Development of breathable Janus superhydrophobic polyester fabrics using alkaline hydrolysis and blade coating

Abstract

Alkaline hydrolysis is a common finishing method that is used to give polyester (polyethylene terephthalate, PET) a more natural touch and improved luster via chemical or physical changes in the fibers. However, its potential as a tool for surface modification in the development of single-sided superhydrophobic materials has not been studied yet. In this research, Janus superhydrophobic PET fabrics with asymmetric wetting properties (one side of the PET surface was rendered superhydrophobic while the other side was simply hydrophobic) were fabricated in two steps. Fine roughness was first achieved on the surface of PET fabrics by alkaline hydrolysis. Subsequently, optimized foam-coating emulsions were applied on only one surface of the alkaline-hydrolyzed PET. Alkaline treatment time, solution temperature, and viscosity of the foam-coating emulsions were varied to find optimal conditions in terms of structural changes, mechanical properties, superhydrophobicity, and absorption ability. The specimen treated with an aqueous solution of 8% sodium hydroxide at 70℃ for 60 min and coated with the mixture of the fluoro-emulsion and thickener in the volume ratio of 40:2 was determined to be the optimal conditions for the Janus superhydrophobic property. This sample showed a contact angle of 162.8° and a shedding angle of 5.6° on one side, whereas it completely permitted the percolation of water drops on the other side within 109 s. The mechanical properties of the developed Janus PET under the optimal conditions did not decrease significantly; its weight and tensile strength were found to have decreased by 3.3% and 19.2%, respectively. Furthermore, the single-sided superhydrophobic specimen demonstrated higher moisture transmissibility than the double-sided coated PET under the same alkaline treatment conditions. The method developed herein eliminates the requirement for an additional process to deliver nanoscale surface roughness and has the potential to produce waterproof–breathable PET fabrics for outdoor clothing.

Keywords

single-sided superhydrophobicity alkaline hydrolysis blade coating asymmetric wetting breathability

Get full access to this article

View all access options for this article.

References

Reinhoudt

Crego-Calama

. What do we need for a superhydrophobic surface? A review on the recent progress in the preparation of superhydrophobic surfaces. Chem Soc Rev 2007; 36: 1350–1368.

Park

Kim

Park

. Superhydrophobic textiles: review of theoretical definitions, fabrication and functional evaluation. J Eng Fibers Fabrics 2015; 10: 1–18.

Xue

Jia

Zhang

et al.

Large-area fabrication of superhydrophobic surfaces for practical applications: an overview. Sci Technol Adv Mater 2016; 11: 033002–033002.

Chu

Feng

Seeger

. Oil/water separation with selective superantiwetting/superwetting surface materials. Angewandte Chemie Int Ed 2015; 54: 2328–2338.

Ning

Yang

et al.

Fabrication of superhydrophobic surfaces on zinc substrates. Appl Surf Sci 2011; 257: 4801–4806.

Park S, Kim J and Park CH. Influence of micro and nano-scale roughness on hydrophobicity of a plasma-treated woven fabric. Text Res J 2017; 87: 193–207.

Shim

Kim

Park

. The effects of surface energy and roughness on the hydrophobicity of woven fabrics. Text Res J 2014; 84: 1268–1278.

Wang

Jiang

. Definition of superhydrophobic states. Adv Mater 2007; 19: 3423–3424.

Park

Kim

. A quantitative analysis on the surface roughness and the level of hydrophobicity for superhydrophobic ZnO nanorods grown textiles. Text Res J 2014; 84: 1776–1788.

10.

Moon

et al.

Nanostructured superhydrophobic silk fabric fabricated using the ion beam method. RSC Adv 2014; 4: 38966–38973.

11.

Isimjan

Wang

Rohani

. A novel method to prepare superhydrophobic, UV resistance and anti-corrosion steel surface. Chem Eng J 2012; 210: 182–187.

12.

Park

Kim

Park

. Analysis of the wetting state of super-repellent fabrics with liquids of varying surface tension. RSC Adv 2016; 6: 45884–45893.

13.

Kwon

et al.

Nanostructured self-cleaning lyocell fabrics with asymmetric wettability and moisture absorbency (part I). RSC Adv 2014; 4: 45442–45448.

14.

Kaliyamoorthi

Thangavelu

. Union dyeing of cotton/nylon blended fabric by plasma-nano chitosan treatment. Fashion Text 2015; 2: 1–10.

15.

Xue

Jia

Chen

et al.

Superhydrophobic cotton fabrics prepared by sol–gel coating of TiO2 and surface hydrophobization. Sci Technol Adv Mater 2016; 9: 035001–035001.

16.

Shim

Kim

Park

. Development of superhydrophobic fabrics by surface fluorination and formation of CNT-induced roughness. Mater Sci 2015; 21: 68–73.

17.

Kwon

Park

Kim

. Breathable, antistatic and superhydrophobic PET/lyocell fabric. J Eng Fabrics Fibers 2015; 10: 46–55.

18.

You

Yoo

et al.

Simple and reliable method to incorporate the Janus property onto arbitrary porous substrates. ACS Appl Mater Interfaces 2014; 6: 4005–4010.

19.

Liu

Feng

Zhai

et al.

Reversible wettability of a chemical vapor deposition prepared ZnO film between superhydrophobicity and superhydrophilicity. Langmuir 2004; 20: 5659–5661.

20.

Jiang

Zhao

Zhai

. A lotus-leaf-like superhydrophobic surface: a porous microsphere/nanofiber composite film prepared by electrohydrodynamics. Angewandte Chemie 2004; 116: 4438–4441.

21.

Sasaki

Tenjimbayashi

Manabe

et al.

Asymmetric superhydrophobic/superhydrophilic cotton fabrics designed by spraying polymer and nanoparticles. ACS Appl Mater Interfaces 2015; 8: 651–659.

22.

Grumezescu AM. (ed.) Multifunctional systems for combined delivery, biosensing and diagnostics. William Andrew, 2017. Amsterdam: Elsevier Science Ltd.

23.

Zeronian

Collins

. Surface modification of polyester by alkaline treatments. Text Progr 1989; 20: 1–26.

24.

Nguyen-Tri

El Aidani

Leborgne

et al.

Chemical ageing of a polyester nonwoven membrane used in aerosol and drainage filter. Polym Degrad Stabil 2014; 101: 71–80.

25.

Solbrig

Obendorf

. Alkaline hydrolysis of titanium dioxide delustered poly (ethylene terephthalate) yarns 1. Text Res J 1991; 61: 177–181.

26.

Mazrouei-Sebdani

Khoddami

. Alkaline hydrolysis: a facile method to manufacture superhydrophobic polyester fabric by fluorocarbon coating. Progr Organic Coatings 2011; 72: 638–646.

27.

Han

Park

. Development of superhydrophobic polyester fabrics using alkaline hydrolysis and coating with fluorinated polymers. Fibers Polym 2016; 17: 241–247.

28.

Xue

Zhang

et al.

Washable and wear-resistant superhydrophobic surfaces with self-cleaning property by chemical etching of fibers and hydrophobization. ACS Appl Mater Interfaces 2014; 6: 10153–10161.

29.

Yoon HS, Son TW, Kim BC, et al. Heat-and Chemical-resistant Acrylic Short Fibers Without Spinning. Patent 5,401,576, USA, 1995.

30.

Liu

Xin

Choi

. Cotton fabrics with single-faced superhydrophobicity. Langmuir 2012; 28: 17426–17434.

31.

ASTM D5034-95:1995. Standard test method for breaking strength and elongation of textile fabrics (grab test).

32.

Zimmermann

Seeger

Reifler

. Water shedding angle: a new technique to evaluate the water-repellent properties of superhydrophobic surfaces. Text Res J 2009; 79: 1565–1570.

33.

ASTM D737-75:2012. Standard test method for air permeability of textile fabrics.

34.

ASTM E96-80:2010. Standard test method for water vapour transmission of materials.

35.

Lee JS and Ryu HS. Alkaline softening of polyester fabrics treated with aqueous NaOH solutions containing CTAB&EDA. In: proceedings of the 3rd Asian textile conference, Hong Kong, 1995, Vol. 1, pp.256-261.

36.

37.

Farnworth

Lotens

Wittgen

PPMM

. Variation of water vapor resistance of microporous and hydrophilic films with relative humidity. Text Res J 1990; 60: 50–53.