Cross-sectional Distribution of Crystalline and Fibril Orientations of Typical Regenerated Cellulose Fibers in Relation to their Fibrillation Resistance

Abstract

The structural distributions and their formation mechanisms, on both the morphological and crystallographic scales of two types of regenerated cellulose fiber, cuprammonium rayon (Cupra) and solvent spun rayon (Lyocell), were studied in relation to fibrillar formation using transmission electron microscopy and electron micro-diffraction analysis. Cupra had a multilayer structure. The outer layer of the fiber had a network structure without distinct fibrils, but with high crystallinity (χ_c) and crystalline orientation (F _c), whereas the center of the fiber had a well-developed fibrillar structure with an amorphous state. The high χ_c in the outer layer probably resulted from the release of both copper and ammonia from the fiber during coagulation. The fibrillar structures in the center could have been formed by the deformation of the network structure along the elongation direction before crystallization took place. Lyocell was crystallographically and morphologically uniform along the fiber radius, with a highly developed fibrillar structure with high χ_c and F _c. The type of fibrillar formation was closely correlated with the morphological distribution, that is, fibrillation started from layers with a well-developed fibrillar structure.

Keywords

structure-properties fiber yarn fabric formation

Get full access to this article

View all access options for this article.

References

Chanzy, H. , Paillet, M. , and Hagege, R. , Spinning of Cellulose from N-Methyl Morpholine N-Oxide in the Presence of Additives, Polymer, 31, 400-405 (1990).

Mortimer, S.A. , and Peguy, A.A. , Methods for Reducing the Tendency of Lyocell Fibers to Fibrillate, J. Appl. Polym. Sci., 60, 305-316 (1996).

Pitowski, H.J. , and Wachsmann, U.W. , U.S. patent 6,159,601.

Firgo, H. , Mulleder, E. , and Seidl, S. , U.S. patent 5,919,412.

Hashemzadeh, A. , U.S. patent 6,180,234.

Nicolai, M. , Nechwatal, A. , and Mieck, K.P. , Textile CrossLinking Reactions to Reduce the Fibrillation Tendency of Lyocell Fibers, Text. Res. J., 66, 575-580 (1996).

Taylor, J. , U.S. patents 5,403,530; 5,520,869; 5,580,354; and 5,580,356.

Yamane, C. , Mori, M. , Saito, M. , and Okajima, K. , Structure and Mechanical Properties of Cellulose Filament Spun from Cellulose/Aqueous NaOH Solution System, Poly. J., 28, 1039- 1047 (1996).

Imai, T. , and Sugiyama, J. , Nanodomains of Iα and Iβ Cellulose in Algal Microfibrils, Macromolecules, 31, 6275-6279 (1998 ).

10.

Muller, M. , Riekel, C. , Vuong, R. , and Chanzy, H. , Skin/Core Micro-Structure in Viscose Rayon Fibres Analyzed by X-ray Microbeam and Electron Diffraction Mapping, Polymer, 41, 2627-2632 (2000).

11.

Isogai, A. , and Usuda M. , Crystallinity Indexes of Cellulosic Materials, Sen-I Gakkaishi , 46, 324-329 (1990).

12.

Segal, L. , Creely, J.J. , Martin, Jr. A.E. , and Conrad, C.M. , An Empirical Method for Estimating the Degree of Crystallinity of Native Cellulose Using the X-ray Diffractometer, Text. Res. J., 29, 786-794 (1959).

13.

Stein, R.S. , The X-Ray Diffraction, Birefringence, and Infrared Dichroism of Stretched Polyethylene. II. Generalized Uniaxial Crystal Orientation, J. Poly. Sci., 31, 327-334 (1958).

14.

Kamide, K. , "Thermodynamics of Polymer Solution, Phase Equilibria and Critical Phenomena", Elsevier: Amsterdam , 1990, pp. 450-454.

15.

Miyamoto, I. , Inamoto, M. , Matsui , T. , and Okajima, K. , Studies on Structure of Cuprammonium Cellulose I. A Circular Dichroism Study on the Dissolution State of Cellulose in Cuprammonium Solution, Poly. J., 27, 1113-1122 (1995 ).

16.

Hermans, P.H. , and Weidinger, A. , Quantitative X-ray Investigations on the Crystallinity of Cellulose Fibers, J. App. Phys., 19, 491-506 (1948).

17.

Yamane, C. , Aoyagi, T. , Satho, K. , Okajima, K. , and Takahashi, T. , Two Different Surface Properties of Regenerated Cellulose Due to Structural Anisotropy, Poly. J., 38, 819-826 (2006).