Scanning Transmission Electron Microscopy/Energy-dispersive Spectroscopy Analysis of the Dentin Adhesive Interface Using a Labeled 2-Hydroxyethylmethacrylate Analogue

Abstract

In an attempt to compare the morphology of the dentin adhesive interface and the wetting and penetration of the adhesive in relation to the dentin surface, we studied four dentin adhesive systems using scanning transmission electron microscopy (STEM) and energy-dispersive spectroscopy (EDS). 2-Hydroxyethylmethacrylate (HEMA), a monomer common to many commercial dentin adhesive systems, was altered to produce a thiolated analogue (HETMA). Sulfur, traceable by EDS and STEM, was substituted for the oxygen atom in the backbone of the HEMA molecule. The resulting analogue, with solubility parameters and other wetting and physical properties very similar to those of HEMA, was applied to four sets of tooth specimens, each pre-treated with a different primer or etchant. Three separate pre-treatments-nitric acid, maleic acid, and citric acid/ferric chloride—created a demineralized zone approximately 1 to 3 μm thick at the dentin surface. The HETMA was found to permeate freely into this zone when either of the latter two pre-treatments was used. However, the band of dentin that was demineralized by the nitric acid pre-treatment appeared impermeable to the HETMA. The fourth pre-treatment, an alcohol-based solution including the phosphorus acid ester PENTA and HEMA, modified the smear layer of the tooth slightly and did not appear to demineralize the dentin. HETMA applied to the specimens pre-treated with PENTA and HEMA was clearly in intimate contact with the dentin or modified smear layer; however, it did not penetrate or diffuse into these areas. It did flow into the dentinal tubules, as was also evident with each of the other systems. It was concluded that the acid pre-treatment of the dentin greatly influenced the wetting behavior of the dentin adhesive and thus could substantially affect the resultant bond strength of the dentin adhesive systems.

Keywords

dentin bonding STEM/EDS analysis HEMA

Get full access to this article

View all access options for this article.

References

Barkmeier WW , Cooley RL (1991). Laboratory evaluation of adhesive systems. Oper Dent (Suppl 5):50-61.

Chappell RP , Eick JD ( 1994). Shear bond strength and scanning electron microscopic observation of six current dentinal adhesives. Quintessence Int 25:359-368.

Chappell R. , Eick J. , Theisen F. , Carracho AL (1991). Shear bond strength and scanning electron microscopic observation of current dentinal adhesives. Quintessence Int 22:831-839.

Davidson CL , DeGee A. (1984). Relocation of polymerization contraction stress by flow in dental composites. J Dent Res 63:146-148.

Eick J. ( 1992). Smear layer-materials surface. Proc Finn Dent Soc 88(Suppl 1):225- 242.

Eick J. , Cobb CM , Chappell R. , Spencer P. , Robinson SJ (1991). The dentinal surface: Its influence on dentinal adhesion, Part 1. Quintessence Int 22:967-977.

Eick JD , Robinson SJ , Cobb CM , Chappell R. , Spencer P. (1992). The dentinal surface: Its influence on dentinal adhesion, Part II. Quintessence Int 23:43-51.

Eick JD , Robinson SJ , Byerley TJ , Chappelow CC (1993a). Adhesives and nonshrinking dental resins of the future. Quintessence Int 24:632-640.

Eick JD , Robinson SJ , Chappell RP , Cobb CM , Spencer P. (1993b). The dentinal surface: Its influence on dentinal adhesion, Part III. Quintessence Int 24:571-582.

10.

Eliades G. , Palaghias G. , Vougiouklakis G. (1990). Surface reactions of adhesive on dentin. Dent Mater 6:208-216.

11.

Erickson RL (1989). Mechanism and clinical implications of bond formation for two dentin bonding agents. Am J Dent 2:117-123.

12.

Erickson RL (1992). Surface interactions of dentin adhesive materials . Oper Dent (Suppl 5):81-94.

13.

Gwinnett A. , Kanca J. (1992). Micromorphological relationship between resin and dentin in vivo and in vitro. Am J Dent 5:19-23.

14.

Munksgaard EC , Ine M. , Asmussen E. (1985). Dentin-polymer bond promoted by Gluma and various resins. J Dent Res 64:1409-1411.

15.

Nakabayashi N. (1982). Resin reinforced dentine due to infiltration of monomers into dentine at the adhesive interface. J Jpn Dent Mater 1:78-81.

16.

Nakabayashi N. (1992). The hybrid layer: A resin-dentin composite. Proc Finn Dent Soc 88(Suppl 1):321-329.

17.

Nakabayashi N. , Takarada K. (1992). Effect of HEMA on bonding to dentin. Dent Mater 8:125-130.

18.

Nakabayashi N. , Ashizawa M. , Nakamura M. (1992). Identification of a resin-dentin hybrid layer in vital human dentin created in vivo: Durable bonding to vital dentin. Quintessence Int 23:135-141.

19.

Pashley DH , Ciucchi B. , Sano H. , Horner JA (1993). Permeability of dentin to adhesive agents. Quintessence Int 24:618-631.

20.

Spencer P. , Byerley TJ , Eick J. , Witt J. ( 1992). Chemical characterization of the dentin/adhesive interface by Fourier Transform Infrared Photoacoustic Spectroscopy. Dent Mater 8:10-15.

21.

Stangel J. , Ostra E. , Domingue A. , Sacher E. , Bertrand L. (1991).

22.

Photoacoustic Fourier transform IR spectroscopic study of polymer-dentin interaction. In: Polymer-solid interfaces. Peredux JJ , Bertrand P , Breclas JL , editors. Bristol and Philadelphia: Institute of Physics Publishing, pp. 157-167.

23.

Suzuki M. , Kato H. , Wakumoto S. (1991). Vibrational analysis by Raman spectroscopy of the interface between dental adhesive resin and dentin. J Dent Res 70:1092-1097.

24.

Van Krevelen DW (1990). Properties of polymers, their correlation with chemical structure: Their numerical estimation and prediction from additive group contributions. 3rd ed. Amsterdam: Elsevier, p. 291.

25.

Van Meerbeek B. , Inokoshi S. , Braem M. , Lambrechts P. , Vanherle G. (1992a). Morphological aspects of the resin-dentin interdiffusion zone with different dentin adhesive systems. J Dent Res 71:1530-1540.

26.

Van Meerbeek B. , Vanherle G. , Lambrechts P. , Braem M. (1992b). Dentin- and enamel-bonding agents. Perio Rest Dent 2 :117-127.

27.

Van Meerbeek B. , Dhem A. , Goret-Nicaise M. , Braem M. , Lambrechts P. , Vanherle G. (1993a). Comparative SEM and TEM examination of the ultrastructure of the resin-dentin interdiffusion zone. J Dent Res 72:495-501.

28.

Van Meerbeek B. , Mohrbacher H. , Celis JP , Roos JR , Braem M. , Lambrechts P. , et al. (1993b). Chemical characterization of the resin-dentin interface by micro-Raman spectroscopy. J Dent Res 72:1423-1428.

29.

Walshaw PR , McComb D. (1994). SEM evaluation of the resin-dentin interface with proprietary bonding agents in human subjects. J Dent Res 73:1079-1087.