The paper deals with the mechanical degradation of composite material components in seawater at room temperature. In particular, this study compares quasi-static and dynamic behaviour of carbon fiber/vinyl ester components, dry and water saturated in a saline environment at 3% to simulate the seawater exposition. At this regard, short-beam shear, flexural and low-velocity impact tests were systematically performed before and after the conditioning of the material under examination. Finally, the damage of the impacted specimens was carefully analyzed by visual inspections and ultrasound investigations. Despite a very low water absorption, the analyses allow to highlight different phenomena, reflecting on variations in the mechanical properties and in the extent of the damage of the investigated samples.
MenailYEl MahiAAssararM, et al.
The effects of water aging on the mechanical properties of glass-fiber and kevlar-fiber epoxy composite materials. Mechanika2009;
76: 28–32.
2.
BeheraADehuryJThawareMM.A comparative study on laminated and randomly oriented luffa-kevlar reinforced hybrid composites. J Nat Fibers2019;
16: 237–244.
3.
BeheraAThawreMMBallalA.Effect of matrix crack generation on fatigue life of CFRP multidirectional laminates. Mater Today Proc2018;
5: 20078–20084.
4.
MouritzAPGellertEBurchillP, et al.
Review of advanced composite structures for naval ships and submarines. Compos Struct2001;
53: 21–42.
5.
Williams C. Effect of water absorption on the room temperature properties of carbon fiber and glass fiber reinforced polymer composites. In: DTRC/SME-88-85, David Taylor Research Center, Annapolis, MD, December 1988.
6.
SalaG.Composite degradation due to fluid absorption. Compos Part B Eng2000;
31: 357–373.
7.
BaoLRYeeAF.Effect of temperature on moisture absorption in a bismaleimide resin and its carbon fiber composites. Polymer (Guildf)2002;
43: 3987–3997.
8.
NakamuraTSinghRPVaddadiP.Effects of environmental degradation on flexural failure strength of fiber reinforced composites. Exp Mech2006;
46: 257–268.
9.
KumarBGSinghRPNakamuraT.Degradation of carbon fiber-reinforced epoxy composites by ultraviolet radiation and condensation. J Compos Mater2002;
36: 2713–2733.
10.
CaprinoGLoprestoV.The significance of indentation in the inspection of carbon fibre-reinforced plastic panels damaged by low-velocity impact. Compos Sci Technol2000;
60: 1003–1012.
11.
LoprestoVLangellaAPapaI.Dynamic load on composite laminates in the presence of water. Polym Eng Sci2017;
57: 613–620.
12.
LoprestoVPapaILangellaA.Residual strength evaluation after impact tests in extreme temperature conditions. New equipment for CAI tests. Compos Part B Eng2017;
127: 44–52.
ShivakumarKNSwaminathanGSharpeM.Carbon/vinyl ester composites for enhanced performance in marine applications. J Reinf Plast Compos2006;
25: 1101–1116.
17.
GellertEPTurleyDM.Seawater immersion ageing of glass-fibre reinforced polymer laminates for marine applications. Compos Part A Appl Sci Manuf1999;
30: 1259–1265.
18.
WeitsmanYJElahiM.Effects of fluids on the deformation, strength and durability of polymeric composites -- an overview. Mech Time-Dependent Mater2000;
4: 107–126.
LoprestoVLangellaAPapaI.Interaction of water with carbon fiber reinforced polymer laminates under dynamic loading conditions. J Mater Eng Perform2019;
28: 3220–3227.
21.
PapaIFormisanoALoprestoV, et al.
Water ageing effects on the mechanical properties of flax fibre fabric/polypropylene composite laminates. J Compos Mater2020;
54: 3481–3489.
22.
BerketisKTzetzisD.Long-term water immersion ageing characteristics of GFRP composites. J Mater Sci2009;
44: 3578–3588.
23.
HodgkinsonJM. Testing the strength and stiffness of polymer matrix composites. In: Robinson P, Greenhalgh E and Pinho S (eds) Failure mechanisms in polymer matrix composites. Amsterdam: Elsevier, 2012, pp.129–182.
24.
PapaILangellaALoprestoV.CFRP laminates under low‐velocity impact conditions: influence of matrix and temperature. Polym Eng Sci2019;
59: 2429–2437.
25.
YuYLiPSuiG, et al.
Effects of hygrothermal aging on the thermal-mechanical properties of vinylester resin and its pultruded carbon fiber composites. Polym Compos2009;
30: 1458–1464.
26.
GarciaRCastellanosAPrabhakarP.Influence of arctic seawater exposure on the flexural behavior of woven carbon/vinyl ester composites. J Sandw Struct Mater2019;
21: 1190–1208.
27.
DaleMAchaBACarlssonLA.Low velocity impact and compression after impact characterization of woven carbon/vinylester at dry and water saturated conditions. Compos Struct2012;
94: 1582–1589.