Hydrophilization of wool fabrics was performed by silver nanoparticles with different surface charge using three different methods: exhausting, pad–dry–cure and in situ synthesis. Dynamic wetting measurements and surface topography analysis were used to evaluate surface changes on wool fabrics. The wool samples in situ loaded revealed the highest fabric roughness and porosity, while the use of the pad–dry–cure method leads to the lowest fabric porosity, and its roughness values approximately were the same as those for samples loaded with the exhaustion method. The results revealed that loading silver nanoparticles with high surface charges onto wool fabrics via the exhaustion method can significantly improve the hydrophilicity of wool fibre surface. The possible reasons for this improvement are discussed.
RistićNJovančićPCanalCJocićD. Influence of corona discharge and chitosan surface treatment on dyeing properties of wool. J Appl Polym Sci2010; 117: 2487–2496.
10.
MeadeSJCaldwellJPHancockAJCoyleKDyerJMBrysonWG. Covalent modification of the wool fiber surface: the attachment and durability of model surface treatments. Textile Res J2008; 78: 1087–1097.
11.
MontazerMPakdelEMoghadamMB. The role of nano colloid of TiO2 and butane tetra carboxylic acid on the alkali solubility and hydrophilicity of proteinous fibers. Colloids Surf A Physicochem Eng Aspects2011; 375: 1–11.
12.
DastjerdiRMontazerMShahsavanS. A novel technique for producing durable multifunctional textiles using nanocomposite coating. Colloids Surf B Biointerfaces2010; 81: 32–41.
TangBWangJXuS. Application of anisotropic silver nanoparticles: Multifunctionalization of wool fabric. J Colloid Interface Sci2011; 356: 513–518.
15.
KingDGPierlotAP. Absorption of nanoparticles by wool. Coloration Technol2009; 125: 111–116.
16.
El-ShishtawyRMAsiriAMAbdelwahedNAMAl-OtaibiMM. In situ production of silver nanoparticle on cotton fabric and its antimicrobial evaluation. Cellulose2011; 18: 75–82.
17.
DongQSuHZhangD. In situ depositing silver nanoclusters on silk fibroin fibers supports by a novel biotemplate redox technique at room temperature. J Phys Chem B2005; 109: 17429–17434.
18.
BaraniHMontazerM. A review on applications of liposomes in textile processing. J Liposome Res2008; 18: 249–262.
19.
BaraniHMalekiH. Plasma and ultrasonic process in dyeing of wool fibers with madder in presence of lecithin. J Dispersion Sci Technol2011; 32(8): 1191–1199.
20.
BaptistaALFCoutinhoPJGOliveiraMECDRGomesJINR. Lipid interaction with textile fibres in dyeing conditions. Prog Colloid Polym Sci2004; 123: 88–93.
21.
BaraniHMontazerMSamadiNToliyatT. Nano silver entrapped in phospholipids membrane: Synthesis, characteristics and antibacterial kinetics. Mol Membrane Biol2011; 28: 206–215.
22.
CalvimontesAGrundkeKMüllerA. Volumetrical characterization of sheet molding compounds. Materials2010; 3: 5083–5096.
Stout KJ, Sullivan PJ, Dong WP, et al. The development of methods for the characterization of roughness on three dimensions. Publication number EUR 15178 EN, Commission of the European Communities, Luxembourg, 1994.
25.
DutschkVSabbatovskiyKGStolzMGrundkeKRudoyVM. Unusual wetting dynamics of aqueous surfactant solutions on polymer surfaces. J Colloid Interface Sci2003; 267: 456–462.
26.
BaraniHMontazerMToliyatTSamadiN. In situ synthesis of nano silver/lecithin on wool: Enhancing nanoparticles diffusion. Colloids Surf B Biointerfaces2012; 92: 9–15.
27.
Carr CM. Chemistry of the Textiles Industry. New York: Springer-Verlag.
28.
BahiAJonesJTCarrCMUlijnRVShaoJ. Surface characterization of chemically modified wool. Textile Res J2007; 77: 937–945.
29.
WortmannF-JPhanK-H. Cuticle scale heights of wool and specialty fibers and their changes due to textile processing. Textile Res J1999; 69: 139–144.
30.
JachowiczJGarciaMWis-SurelG. Relationship between triboelectric charging and surface modification of human hair: polymeric versus monomeric long alkyl chanin quaternary ammonium salts. Textile Res J1987; 57: 543–548.