The EMI shielding composites consisted of carbon fabric and nonwovens were developed based on needle punching and thermal bonding techniques, and their static and dynamic puncture resistances were also evaluated to resist against different puncture behaviors. The result shows that, needle-punched density and thermal bonding correlate with the EMI shielding effectiveness (SE) at particular medium and high frequency range, and respectively has interaction effect with number of layers. The mechanism of EMI shielding is reflection and absorption loss in medium-frequency, and only absorption loss in high-frequency. The static and dynamic puncture resistances improve linearly with number of layers, but both display an upward and then downward trend at increasing needle-punched density. After thermal bonding, the influence of thickness on static puncture resistance becomes significantly but on dynamic puncture resistance insignificantly. The resultant composites are expected to be used as wall interlayer and package interline in the future.
KimMSKimHKByunSW. PET fabric/polypyrrole composite with high electrical conductivity for EMI shielding. Synth Met2002; 126: 233–239.
5.
LiHHShiCQYeW. Polypyrrole-carbon fiber composite film prepared by chemical oxidative polymerization of pyrrole. J Appl Polym Sci1997; 64: 2149–2154.
6.
KimSHJangSHByunSW. Electrical properties and EMI shielding characteristics of polypyrrole–nylon 6 composite fabrics. J Appl Polym Sci2003; 87: 1969–1974.
7.
OhKWKimSHKimEA. Improved surface characteristics and the conductivity of polyaniline–nylon 6 fabrics by plasma treatment. J Appl Polym Sci2001; 81: 684–694.
8.
OhKWHongKHKimSH. Electrically conductive textiles by in situ polymerization of aniline. J Appl Polym Sci1999; 74: 2049–2101.
9.
FolguerasLCNoharaELFaezR. Dielectric microwave absorbing material processed by impregnation of carbon fiber fabric with polyaniline. Mat Res2007; 10: 95–99.
10.
LuYJiangSHuangY. Ultrasonic-assisted electroless deposition of Ag on PET fabric with low silver content for EMI shielding. Surf Coat Tech2010; 204: 2829–2833.
11.
GuoRHJiangSQYuenCWM. Influence of nickel ions for electroless Ni–P plating on polyester fabric. J Coat Technol Res2012; 9: 171–176.
12.
ChengKBRamakrishnaSLeeKC. Electromagnetic shielding effectiveness of copper/glass fiber knitted fabric reinforced polypropylene composites. Compos Part A Appl S2000; 31: 1039–1045.
13.
ChengKBLeeKCUengTH. Electrical and impact properties of the hybrid knitted inlaid fabric reinforced polypropylene composites. Compos Part A Appl S2002; 33: 1219–1226.
14.
ChenHCLeeKCLinJH. Electromagnetic and electrostatic shielding properties of co‐weaving-knitting fabrics reinforced composites. Compos Part A Appl S2004; 35: 1249–1256.
15.
ChenHCLeeKCLinJH. Comparison of electromagnetic shielding effectiveness properties of diverse conductive textiles via various measurement techniques. J Mater Process Tech2007; 192–193: 549–554.
LinJHLouCW. Electrical properties of laminates made of a new fabric with PP/Stainless steel commingled yarn. Textil Res J2003; 73: 322–326.
18.
LouCWLinCMHsingWH. Manufacturing techniques and electrical properties of conductive fabrics with recycled polypropylene nonwoven selvage. Textil Res J2011; 81: 1331–1343.
19.
LiTTWangRLouCW. Acoustic absorption evaluation of high-modulus puncture resistance composites made by recycled selvages. Textil Res J2012; 82: 1597–1611.
20.
Li TT, Wang R, Lou CW, et al. Evaluation of high-modulus, puncture-resistance composite nonwoven fabrics by response surface methodology. J Ind Textil. Epub ahead of print 5 July 2012. DOI: 10.1177/1528083712452900.
21.
WieckowskiTWJanukiewiczJM. Methods for evaluating the shielding effectiveness of textiles. Fibres Text East Eur2006; 14: 18–22.
Šafárová V and Grégr J. Electrical conductivity measurement if fibers and yarns. In: 7th international conference- TEXSCI 2010, Liberec, Czech Republic, 6–8 September 2010.
24.
YangYZhangBXuW. Preparation and properties of a novel iron-coated carbon fiber. J Magn Magn Mater2003; 256: 129–132.