Improving wear resistance in Haynes 25 alloy is crucial for the development of flexible nuclear power reactors. Herein, laser-directed energy deposition (L-DED)-assisted substrate preheating is reported as an efficient strategy to alleviate cracks and pores in the alloy. The substrate-preheated alloy (300PH) exhibited no microcracks and a 45.2% reduction in pore fraction compared to the non-preheated alloy (NonPH). Moreover, 300PH exhibited a 7% lower Vickers microhardness than that of NonPH, whereas its nanohardness decreased by 3.6 and 2.9% in the dendritic and interdendritic regions, respectively. Dislocation strengthening was the dominant contributor to the theoretical yield strength and microhardness. Furthermore, preheating influenced the dislocation contribution substantially by reducing the residual stress leading to reductions in geometrically necessary dislocations and total dislocation density, thereby reducing microhardness. Therefore, preheating the substrate mitigated pores and cracks, effectively improved the structural integrity of L-DED Haynes 25 alloy, without significantly compromising the hardness.
TeagueJCerretaEStoutM. Tensile properties and microstructure of Haynes 25 alloy after aging at elevated temperatures for extended times. Metall Mater Trans A2004; 35: 2767–2781.
2.
AhluwaliaH. ASM Specialty handbook: nickel, cobalt, and their alloys. Corrosion2002; 58: 381.
3.
KlastromDL. Wrought cobalt-base superalloys. J Mater Eng Perform1993; 2: 523–530.
4.
HullDBaconDJ. Introduction to dislocations. Liverpool: Butterworth-Heinemann, 2011.
5.
RashidiPAGArabiHAbbasiSM. Effect of cold-rolling on mechanical properties of Haynes 25 cobalt-based superalloy. Metall Mater Eng2017; 23: 31–45.
6.
NakanoTHagiharaKRibeiroAR, et al.Orientation dependence of the wear resistance in the Co–Cr–Mo single crystal. Wear2021; 478: 203758.
7.
MoriMYamanakaKChibaA. Cold-rolling behavior of biomedical Ni-free Co–Cr–Mo alloys: role of strain-induced ɛ martensite and its intersecting phenomena. J Mecha Behav Biomed Mater2016; 55: 201–214.
8.
MoriMYamanakaKSatoS, et al.Tuning strain-induced γ-to-ɛ martensitic transformation of biomedical Co–Cr–Mo alloys by introducing parent phase lattice defects. J Mecha Behav Biomed Mater2019; 90: 523–529.
9.
KoizumiYSuzukiSYamanakaK, et al.Strain-induced martensitic transformation near twin boundaries in a biomedical Co–Cr–Mo alloy with negative stacking fault energy. Acta Mater2013; 61: 1648–1661.
10.
CarpenterJLJr. Bibliography of information on mechanics of structural failure (hydrogen embrittlement, protective coatings, composite materials, NDE). Report no. OR-14177, 1976.
11.
LemaireELe CalvarM. Evidence of tribocorrosion wear in pressurized water reactors. Wear2001; 249: 338–344.
WangYZhangCYuC, et al.Construction of cellular substructure in laser powder bed fusion. Metals (Basel)2019; 9: 1231.
14.
KimJ-YLeeD-M. LAM-DED process for repair and maintenance of cast iron components using metallic powder alloys. J Weld Join2020; 38: 349–358.
15.
GuoCLiGLiS, et al.Additive manufacturing of Ni-based superalloys: residual stress, mechanisms of crack formation and strategies for crack inhibition. Nano Mater Sci2023; 5: 53–77.
16.
KwonJHKangJHKimWJ. Development of materials technology for reactor components based on 3D printing. Report no. KAERI/RR–4630/2020. Korea Atomic Energy Research Institute, 2014.
17.
JiangJLianGXuM, et al.Influence of preheating temperature on mechanical properties of laser cladding layer. In: ASME International Manufacturing Science and Engineering Conference, 2016, vol. 49897, pp.V001T02A031.
18.
LiHHuangYSunJ, et al.The relationship between thermo-mechanical history, microstructure and mechanical properties in additively manufactured CoCrFeMnNi high entropy alloy. J Mater Sci Technol2021; 77: 187–195.
19.
KumarDShankarGPrashanthKG, et al.Texture dependent strain hardening in additively manufactured stainless steel 316L. Mater Sci Eng A2021; 820: 141483.
20.
KauzlarichJJWilliamsJA. Archard wear and component geometry. Proc Inst Mech Eng J: J Eng Tribol2001; 215: 387–403.
21.
EdingtonJW. Electron diffraction in the electron microscope. London: Macmillan Education UK, 1975.
22.
LiuTFPengSWLinYL, et al.Orientation relationships among M23C6, M6C, and austenite in an fe-mn-al-mo-C alloy. Metall Trans A1990; 21: 567–574.
23.
FavreJ. Recrystallization of L-605 cobalt superalloy during hot-working process. Doctoral dissertation, INSA de Lyon; Tōhoku Daigaku, Sendai, Japon, 2012.
24.
AndreuAKimSKimI, et al.Processing challenges and delamination prevention methods in titanium-steel DED 3D printing. Int J Precis Eng Manuf Green Technol2024; 11: 1663–1679.
25.
ChoiJPShinGHBrochuM, et al.Densification behavior of 316L stainless steel parts fabricated by selective laser melting by variation in laser energy density. Mater Trans2016; 57: 1952–1959.
26.
DebRoyTWeiHLZubackJS, et al.Additive manufacturing of metallic components–process, structure and properties. Prog Mater Sci2018; 92: 112–224.
27.
NezhadfarPDShamsaeiNPhanN. Enhancing ductility and fatigue strength of additively manufactured metallic materials by preheating the build platform. Fatigue Fract Eng Mater Struct2021; 44: 257–270.
28.
ShimDSBaekGYLeeEM. Effect of substrate preheating by induction heater on direct energy deposition of AISI M4 powder. Mater Sci Eng A2017; 682: 550–562.
29.
YangBShangZDingJ, et al.Investigation of strengthening mechanisms in an additively manufactured haynes 230 alloy. Acta Mater2022; 222: 117404.
30.
PrashanthKGEckertJ. Formation of metastable cellular microstructures in selective laser melted alloys. J Alloys Comp 2017; 707: 27–34.
31.
FriandaniSSUedaKNarushimaT. Systematic study on the microstructures of biomedical co–20Cr–15W–10Ni alloys with carbon contents ranging from 0 to 0.2 mass pct. Metall Mater Trans A2024; 55: 1011–1024.
32.
HaleyJLeachCJordanB, et al.In-situ digital image correlation and thermal monitoring in directed energy deposition additive manufacturing. Opt Express2021; 29: 9927–9941.
33.
XueHLiangYPengH, et al.Additive manufacturing of micro/nano multiphase synergistically reinforced Ti-55Al-7.5 Nb with a reticular boundary precipitate via direct laser deposition. Addit Manuf2022; 58: 102989.
34.
SuYWangZLuH, et al.Improved wear resistance of directed energy deposited Fe-Ni-Cr alloy via closed-loop controlling laser power. J. Manuf. Process2022; 75: 802–813.
35.
ChenSYuHLuN, et al.The effect of carbon content on the printability and mechanical properties of Ni-based superalloy in laser additive manufacturing. Mater Sci Eng A2024; 898: 146398.
36.
HuangYCWuHXuTZ, et al.Microstructure, tribological property and high temperature tensile property of Co-Cr-Ni-W alloy parts fabricated by laser directed energy deposition. Surf Coat Technol2024; 483: 130807.
37.
VanDDindaGPParkJ, et al.Enhancing hardness of Inconel 718 deposits using the aging effects of cold metal transfer-based additive manufacturing. Mater Sci Eng A2020; 776: 139005.
38.
TaoPLiHHuangB, et al.The crystal growth, intercellular spacing and microsegregation of selective laser melted Inconel 718 superalloy. Vacuum2019; 159: 382–390.
39.
FerganiOBrotanVBambachM, et al.Texture evolution in stainless steel processed by selective laser melting and annealing. Mater. Sci. Technol2018; 34: 2223–2230.
40.
PhamMSDovgyyBHooperPA, et al.The role of side-branching in microstructure development in laser powder-bed fusion. Nat Commun2020; 11: 749.
41.
KumarDShankarGPrashanthKG, et al.Texture dependent strain hardening in additively manufactured stainless steel 316L. Mater Sci Eng A2021; 820: 141483.
42.
KhodabakhshiFFarshidianfarMHGerlichAP, et al.Engineering of textured gradient microstructures using directed energy deposition: the impact of adaptive cooling rate. Mater Des2024; 245: 113266.
43.
WangDSongCYangY, et al.Investigation of crystal growth mechanism during selective laser melting and mechanical property characterization of 316L stainless steel parts. Mater Des2016; 100: 291–299.
44.
SmithTRSugarJDSan MarchiC, et al.Strengthening mechanisms in directed energy deposited austenitic stainless steel. Acta Mater2019; 164: 728–740.
45.
ZhengBZhouYSmugereskyJE, et al.Thermal behavior and microstructure evolution during laser deposition with laser-engineered net shaping: part II. Experimental investigation and discussion. Metall Mater Trans A2008; 39: 2237–2245.
46.
TaoPLiHHuangB, et al.The crystal growth, intercellular spacing and microsegregation of selective laser melted Inconel 718 superalloy. Vacuum2019; 159: 382–390.
47.
KamikawaNSatoKMiyamotoG, et al.Stress–strain behavior of ferrite and bainite with nano-precipitation in low carbon steels. Acta Mater2015; 83: 383–396.
48.
FriandaniSSHiyamaKUekiK, et al.Exceptional balance of strength and ductility in biomedical Co-Cr-W-Ni alloy with added carbon. Mater Sci Eng A2024; 908: 146722.
49.
ShangZDingJFanC, et al.Tailoring the strength and ductility of T91 steel by partial tempering treatment. Acta Mater2019; 169: 209–224.
50.
MitchellDRGDonnellySE. A TEM investigation of solid krypton bubbles formed in cobalt by ion implantation. Radiat Eff Defects Solids1990; 114: 253–261.
51.
SweeneyCADunneFPEMcHughPE,et al.Micro-scale testing and micromechanical modelling for high cycle fatigue of CoCr stent material. J Mech Behav Biomed Mater2015; 46: 244–260.
52.
UngárTHarjoSKawasakiT, et al.Composite behavior of lath martensite steels induced by plastic strain, a new paradigm for the elastic-plastic response of martensitic steels. Metall Mater Trans A2017; 48: 159–167.
53.
ChenZChenAJiaQ, et al.Investigation of microstructures and strengthening mechanisms in an N-doped Co-Cr-Mo alloy fabricated by laser powder bed fusion. Virtual Phys Prototyp2023; 18: e2219665.
54.
MonshiAForoughiMRMonshiMR. Modified Scherrer equation to estimate more accurately nano-crystallite size using XRD. WJNSE2012; 2: 154–160.
55.
TaborD. The Hardness of Metals. Oxford, London: Clarendon, 1951.
56.
SerjoueiALiburaTBrodeckiA, et al.Strength-hardness relationship for AlSi10Mg alloy produced by laser powder bed fusion: an experimental study. Mater Sci Eng A2022; 861: 144345.
57.
YooYSJBookTASangidMD, et al.Identifying strain localization and dislocation processes in fatigued Inconel 718 manufactured from selective laser melting. Mater Sci Eng A2018; 724: 444–451.
58.
WangGOuyangHFanC, et al.The origin of high-density dislocations in additively manufactured metals. Mater Res Lett2020; 8: 283–290.
59.
WaqarSGuoKSunJ. Evolution of residual stress behavior in selective laser melting (SLM) of 316L stainless steel through preheating and in-situ re-scanning techniques. Opt Laser Technol2022; 149: 107806.
60.
YanZZouXLiS, et al.A study on the thermo-mechanical history, residual stress, and dynamic recrystallization mechanisms in additively manufactured austenitic stainless steels. Metals (Basel)2022; 12: 1109.
61.
FuJQuSDingJ, et al.Comparison of the microstructure, mechanical properties and distortion of stainless steel 316 L fabricated by micro and conventional laser powder bed fusion. Addit Manuf2021; 44: 102067.
62.
GaoSHuZDuchampM, et al.Recrystallization-based grain boundary engineering of 316L stainless steel produced via selective laser melting. Acta Mater2020; 200: 366–377.
63.
MuranskyOBaloghLTranM, et al.On the measurement of dislocations and dislocation substructures using EBSD and HRSD techniques. Acta Mater2019; 175: 297–313.
64.
AnderogluO. Residual stress measurement using X-ray diffraction. Doctoral dissertation, Texas A&M University, Texas, USA, 2005.
65.
ASM Materials for Medical Devices Database Committee. Materials and coatings for medical devices: Cardiovascular. Ohio: ASM International, Materials Park, 2009.
66.
SmithTRSugarJDSchoenungJM, et al.Anomalous annealing response of directed energy deposited type 304L austenitic stainless steel. Jom2018; 70: 358–363.
Supplementary Material
Please find the following supplemental material available below.
For Open Access articles published under a Creative Commons License, all supplemental material carries the same license as the article it is associated with.
For non-Open Access articles published, all supplemental material carries a non-exclusive license, and permission requests for re-use of supplemental material or any part of supplemental material shall be sent directly to the copyright owner as specified in the copyright notice associated with the article.