Synthesis process control and property evaluation of a low-viscosity urethane acrylate oligomer for blue light curable ink of textile digital printing

Abstract

A low-viscosity urethane acrylate oligomer was synthesized under optimized conditions using a specially selected low molecular weight polyether diol. The synthesis process and the reaction endpoint were monitored by Fourier transform infrared spectroscopy. The rheological properties of the synthesized urethane acrylate oligomer were evaluated by rheology measurements in both steady and dynamic modes, and the blue light induced photopolymerization behavior of the oligomer with camphorquinone and ethyl-4-dimethylaminobenzoate as photoinitiators was examined with photo-differential scanning calorimetry analysis. A blue light curable pigment ink based on the low-viscosity urethane acrylate oligomer was prepared, and jet printed on cotton fabrics using a simulating digital printing device, then photo-cured under blue light irradiation. The printed fabric samples showed fine patterns with soft fabric handle.

Keywords

urethane acrylate oligomer low-viscosity inks blue light curing digital printing textile printing

Get full access to this article

View all access options for this article.

References

Calvert

. Inkjet printing for materials and devices. Chem Mater 2001; 13: 3299–3305.

Lewis

Smay

Stuecker

. Direct ink writing of three-dimensional ceramic structures. J Am Ceram Soc 2006; 89: 3599–3609.

Walsh

Oraby

. Radiation curing of pigment prints on textiles. Radiat Phys Chem 1979; 14: 893–904.

Luiken

Marsman

MPW

Holweg

RBM

. Radiation curable coatings and pigment binders for textile substrates. J Ind Text 1992; 21: 268–280.

Neral

Šostar-Turk

Vončina

. Properties of UV-cured pigment prints on textile fabric. Dyes Pigments 2006; 68: 143–150.

Mikuž

Turk

SŠ

Tavčer

. Properties of ink-jet printed, ultraviolet-cured pigment prints in comparison with screen-printed, thermo-cured pigment prints. Color Technol 2010; 126: 249–255.

Tyler

. Textile digital printing technologies. Text Prog 2005; 37: 1–65.

Ruyter

Øysæd

. Conversion in different depths of ultraviolet and visible light activated composite materials. Acta Odontol Scand 1982; 40: 179–192.

Swartz

Phillips

Rhodes

. Visible light-activated resins--depth of cure. J Am Dent Assoc 1983; 106: 634–637.

10.

Shao

Huang

Fan

. Visible light initiating systems for photopolymerization: status, development and challenges. Polym Chem UK 2014; 5: 4195–4210.

11.

Lin

Tsay

Speckhard

. Properties of UV-cured polyurethane acrylates: effect of polyol type and molecular weight. Chem Eng Commun 1984; 30: 251–273.

12.

Barbeau

Gerard

Magny

. Effect of the diisocyanate on the structure and properties of polyurethane acrylate prepolymers. J Polym Sci Pol Phys 2000; 38: 2750–2768.

13.

Oprea

Vlad

Stanciu

. Synthesis and characterization of poly(urethane-urea-acrylate)s. Eur Polym J 1999; 35: 1269–1277.

14.

Wang

. Study on microstructure of UV-curable polyurethane acrylate films. Prog Org Coat 2008; 62: 245–250.

15.

Shi

. Synthesis and characterization of hyperbranched polyurethane acrylates used as UV curable oligomers for coatings. Prog Org Coat 2005; 52: 110–117.

16.

Mequanint

Sanderson

Pasch

. Phosphated polyurethane–acrylic dispersions: synthesis, rheological properties and wetting behaviour. Polymer 2002; 43: 5341–5346.

17.

Glöckner

Jung

Struck

. Radiation curing: Coatings and printing inks; technical basics, applications and trouble shooting, Hannover: Vincentz Network, 2008. .

18.

Tant

Mauritz

Wilkes

. Ionomers: Synthesis, structure, properties and applications, New York, Springer, 1997.

19.

Ostwald

. Ueber die rechnerische Darstellung des Strukturgebietes der Viskosität. Kolloid-Zeitschrift 1929; 47: 176–187.

20.

Carlson JG, Anderson JT, Ylitalo CM, et al. Inks and other compositions incorporating low viscosity, radiation curable, polyester urethane oligomer. Patent 6,534,128, USA, 2003.

21.

Yang

. Viscosities of unsaturated polyester resins: combining effects of prepolymer structure, resin composition, and temperature. J Appl Polym Sci 1996; 60: 2387–2395.

22.

Huang

Fang

. Optimization of blue light induced hyperbranched polyurethane acrylate system applied to textiles. Adv Mater Res 2013; 821: 476–479.

23.

Scott

Cook

Forsythe

. Photo-DSC cure kinetics of vinyl ester resins. I Influence of temperature. Polymer 2002; 43: 5839–5845.

24.

Andrzejewska

Andrzejewski

. Polymerization kinetics of photocurable acrylic resins. J Polym Sci Pol Chem 1998; 36: 665–673.

25.

Kurdikar

Peppas

. A kinetic study of diacrylate photopolymerizations. Polymer 1994; 35: 1004–1011.

26.

Lecamp

Youssef

Bunel

. Photoinitiated polymerization of a dimethacrylate oligomer: 1. Influence of photoinitiator concentration, temperature and light intensity. Polymer 1997; 38: 6089–6096.

27.

Anseth

Wang

Bowman

. Kinetic evidence of reaction diffusion during the polymerization of multi(meth)acrylate monomers. Macromolecules 1994; 27: 650–655.

28.

Scherzer

Decker

. Kinetic investigations on the UV-induced photopolymerization of a diacrylate by time-resolved FTIR spectroscopy: the influence of photoinitiator concentration, light intensity and temperature. Radiat Phys Chem 1999; 55: 615–619.

29.

Scherzer

Decker

. Real-time FTIR-ATR spectroscopy to study the kinetics of ultrafast photopolymerization reactions induced by monochromatic UV light. Vib Spectrosc 1999; 19: 385–398.