Fire performance of composites made from carbon/phenolic prepregs with nanoclays

Abstract

This article describes the development of fire resistant composite materials based on phenolic resin and carbon fibers. Two types of composites were developed, with neat phenolic resin and with phenolic resin/modified bentonite. Composite materials were processed from prepregs by compression molding and were characterized by density, fiber content, cone calorimeter test, scanning electron microscope, and mechanical properties before and after the exposure to fire. In both cases, high fiber content materials were developed, about 75% by volume. The addition of clay improved some fire properties such as the peak of the heat release rate and the residual mass of the burned samples. Also, the bentonite-modified composite required higher time to develop the maximum of the heat release rate in the material; therefore, the addition of modified nanoclays improved the fire properties of the developed composites. Regarding to mechanical behavior the modified composites presented low modulus and flexural stiffness than the unmodified materials, and presented a higher decreased in the properties after fire, which could be related with the different fiber content in both composites.

Keywords

Composite phenolic resin carbon fiber fire properties

Get full access to this article

View all access options for this article.

References

Reghunadhan Nair

. Advances in addition-cure phenolic resins. Progr Polym Sci 2004; 29: 401–498.

Natali

Monti

Puglia

et al.

Ablative properties of carbon black and MWNT/phenolic composites: A comparative study. Compos A 2012; 43: 174–182.

Gardziella A, Pilato LA and Knop A. Phenolic resins: Chemistry, applications, standardization, safety and ecology. Ed. Heidelberg, Germany: Springer, 2000.

Feih

Mathys

et al.

Influence of water content on failure of phenolic composites in fire. Polym Degrad Stab 2008; 93: 376–382.

Schmidt DL and Craig RD. Advanced carbon fabric/phenolic for thermal protection applications. Technical Report of the Air Force Wright Aeronautical laboratories, Ohio, US, AFWAL-TR-81-4136, 1982.

Park

Cho

Kang

. A comparison of the interfacial, thermal, and ablative properties between spun and ﬁlament yarn type carbon fabric/phenolic composites. Carbon 2004; 42: 795–804.

Noland RL. Ablative and insulative structures and microcellular carbon fibers forming same. Patent 5298313, USA, 1994.

Perret

Schartel

Sot

et al.

Novel DOPO-based flame retardants in high-performance carbon fibre epoxy composites for aviation. Eur Polym J 2011; 47: 1081–1089.

Bahramian

Kokabi

. Polymer nanocomposites as ablative materials. Polymer green flame retardants, Amsterdam: Elsevier, 2014.

10.

Mc Allister LE and Hill JE. Ablative composition. Patent 4656095, USA, 1987.

11.

Natali

Monti

Kenny

et al.

A nanostructured ablative bulk molding compound: Development and characterization. Compos Part A 2011; 42: 1197–1204.

12.

Bian

Xiao

Zeng

et al.

Microstructural interpretation of the ablative properties of phenolic–quartz hybrid fabric reinforced phenolic resin composites. Mater Des 2014; 62: 424–429.

13.

Koo

Pilato

Wissler

. Polymer nanostructured materials for propulsion systems. J Spacecraft Rockets 2007; 44: 1250–1262.

14.

Tate

Gaikwad

Theodoropoulou

et al.

Carbon/phenolic nanocomposites as advanced thermal protection material in aerospace applications. J Compos 2013; 2013: 1–9.

15.

Wang

Kwon

et al.

Ablative and mechanical evaluation of CNT/phenolic composites by thermal and microstructural analyses. Compos B 2014; 60: 597–602.

16.

Bahramian

Kokabi

. Ablation mechanism of polymer layered silicate nanocomposite heat shield. J Hazard Mater 2009; 166: 445–454.

17.

Asaro

Rivero

Manfredi

et al.

Development of carbon fiber/phenolic resin prepregs modified with nanoclays. J Compos Mater 2016; 50: 1287–1300.

18.

Manfredi

De la Osa

Galego Fernández

et al.

Structure properties relationship for resols with different formaldehyde/phenol molar ratio. Polymer 1999; 40: 3867–3875.

19.

Ollier

Rodriguez

Alvarez

. Unsaturated polyester/bentonite nanocomposites: Influence of clay modification on final performance. Compos A 2013; 48: 137–143.

20.

Manfredi

Puglia

Tomasucci

et al.

Influence of clay modification on the properties of resol nanocomposites. Macromol Mater Eng 2008; 293: 878–886.

21.

Lei

Lian

. Cure kinetics of aqueous phenol formaldehyde resins used for oriented strandboard manufacturing: Analytical technique. J Appl Polym Sci 2006; 100: 1642–1650.

22.

Erdal

Guceri

Danforth

. Impregnation molding of particle filled preceramic polymers: process modeling. J Am Ceram Soc 1999; 82: 2017–2028.

23.

Mouritz

Mathys

Gibson

. Heat release of polymer composites in fire. Compos A: Appl Sci Manuf 2006; 37: 1040–1054.

24.

Rivero

Villanueva

Manfredi

. Furan resin as a replacement of phenolics: influence of the clay addition on its thermal degradation and fire behavior. Fire Mater 2014; 38: 683–694.

25.

Zanetti

Kashiwagi

Falqui

et al.

Cone calorimeter combustion and gasification studies of polymer layered silicate nanocomposites. Chem Mater 2002; 14: 881–887.

26.

Lewin

. Reflections on migration of clay and structural changes in nanocomposites. Polym Adv Technol 2006; 17: 758–758.

27.

Koo JH, Muskopf B, Sorathia U, et al. Fire performance of polymeric matrix composites for marine applications. In: Proceedings of 2001 fire and materials conference, interscience communication, London, 2001.

28.

Koo

Muskopf

McCord

et al.

Characterization of fire safe polymer matrix composites for naval applications. Int’l SAMPE Symp Exhib 2001; 46: 2170–2182.

29.

Koo

. Polymer nanocomposites: Processing, characterization, and applications, New York: McGraw-Hill Professional, 2006, pp. 176–182.

30.

Song

Wang

Meng

et al.

Influences of catalysis and dispersion of organically modified montmorillonite on flame retardancy of polypropylene nanocomposites. J Appl Polym Sci 2007; 106: 3488–3488.

31.

Monti

Hoydonckx

Stappers

et al.

Thermal and combustion behavior of furan resin/silica nanocomposites. Eur Polym J 2015; 67: 561–569.

32.

Mouritz

. Post-fire flexural properties of fibre-reinforced polyester, epoxy and phenolic composites. J Mater Sci 2002; 37: 1377–1386.

33.

Mouritz

Mathysb

Gardiner

. Thermomechanical modelling the fire properties of fibre–polymer composites. Compos B 2004; 35: 467–474.

34.

Katsoulis

Kandola

Myler

et al.

Post-fire flexural performance of epoxy-nanocomposite matrix glass fibre composites containing conventional flame retardants. Compos A 2012; 43: 1389–1399.