Effect of Cubic Leucite Stabilization on the Flexural Strength of Feldspathic Dental Porcelain

Abstract

Previous studies (Mackert and Evans, 1993) have shown that, when feldspathic dental porcelain is cooled, leucite undergoes a transformation from cubic to tetragonal, associated with a 1.2% volume contraction. This contraction leads to the formation of microcracks in and around the crystals and the development of tangential compressive stresses around the crystals. Our aim was to stabilize increasing amounts of the cubic form of leucite in a leucite-reinforced dental porcelain, evaluate its effect on the flexural strength, and characterize its microstructure. The hypothesis was that in the absence of crystallographic transformation, the contraction of the leucite crystals would be lower, thereby limiting the formation of microcracks and minimizing the development of tangential compressive stresses around the leucite particles. We prepared 8 porcelain compositions by mixing increasing amounts of either leucite (KAlSi₂O₆) or pollucite (CsAlSi₂O₆) with Optec HSP porcelain (Jeneric/Pentron Inc., Wallingford, CT). Porcelain disks were made from each composition (n = 10 per group). X-ray diffraction analyses showed that the amount of stabilized leucite increased with the amount of pollucite added. The microstructure of the specimens containing tetragonal leucite was characterized by twinned leucite crystals, whereas no twinning was observed in the specimens containing cubic leucite. The evaluation of crack deflection showed that significantly less deflection occurred in the specimens containing cubic leucite. The mean biaxial flexural strength for the group corresponding to 22.2 wt% added pollucite, fired at 1038°C, was significantly lower than that for the control group. The group corresponding to 22.2 wt% added leucite fired at 1150°C exhibited a mean biaxial flexural strength significantly higher than that of all other groups that were not significantly different from the control group. Overall, the stabilization of cubic leucite reduced the flexural strength and the number of crack deflections in leucite-reinforced porcelain. Apparently, the development of tangential compressive stresses around the leucite crystals when cooled is responsible for a significant amount of strengthening of feldspathic dental porcelain.

Keywords

ceramics dental porcelain leucite,x-ray diffraction Received August 14,1995 Accepted August 14,1996

Get full access to this article

View all access options for this article.

References

Anusavice KJ , Hojjatie B. (1992). Tensile stress in glass-ceramic crowns: effect of flaws and cement voids. Int J Prosthodont 5:351-358.

Azároff LV , Buerger MJ (1958). The powder method in x-ray crystallography. New York: McGraw-Hill Book Company, Inc., pp. 233-245.

Dong JK , Luthy H. , Wohlwend A. , Schärer P. (1992). Heat-pressed ceramics: technology and strength . Int J Prosthodont 5:9-16.

Hermansson L. , Carlsson R. (1976). High and low temperature forms of leucite. In: Proceedings, 8th International Symposium on the Reactivity of Solids. Gothenberg, Sweden: Swedish Institute for Silicate Research, pp. 541-545.

Mackert JR Jr (1988). Effects of thermally induced changes on porcelain-metal compatibility. In: Proceedings, Fourth International Symposium on Ceramics. Preston JD, Editor. Chicago: Quintessence Publishing Co., pp. 53-64. Mackert JR Jr, Evans AL (1993). Multiple firing effect on microcrack density in dental porcelain (abstract). J Dent Res 72:263.

Mackert JR Jr , Butts MB , Fairhurst CW (1986a). The effect of the leucite transformation on dental porcelain expansion. Dent Mater 2:32-36.

Mackert JR Jr , Butts MB , Morena R. , Fairhurst CW (1986b). Phase changes in a leucite-containing dental porcelain frit. J Am Ceram Soc 69:C69-C72.

Mazzi F. (1976). The crystal structure of tetragonal leucite. Am Mineral 61:108-115.

Naray-Szabo I. (1969). Inorganic crystal chemistry. Budapest: Akademiai Kiado, pp. 40, 375.

10.

Palmer DC , Putnis A. , Salje Ekh (1988). Twinning in tetragonal leucite. Phys Chem Minerals 16:298-303.

11.

Palmer DC , Salje Ekh , Schmahl WW (1989). Phase transitions in leucite: x-ray diffraction studies. Phys Chem Minerals 16:714-719.

12.

Piché PW, O'Brien WJ, Groh CL, Boenke KM (1994). Leucite content of selected dental porcelains. J Biomed Mater Res 28:603-609. Prasad A, Vaidyanathan TK (1990). Crystallization of cubic leucite by composition additives (abstract). J Dent Res 69:210. Schmid M, Fischer J, Salk M, Strub J (1992). Mikrogefüge leucit

13.

Shetty DK , Rosenfield AR , McGuire PA , Bansal GK , Duckworth WH (1980). Biaxial fracture tests for ceramics. Ceram Bull 59:1193-1197.

14.

Taylor D, Henderson CMB (1968). The thermal expansion of the leucite group of minerals. Am Miner 53:1476-1489. Wachtman JB, Capps W, Mande J (1972). Biaxial flexure testing of ceramic substrates. J Mater Sci 7:188-194. Wyckoff RWG (1963). Crystal structures. Vol. 4. 2nd ed. New York: John Wiley and Sons, pp. 400-401.