Durable Hydrophobic Textile Fabric Finishing Using Silica Nanoparticles and Mixed Silanes

Abstract

Cotton fabric surface was treated with combinations of silica nanoparticles, silane hydrophobes, and silane crosslinkers to obtain durable hydrophobicity. Performance analysis was done by measuring the contact angle of water on the treated fabric surface. To evaluate the durability of the surface hydrophobicity, AATCC crocking and laundering tests were performed. Cotton fabrics with good hydrophobicity (contact angle = 139.1°) and excellent durability (e.g. 95% recovery of contact angle after laundering) were obtained when treated with Aerosil^® 90 nanoparticles, n-octyltrimethoxysilane, and bis(triethoxysilyl)ethane. This study demonstrated that the surface treatment using silica nanoparticles and mixed silanes is a promising alternative to fluoropolymer chemistry for achieving durable hydrophobic fabrics.

Keywords

fabric finishing hydrophobicity nanotechnology silane silica

Get full access to this article

View all access options for this article.

References

Mahltig, B. , Haufe, H. , and Böttcher, H. , Functionalisation of Textiles by Inorganic Sol-Gel Coatings, J. Mater. Chem., 15, 4385-4398 (2005 ).

Zhang, X. , and Fedkiw, P.S. , Ionic transport and Interfacial Stability of Sulfonate-Modified Fumed Silicas as Nanocomposite Electrolytes, J. Electrochem. Soc., 152, A2413-A2420 (2005).

Schmidt, H. , Considerations about the Sol-Gel Process: From the Classical Sol-Gel Route to Advanced Chemical Nanotechnologies, J. Sol-Gel. Sci. Technol. , 40, 115-130 (2006).

Pipatchanchai, T. , and Srikulkit , Hydrophobicity Modification of Woven Cotton Fabric by Hydrophobic Fumed Silica Coating, K, J. Sol-Gel Sci. Technol., 44, 119-123 (2007).

Mahltig, B. , and Böttcher, H. , Modified Silica Sol Coatings for Water-Repellent Textiles, J. Sol-Gel Sci. Technol., 27, 43-52 (2003).

Daoud, W.A. , Xin, J.H. , and Tao, X. , Superhydrophobic Silica Nanocomposite Coating by a Low-Temperature Process , J. Am. Ceram. Soc., 87, 1782-1784 (2004 ).

Textor, T. , Bahners, T. , and Schollmeyer, E. , Organically Modified Ceramics for Coating Textile Materials, Prog. Colloid Polym. Sci., 117, 76-79 (2002).

Yu, M. , Gu, G. , Meng, W.D. , and Qing, F.L. , Superhydrophobic Cotton Fabric Coating Based on a Complex Layer of Silica Nanoparticles and Perfluorooctylated Quaternary Ammonium Silane Coupling Agent , Appl. Surf. Sci., 253, 3669-3673 (2007 ).

Černe, L. , and Simončič , B. , Influence of Repellent Finishing on the Surface Free Energy of Cellulosic Textile Substrates, Text. Res. J., 74, 426-432 (2004).

10.

Michael, G. , and Ferch, H. , Basic Characteristics of AERO-SIL, Degussa Technical Bulletin Pigments, No. 11 (1998).

11.

Soeno, T. , Inokuchi, K. , and Shiratori, S. , Ultra-Water-Repellent Surface: Fabrication of Complicated Structure of SiO2 Nanoparticles by Electrostatic Self-Assembled Films, Appl. Surf. Sci., 237, 543-547 (2004).

12.

Yoneda, T. , and Morimoto, T. , Mechanical Durability of Water Repellent Glass, Thin Solid Films, 351, 279 (1999).

13.

Nakagawa, T. , and Hiwatashi, T. , Water-Repellent Thin Film W\with High Alkali Resistance Using The Sol-Gel Method for Ink Jet Printer Head, Jpn. J. Appl. Phys., 41, 3896-3901 (2002 ).

14.

Barthlott, W. , and Neinhuis, C. , Purity of the Sacred Lotus, or Escape From Contamination in Biological Surfaces, Planta, 202, 1-8 (1997).