Multifunctional textiles combining ultraviolet protection, thermal insulation and superhydrophobic and aromatic performance were successfully prepared using an aluminum-doped zinc oxide (AZO)-embedded lemon microcapsule and SiO2 dual-layer coating. AZO-loaded lemon microcapsules with average diameter of 1.5 µm were obtained via interfacial polymerization. Results showed that the high concentration of the AZO-embedded lemon microcapsule contributed to enhancing the waterproof property, aromatic performance, and visible and near-infrared light transmittance. The lemon content was up to 2.789 mg/g (weight of essence:weight of fabric). The water contact angle was high at 153.35°, exhibiting an outstanding superhydrophobic performance. The light transmittance decreased as the amount of AZO-embedded lemon microcapsule increased. The ultraviolet protection factor value reached 88.78 when the dosage of the AZO-embedded lemon microcapsule was 6%. Given the above research results, the cotton fabric coated with the AZO-embedded lemon microcapsule and SiO2 dual-layer composite coating would have potential applications in the water/oil purification field and functional protective fabrics.
TimothyRPragasamAJA. Effect of weave structures and zinc oxide nanoparticles on the ultraviolet protection of cotton fabrics. Fibres Text East Eur2018; 26: 113–119.
2.
WyszeckiGStilesWS. Color science: Concepts and methods, quantitative data and formulae, 2nd ed. New York: John Wiley and Sons, Inc., 2000.
3.
MohaddesFIslamSShanksR, et al.Modification and evaluation of thermal properties of melamine-formaldehyde/n-eicosane microcapsules for thermal-regulation applications. Appl Therm Eng2014; 71: 11–15.
4.
LuXMSunYTChenZ, et al.A multi-functional textile that combines self-cleaning, water-proofing and VO2-based temperature-responsive thermoregulating. Sol Energ Mat Sol C2017; 159: 102–111.
5.
HuangMHMaoSFeickH, et al.Room-temperature ultraviolet nanowire nanolasers. Science2001; 292: 1897–1899.
6.
YangYNZhaoJHCuiC, et al.Hydrothermal growth of ZnO nanowires scaffolds within mesoporous TiO2 photoanodes for dye-sensitized solar cells with enhanced efficiency. Electrochim Acta2016; 196: 348–356.
7.
LuoYSYangJPDaiXJ, et al.Preparation and optical properties of novel transparent Al-doped-ZnO/epoxy nanocomposites. J Phys Chem C2009; 113: 9406–9411.
8.
HsiaoKCLiaoSCChenYJ. Synthesis, characterization and photocatalytic property of nanostructured Al-doped ZnO powders prepared by spray pyrolysis. Mater Sci Eng A2007; 447: 71–76.
9.
CimitanSAlbonettiSForniL, et al.Solvothermal synthesis and properties control of doped ZnO nanoparticles. J Colloid Interface Sci2009; 329: 73–80.
10.
HammarbergEProdi-SchwabAFeldmannC. Microwave-assisted polyol synthesis of aluminium- and indium-doped ZnO nanocrystals. J Colloid Interface Sci2009; 334: 29–36.
11.
SirohiSSinghRJainN, et al.Synthesis and characterization of multifunctional ZnO/polyester green composite films. J Polym Res2017; 24: 193–193.
12.
XuBCaiZS. Fabrication of a superhydrophobic ZnO nanorod array film on cotton fabrics via a wet chemical route and hydrophobic modification. Appl Surf Sci2008; 254: 5899–5904.
13.
PandimuruganRThambiduraiS. UV protection and antibacterial properties of seaweed capped ZnO nanoparticles coated cotton fabrics. Int J Biol Macromol2017; 105: 788–795.
14.
ThiVHTLeeB-K. Development of multifunctional self-cleaning and UV blocking cotton fabric with modification of photoactive ZnO coating via microwave method. J Photochem Photobiol A2017; 338: 13–22.
15.
DuoSWZhongRFLiuZ, et al.One-step hydrothermal synthesis of ZnO microflowers and their composition-/hollow nanorod-dependent wettability and photocatalytic property. J Phys Chem Solids2018; 120: 20–33.
16.
LiYQKangYXiaoHM, et al.Preparation and characterization of transparent Al doped ZnO/epoxy composite as thermal-insulating coating. Compos Part B-Eng2011; 42: 12176-2180–12176-2180.
17.
BecheriADurrMLo NostroP, et al.Synthesis and characterization of zinc oxide nanoparticles: application to textiles as UV-absorbers. J Nanopart Res2008; 10: 679–689.
18.
Singh A and Singh S. ZnO nanowire-coated hydrophobic surfaces for various biomedical applications. Bull Mater Sci 2018; 41: 94(1-6).
19.
YadavKMehtaBRBhattacharyaS, et al.A fast and effective approach for reversible wetting-dewetting transitions on ZnO nanowires. Sci Rep2016; 6: 35073–35073.
20.
FengXJFengLJinMH, et al.Reversible super-hydrophobicity to super-hydrophilicity transition of aligned ZnO nanorod films. J Am Chem Soc2004; 126: 62–63.
21.
WangHXFangJChengT, et al.One-step coating of fluoro-containing silica nanoparticles for universal generation of surface superhydrophobicity. Chem Commun2008; 21: 877–879.
LiSHuangJChenZ, et al.A review on special wettability textiles: theoretical models, fabrication technologies and multifunctional applications. J Mater Chem A2017; 5: 31–55.
24.
GuoFWenQPengY, et al.Simple one-pot approach toward robust and boiling-water resistant superhydrophobic cotton fabric and the application in oil/water separation. J Mater Chem A2017; 5: 21866–21874.
25.
HuangJYLiSHGeMZ, et al.Robust superhydrophobic TiO2 fabrics for UV shielding, self-cleaning and oil–water separation. J Mater Chem A2015; 3: 2825–2832.
26.
SoumyaSMohamedAPMohanK, et al.Enhanced near-infrared reflectance and functional characteristics of Al-doped ZnO nano-pigments embedded PMMA coatings. Sol Energ Mat Sol C2015; 143: 335–346.
27.
WangWZhangLPLiuY, et al.Synthesis and infrared stealth property of ordered mesoporous carbon–aluminum-doped zinc oxide composites. Ind Eng Chem Res2013; 52: 15066–15074.
28.
LuoNWangDNYingSK. Crystallinity and hydrogen bonding of hard segment in segmented poly(urethane urea) copolymers. Polymer1996; 37(16): 3577–3583.
29.
ZhaoYTangYWangX, et al.Superhydrophobic cotton fabric fabricated by electrostatic assembly of silica nanoparticles and its remarkable buoyancy. Appl Surf Sci2010; 256: 6736–6742.
30.
VelayiENorouzbeigiR. Robust superhydrophobic needle-like nanostructured ZnO surfaces prepared without post chemical-treatment. Appl Surf Sci2017; 426: 674–687.