Biomass-derived silk fibroin (SF)-doped NaTaO3 catalysts were successfully synthesized by a simple hydrothermal process using SF as the dopant. The as-prepared samples were characterized by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and ultraviolet-visible diffuse reflectance spectroscopy (UV-vis DRS) analyses. The samples were tested as photocatalysts in the degradation of methylene blue under UV and visible light. XRD results showed the monoclinic structure of NaTaO3 lacking significant structural changes after anion doping. SEM and TEM images revealed the nanocubic morphology of the samples, the crystal particle sizes of which were about 100–300 nm. The XPS spectrum showed the peak of Ta4p3&N1s, indicating the combination of N and Ta. The UV-vis DRS results of the samples revealed a cut-off edge that red shifted from 315 nm of the pure NaTaO3 to 324 nm of the SF-doped counterpart. SF doping helped narrow the band gap and rendered the prepared sample sensitive to visible light. Under UV and visible-light irradiation, SF-doped NaTaO3 exhibited higher photocatalytic activity than that the undoped compound. SF-doped NaTaO3 samples also exhibited excellent stability during the recycling photocatalytic process.
FujishimaA. Electrochemical photolysis of water at a semiconductor electrode. Nature1972; 238: 37–38.
2.
NishioJTokumuraMZnadHTet al.Photocatalytic decolorization of azo-dye with zinc oxide powder in an external UV light irradiation slurry photoreactor. J Hazard Mater2006; 138: 106–115.
3.
HameedBH. Evaluation of papaya seeds as a novel non-conventional low-cost adsorbent for removal of methylene blue. J Hazard Mater2009; 162: 939–944.
4.
LiuDRWeiCDXueBet al.Synthesis and photocatalytic activity of N-doped NaTaO3 compounds calcined at low temperature. J Hazard Mater2010; 182: 50–54.
5.
Torres-MartínezLMCruz-LópezAJuárez-RamírezIet al.Methylene blue degradation by NaTaO3 sol–gel doped with Sm and La. J Hazard Mater2009; 165: 774–779.
6.
GogatePRPanditAB. A review of imperative technologies for wastewater treatment I: oxidation technologies at ambient conditions. Adv Environ Res2004; 8: 501–551.
7.
MengNLeungMKHLeungDYCet al.A review and recent development in photocatalytic water-splitting using TiO2 for hydrogen production. Renew Sust Energy Rev2007; 11: 401–425.
8.
Hu H, Pang B, Zhu Y, et al. Preparation of titanium dioxide immobilized on carbon fibers annealed in steam ambient and their photocatalytic properties. Text Res J 2017; 87: 2233–2241.
9.
KatoHKudoA. Water splitting into H2 and O2 on alkali tantalate photocatalysts ATaO3 (A = Li, Na, and K). J Phys Chem B2001; 105: 4285–4292.
10.
LagutaVVGlinchukMDBykovIPet al.Light-induced defects in KTaO3. J Appl Phys2003; 93: 6056–6064.
11.
KatoHKudoA. Photocatalytic decomposition of pure water into H2 and O2 over SrTa2O6 prepared by a flux method. Chem Lett1999; 28: 1207–1208.
12.
XuTZhaoXZhuY. Synthesis of hexagonal BaTa2O6 nanorods and influence of defects on the photocatalytic activity. J Phys Chem B2006; 110: 25825–25832.
13.
LiFFLiuDRGaoGMet al.Improved visible-light photocatalytic activity of NaTaO3 with perovskite-like structure via sulfur anion doping. Appl Catal B-Environ2015; 166: 104–111.
14.
KanherePTangYZhengJet al.Synthesis, photophysical properties, and photocatalytic applications of Bi doped NaTaO3 and Bi doped Na2Ta2O6 nanoparticles. J Phys Chem Solids2013; 74: 1708–1713.
15.
GreweTMeierKTüysüzH. Photocatalytic hydrogen production over various sodium tantalates. Catal Today2014; 225: 142–148.
16.
LiZHChenGLiuJW. Electron structure and optical absorption properties of cubic and orthorhombic NaTaO3 by density functional theory. Solid State Commun2007; 143: 295–299.
17.
QiLLiX. N-doped NaTaO3: novel visible-light-driven photocatalysts synthesised by a sol–gel method. J Sol-Gel Sci Techn2014; 69: 625–629.
18.
Hu CC, Huang HH and Huang YC. N-doped NaTaO3 synthesized from a hydrothermal method for photocatalytic water splitting under visible light irradiation. J Energy Chem 2017; 26: 515–521.
FuHZhangSZhangLet al.Visible-light-driven NaTaO3−xNx catalyst prepared by a hydrothermal process. Mater Res Bull2008; 43: 864–872.
21.
LiuDHuangJCaoLet al.Comparative study on the photocatalytic activity of biomass carbon doped Bi2WO6 crystallite with self-assembled hierarchical structure. J Mater Sci-Mater El2016; 27: 2473–2480.
22.
XuGHanJDingBet al.Biomass-derived porous carbon materials with sulfur and nitrogen dual-doping for energy storage. Green Chem2015; 17: 1668–1674.
23.
WangKWangHJiSet al.Biomass-derived activated carbon as high-performance non-precious electrocatalyst for oxygen reduction. RSC Adv2013; 3: 12039–12042.
24.
GaoNLuZZhaoXet al.Enhanced photocatalytic activity of a double conductive C/Fe3O4/Bi2O3 composite photocatalyst based on biomass. Chem Eng J2016; 304: 351–361.
25.
ShiNYanRZhouHet al.Biomass-inspired semiconductor photocatalysts for solar degradation of organics. Curr Org Chem2015; 19: 521–539.
26.
KohLDChengYTengCPet al.Structures, mechanical properties and applications of silk fibroin materials. Prog Polym Sci2015; 46: 86–110.
27.
KunduBRajkhowaRKunduSCet al.Silk fibroin biomaterials for tissue regenerations. Adv Drug Delivery Rev2013; 65: 457–470.
28.
SunYLuoYDongYet al.Shape memory and mechanical properties of silk fibroin/poly (ε-caprolactone) composites. Mater Lett2017; 193: 26–29.
29.
MelkeJMidhaSGhoshSet al.Silk fibroin as biomaterial for bone tissue engineering. Acta Biomater2016; 31: 1–16.
30.
KatoHKudoA. Photocatalytic water splitting into H2 and O2 over various tantalate photocatalysts. Catal Today2003; 78: 561–569.
31.
KanherePNisarJTangYet al.Electronic structure, optical properties, and photocatalytic activities of LaFeO3–NaTaO3 solid solution. J Phys Chem C2012; 116: 22767–22773.
32.
GreweTMeierKTüysüzH. Photocatalytic hydrogen production over various sodium tantalates. Catal Today2014; 225: 142–148.
33.
HuCCTengH. Influence of structural features on the photocatalytic activity of NaTaO3 powders from different synthesis methods. Appl Catal A-Gen2007; 331: 44–50.
34.
LeeYWatanabeTTakataTet al.Preparation and characterization of sodium tantalate thin films by hydrothermal−electrochemical synthesis. Chem Mater2005; 17: 2422–2426.
35.
LiXZangJ. Facile hydrothermal synthesis of sodium tantalate (NaTaO3) nanocubes and high photocatalytic properties. J Phys Chem C2009; 113: 19411–19418.
36.
HuCCTengH. Influence of structural features on the photocatalytic activity of NaTaO3 powders from different synthesis methods. Appl Catal A-Gen2007; 331: 44–50.
37.
ZhaoYXLiuDRLiFFet al.Preparation, characterization and photocatalytic activity of N-doped NaTaO3 nanocubes. Powder Technol2011; 214: 155–160.
38.
WohlrabSPinnaNAntoniettiMet al.Polymer-induced alignment of dl-alanine nanocrystals to crystalline mesostructures. Chem–Eur J2005; 11: 2903–2913.
39.
ShiJLiuGWangNet al.Microwave-assisted hydrothermal synthesis of perovskite NaTaO3 nanocrystals and their photocatalytic properties. J Mater Chem2012; 22: 18808–18813.
40.
TangJZouZYinJet al.Photocatalytic degradation of methylene blue on CaIn2O4 under visible light irradiation. Chem Phys Lett2003; 382: 175–179.
41.
WeiSHKrakauerHWeinertM. Linearized augmented-plane-wave calculation of the electronic structure and total energy of tungsten. Phys Rev B1985; 32: 7792.