This study aimed to produce fabrics by the digital light processing (DLP) three-dimensional (3D) printing technology and using a polyurethane acrylate photopolymer as the printing material. The effect of the acrylate oligomer concentration on printing was evaluated. The DLP 3D printing conditions, such as the curing time and layer thickness, were controlled considering the physical properties, such as the tensile strength, elongation, and crease recovery of the 3D printed material. The optimal printing conditions were as follows: concentration of acrylate oligomer in the photopolymer: 10% (v/v); curing time per layer: 14 s; and layer thickness: 100 µm. These results are expected to guide further studies on the development of fabrics using DLP 3D printing technology.
ConnerBPManogharanGPMartofAN, et al.Making sense of 3-D printing: creating a map of additive manufacturing products and services. Addit Manuf2014; 1: 64–76.
AvincOYildirimFfYavasA, et al.3D printing technology and its influences on the textile industry. IJIEEE2017; 5: 37–42.
4.
BeecroftM. 3D printing of weft knitted textile based structures by selective laser sintering of nylon powder. IOP Conf Ser Mater Sci Eng2016; 137: 012017–012017.
5.
SpahiuTGrimmelsmannNEhrmannA, et al.Effect of 3D printing on textile fabric. ICEE2017; 1: 1–6.
6.
LeeJSJinS. Study on fashion design using DLP 3D printing. Bull Kor Soc Basic Des Art2017; 18: 449–460.
7.
LeeJSHuhJS. Study of textile structure using 3D printing - focused on the comparison of FDM and DLP. Kor Sci Art For2017; 3: 331–340.
8.
VanderploegALeeSMampM. The application of 3D printing technology in the fashion industry. J Fash Des Technol Educ2017; 10: 170–179.
9.
Jasveer S and Jianbin X. Comparison of different types of 3D printing technologies. Int J Sci Res 2018; 8.
10.
Wang X, Jiang M, Zhou Z, et al. 3D printing of polymer matrix composites: a review and prospective. Compos B Eng 2017; 110: 442–458.
11.
GeLDongLWangD, et al.A digital light processing 3D printer for fast and high-precision fabrication of soft pneumatic actuators. Sens Actuator A2018; 273: 285–292.
VoetVSDStratingTSchneltingGHM, et al.Biobased acrylate photocurable resin formation for stereolithography 3D printing. ACS Omega2018; 3: 1403–1408.
14.
DizonJRCEsperaAHChenQ, et al.Mechanical characterization of 3D-printed polymers. Addit Manuf2017; 20: 44–67.
15.
PatelDKSakhaeiAHLayaniM, et al.Highly stretchable and UV curable elastomers for digital light processing based 3D printing. Adv Mater2016; 29: 1606000–1606000.
16.
DawoudMTahaIEbeidSJ. Mechanical behavior of ABS: an experimental study using FDM and injection moulding techniques. J Manuf Process2016; 21: 39–45.
17.
Sun D and Valtasa A. 3D printing in modern fashion industry. JTFT 2019; 2: 1–4.
18.
MelnikovaREhrmannAFinsterbuschK. 3D Printing of textile-based structures by fused deposition modelling (FDM) with different polymer materials. IOP Conf Ser Mater Sci Eng2014; 62: 012018–012018.
19.
Steyrer B, Neubauer P, Liska R, et al. Visible light photoinitiator for 3D-printing of tough methacrylate resins. Materials 2017; 10: 1445.
20.
LeeIYLeeYJ. Effect of accuracy and tensile strength by laser velocity parameter & post(curing) process in stereolithography type of 3D printing. JKSPE2017; 2017: 768–769.
21.
SimJLeeEKweonH. Effect of the laser beam size on the cure properties of a photopolymer in stereo lithography. Int J Precis Eng Manuf2017; 8: 50–55.
22.
StampflJBaudisSHellerC, et al.Photopolymers with tunable mechanical properties processed by laser-based high-resolution stereolithography. J Micromech Microeng2008; 18: 125014–125014.
23.
ChenXQiuK. Synthesis of well-defined poly (methyl methacrylate) by radical polymerization with a new initiation system TPED/FeCl3/PPh3. Macromolecules1999; 32: 8711–8715.
24.
VoitBILedererA. Hyperbranched and highly branched polymer architectures—synthetic strategies and major characterization aspects. Chem Rev2009; 109: 5924–573.
25.
KimSHChangHSParkSH, et al.Study on the curing properties of photo-curable acrylate resins. Polymer (Korea)2010; 34: 469–473.
26.
ZhangJXiaoP. 3D printing of photopolymers. Polym Chem2018; 9: 1530–1540.
27.
Mu X. Photomechanics of polymers and its applications to active structures and additive manufacturing. PhD Thesis, Georgia Institute of Technology, Atlanta, USA, 2017.
28.
OhSHChoBJJeongMS, et al.Evaluation of the isothermal curing process of UV-cured resin in terms of elasticity studied through micro-Brillouin light scattering. J Soc Inf Display2016; 17: 87–91.