The main purpose of this study was to investigate mechanical and thermal performance of polylactide specimens against UV irradiation; first when only adding benzotriazole benzotriazole-based organic UV absorber (UVA), micro (200 nm) and nano (50 nm) sized titania (TiO2) particles alone, and then to reveal possible synergism when they are added together. Compounds were prepared by twin-screw extruder melt mixing, while the 2 mm thick specimens were shaped by compression molding. Specimens were exposed to UV irradiation under fluorescent lamps (UVB-313) with 0.50 W/m2 for the periods of 12 and 24 days. Changes in the performance of UV irradiated specimens were evaluated in terms of % weight loss, changes in color and chemical structure, including the decreases in the mechanical and thermal properties. Various tests and analysis revealed that synergistic benefits of using micro and nano TiO2 particles together with benzotriazole-type UVA were not only due to the effective stiffening, strengthening and toughening actions of titania particles, but also due to their very significant “UV screening” actions absorbing the photons of the UV irradiation, thus decreasing the degree of the detrimental photodegradation reactions leading to chain scissions in their PLA matrix.
FinkenstadtVLTisseratB. Poly (lactic acid) and osage orange wood fiber composites for agricultural mulch films. Ind Crops Prod2010; 31: 316–320.
2.
ChenYGeeverLMKillionJA, et al.Review of multifarious applications of poly (lactic acid). Polym Plast Technol Eng2016; 55: 1057–1075.
3.
Niaounakis M. Automotive applications. In: Biopolymers: applications and trends. Amsterdam: Elsevier, pp. 257–289.
4.
TsujiHEchizenYNishimuraY. Photodegradation of biodegradable polyesters: a comprehensive study on poly(l-lactide) and poly(ɛ-caprolactone). Polym Degrad Stab2006; 91: 1128–1137.
5.
JanorkarAVMettersATHirtDE. Degradation of poly(L-lactide) films under ultraviolet-induced photografting and sterilization conditions. J Appl Polym Sci2007; 106: 1042–1047.
6.
SavarisMSantosVdosBrandaliseRN. Influence of different sterilization processes on the properties of commercial poly(lactic acid). Mater Sci Eng C2016; 69: 661–667.
7.
McNeillICLeiperHA. Degradation studies of some polyesters and polycarbonates – 2. Polylactide: degradation under isothermal conditions, thermal degradation mechanism and photolysis of the polymer. Polym Degrad Stab1985; 11: 309–326.
8.
IkadaE. Photo- and bio-degradable polyesters. Photodegradation behaviors of aliphatic polyesters. J Photopolym Sci Technol1997; 10: 265–270.
9.
CopinetABertrandCGovindinS, et al.Effects of ultraviolet light (315 nm), temperature and relative humidity on the degradation of polylactic acid plastic films. Chemosphere2004; 55: 763–773.
10.
Santonja-BlascoLRibes-GreusAAlamoRG. Comparative thermal, biological and photodegradation kinetics of polylactide and effect on crystallization rates. Polym Degrad Stab2013; 98: 771–784.
11.
KaynakCKaygusuzI. Consequences of accelerated weathering in polylactide nanocomposites reinforced with halloysite nanotubes. J Compos Mater2016; 50: 365–375.
12.
KaynakCSarıB. Accelerated weathering performance of polylactide and its montmorillonite nanocomposite. Appl Clay Sci2016; 121: 86–94.
13.
KaynakCErdoganAR. Mechanical and thermal properties of polylactide/talc microcomposites: before and after accelerated weathering. Polym Adv Technol2016; 27: 812–822.
14.
VarsavasSDKaynakC. Weathering degradation performance of PLA and its glass fiber reinforced composite. Mater Today Commun2018; 15: 344–353.
15.
KaynakCDoguB. Effects of accelerated weathering in polylactide biocomposites reinforced with microcrystalline cellulose. Int Polym Process2016; 31: 410–422.
16.
GugumusF. Possibilities and limits of synergism with light stabilizers in polyolefins 2. UV absorbers in polyolefins. Polym Degrad Stab2002; 75: 309–320.
17.
Silvia Díaz-CruzMLlorcaMBarcelóD, et al.Organic UV filters and their photodegradates, metabolites and disinfection by-products in the aquatic environment. Trends Anal Chem2008; 27: 873–887.
18.
MuasherMSainM. The efficacy of photostabilizers on the color change of wood filled plastic composites. Polym Degrad Stab2006; 91: 1156–1165.
XiangXChaiRChenS, et al.Effect of the combination of a benzotriazole-type ultraviolet absorber with thermal stabilizers on the photodegradation of poly(vinyl chloride). J Vinyl Addit Technol2010; 21: 175–182.
21.
ZhangMXieWTangB, et al.Synthesis of TiO2 &SiO 2 nanoparticles as efficient UV absorbers and their application on wool. Text Res J2017; 87: 1784–1792.
22.
LiYChenCLiJ, et al.Photoactivity of poly(lactic acid) nanocomposites modulated by TiO2 nanofillers. J Appl Polym Sci2014; 131: 1–7.
23.
ManCZhangCLiuY, et al.Poly (lactic acid)/titanium dioxide composites: preparation and performance under ultraviolet irradiation. Polym Degrad Stab2012; 97: 856–862.
24.
XiuHQiXBaiH, et al.Simultaneously improving toughness and UV-resistance of polylactide/titanium dioxide nanocomposites by adding poly(ether)urethane. Polym Degrad Stab2017; 143: 136–144.
NakayamaNHayashiT. Preparation and characterization of poly(l-lactic acid)/TiO2 nanoparticle nanocomposite films with high transparency and efficient photodegradability. Polym Degrad Stab2007; 92: 1255–1264.
27.
ZhuangWLiuJZhangJH, et al.Preparation, characterization, and properties of TiO2/PLA nanocomposites by in situ polymerization. Polym Compos2009; 30: 1074–1080.
28.
RabieSTNadaAA. Glucoside/(UV absorber) mixtures as photostabilizers for rigid PVC. J Vinyl Addit Technol2008; 14: 79–83.
29.
RajanVVWäberRWieserJ. Influence of different types of UV absorber/UV stabilizer combination on the photodegradation of PC/ABS blend. J Appl Polym Sci2012; 124: 4007–4015.
30.
ChangSTChouPL. Photodiscoloration inhibition of wood coated with UV-curable acrylic clear coatings and its elucidation. Polym Degrad Stab2000; 69: 355–360.
31.
KuoCJLanWLChenC, et al.Property modification and process parameter optimization design of polylactic acid composite materials. Part I: polylactic acid toughening and photo-degradation modification and optimized parameter design. Text Res J2015; 85: 13–25.
32.
ShiQFGaoJYZhaoDD, et al.Synergism effect between modified carbon black and organic ultraviolet absorber in polymer matrix for ultraviolet protection. J Appl Polym Sci2010; 116: 2566–2572.
33.
BlanchardVBlanchetP. Color stability for wood products during use: effects of inorganic nanoparticles. Bioresources2011; 6: 1219–1229.
34.
AuclairNRiedlBBlanchardV, et al.Improvement of photoprotection of wood coatings by using inorganic nanoparticles as ultraviolet absorbers. Forest Prod J2011; 61: 20–27.
35.
ForsthuberBMüllerUTeischingerA, et al.Chemical and mechanical changes during photooxidation of an acrylic clear wood coat and its prevention using UV absorber and micronized TiO2. Polym Degrad Stab2013; 98: 1329–1338.
36.
MahltigBBöttcherHRauchK, et al.Optimized UV protecting coatings by combination of organic and inorganic UV absorbers. Thin Solid Films2005; 485: 108–114.
37.
YaoQDuMSunM. Improving anti-aging coatings by coupling of organic and inorganic ultraviolet absorbers. Adv Mater Res2013; 652–654: 1723–1727.
38.
SantosRMBotelhoGLMachadoAV. Development of acrylonitrile-butadiene-styrene composites with enhanced UV stability. J Mater Sci2014; 49: 510–518.
39.
Lin-VienDColthupNBFateleyWG, et al.The handbook of infrared and raman characteristic frequencies of organic molecules, San Diego, CA: Academic Press, 1991.
40.
FischerEWSterzelHJWegnerG. Investigation of the structure of solution grown crystals of lactide copolymers by means of chemical reactions. Kolloid Zeitschrift Zeitschrift für Polym1973; 251: 980–990.