Balta-Calleja, F.J. and Peterlin, A. , The Limiting Axial Long Period of Drawn Polypropylene , J. Polymer Sci. A2, 7, 1275-1278 (1969 ).

Balta-Calleja, F.J. and Peterlin, A. , Plastic Deformation of Polypropylene II. The Influence of Temperature and Draw Ratio on the Axial Long Period, J. Materials Sci. 4, 722-729 (1969).

Corneliussen, R. and Peterlin, A. , The Influence of Temperature on the Plastic Deformation of Polyethylene, Makromol. Chem. 105, 192-203 (1967).

Corneliussen, R. and Peterlin, A. , Small-Angle X-ray Diffraction Studies of Plastically Deformed Polyethylene. II. Influence of Draw Ratio, Annealing, Temperature, and Time, J. Polymer Sci. A2, 6, 1273-1282 (1968 ).

Crystal, R.G. and Hansen, D. , Morphology of Cold-Drawn Nylong 66, J. Polymer Sci. A2, 6, 981-993 (1968).

Geil, P.H. , Polymer Deformation. II. Drawing of Single Crystals, J. Polymer Sci. A2, 3813-3834 (1964 ).

Hay, I.L. and Keller, A. , Polymer Deformation in Terms of Spherulites, Kolloid Z.-Z. Polymer 204, 43-74 (1965).

Ingram, P. , Kiho, H. , and Peterlin, A. , Electron Diffraction and Microscopy of Deformed Polymer Crystals. III. Annealing, Polymer 7, 135-149 (1966).

Jellinek, M.H. , Solomon, E. , and Fankuchen, I. , Size Distributions From Small-Angle X-ray Scattering, Ind. Eng. Chem., Anal. Ed. 18, 172-181 (1946).

10.

Kiho, H. , Peterlin, A. , and Geil, P.H. , Polymer Deformation. VI. Twinning and Phase Transformation of Polyethylene Single Crystals as a Function of Stretching Direction, J. Appl. Phys. 35, 1599-1605 (1964).

11.

Kiho, H. , Peterlin, A. , and Geil P.H. , Polymer Deformation. IX. Deformation of Polyethylene Crystals at Large Strain , Polymer Letters 3, 257-269 (1965).

12.

Peterlin, A. , Crystalline Character in Polymers, J. Polymer Sci., C, 9, 61-89 (1965).

13.

Peterlin, A. , Ingram, P. , and Kiho, H. , Electron Diffraction and Microscopy of Deformed Polymer Crystals. II. Fibers, Makromol. Chem. 86, 294-297 (1965).

14.

Peterlin, A. and Sakaoku, K. , Electron Microscopy of Drawn Polyethylene, KoUoid Z.-Z. Polymere 212, 51-53 (1966).

15.

Peterlin, A. , Plastic Deformation of Polyethylene, Mechanism and Properties, J. Polymer Sci. C, 15, 427-443 (1966).

16.

Peterlin, A. and Sakaoku, K. , Surface Replicas of Drawn Polyethylene. III. The Morphology of Drawing with Neck Formation , J. Appl. Phys. 38, 4152-4164 (1967 ).

17.

Peterlin, A. , Folded-Chain Concept of Fiber Structure, KoUoid Z.-Z. Polymere 216, 129-136 (1967).

18.

Peterlin, A. , Folded-Chain Model of Highly Drawn Polyethylene , Polymer Eng. Sci. 9, 172-181 (1969).

19.

Peterlin, A. and Balta-Calleja , F.J. , Plastic Deformation of Polypropylene. III. Small-Angle X-ray Scattering in the Neck Region, J. Appl. Phys 40, 4238-4242 (1969 )

20.

Sakaoku, K. and Peterlin, A. , Surface Replicas of Drawn Polyethylene. II. Annealing of Cold-Drawn Samples with Different Draw Ratios, J. Macromol. Sci. B1, 103-118 (1967).

21.

Samuels, R.J. , Morphology of Deformed Polypropylene. Quantitative Relations by Combined X-ray, Optical and Sonic Methods, J. Polymer Sci. A, 3, 1741-1763 (1965).

22.

Samuels, R.J. , Spherulite Structure , Deformation Morphology , and Mechanical Properties of Isotactic Polypropylene Fibers, J. Polymer Sci. C, 20, 253-284 (1967).

23.

Samuels, R.J. , Quantitative Characterization of Deformation in Polypropylene Fibers, J. Polymer Sci. A2, 6, 2021-2041 (1968 ).

24.

Statton, W.O. , Microvoids in Fibers as Studied by Small-Angle Scattering of X-rays, J. Polymer Sci. 58, 205-220 (1962).