Effect of interference percentage on damage mechanism of carbon fiber reinforced plastics laminate during interference-fit bolt installation

Abstract

The interference-fit joint of composite laminates is widely used in assembly of thin-walled components in aviation product, but the interference percentage has a significant effect on squeezed damage which may reduce structural reliability. An investigation is conducted into the in-plane stress distribution and initial damage mechanism of symmetrical carbon fiber reinforced plastics laminates during the interference-fit bolt installation process. Considering the elastic deformation of the bolt, a general stress distribution model around the interference-fit joint is established with complex potential method. The initial damage mechanism of carbon fiber reinforced plastics laminates is characterized and critical interference percentages without damage are obtained with the mixed damage criteria. The effects of ply orientation and interference percentage on damage mechanism of each individual layer are discussed. Then, extensive finite element models with USDFLD subroutine of interference fit process are used to analyze and simulate the stress distribution and squeezed damage which are validated by strain measurement and micrographs by experiments subsequently. It is observed that theoretical solutions fall within the finite element results. The matrix tensile damage occurs first, and the critical interference percentages decrease from 1.10% to 0.85% with bolt diameters varying from 4 to 10 mm.

Keywords

Carbon fiber reinforced plastics interference fit joint stress distribution damage initiation critical interference percentages

Get full access to this article

View all access options for this article.

References

Cao

Cardew-Hall

. Interference-fit riveting technique in fiber composite laminates. Aerosp Sci Technol 2006; 10: 327–330.

Bunin

. Critical composite joint subcomponents: analysis and rest results, Washington, DC: National Aeronautics and Space Administration, 1983.

Pradhan

Babu

. Assessment of beneficial effects of interference-fit in pin-loaded FRP composites. J Reinf Plast Comp 2007; 26: 771–788.

Lekhnitskij

. Theory of elasticity of an anisotropic body, Moscow: Mir Publishers, 1981.

De Jong

. Stresses around pin-loaded holes in elastically orthotropic or isotropic plates. J Compos Mater 1977; 11: 313–331.

De Jong

. On the calculation of stresses in pin-loaded anisotropic plates, Delft: Delft University of Technology, 1987.

Grüber

Hufenbach

Kroll

. Stress concentration analysis of fibre-reinforced multilayered composites with pin-loaded holes. Compos Sci Technol 2007; 67: 1439–1450.

Toubal

Karama

Lorrain

. Stress concentration in a circular hole in composite plate. Compos Struct 2005; 68: 31–36.

Di Scalea

Cloud

Cappello

. A study on the effects of clearance and interference fits in a pin-loaded cross-ply FGRP laminate. J Compos Mater 1998; 32: 783–802.

10.

Whitworth

. A stiffness degradation model for composite laminates under fatigue loading. Compos Struct 1998; 40: 95–101.

11.

Tserpes

Labeas

Papanikos

. Strength prediction of bolted joints in graphite/epoxy composite laminates. Compos B 2002; 33: 521–529.

12.

Chang

. A progressive damage model for laminated composites containing stress concentrations. J Compos Mater 1987; 21: 834–855.

13.

Chishti

Wang

Thomson

. Numerical analysis of damage progression and strength of countersunk composite joints. Compos Struct 2012; 94: 643–643.

14.

Camanho

Matthews

. Delamination onset prediction in mechanically fastened joints in composite laminates. J Compos Mater 1999; 33: 906–927.

15.

Zhao

Cho

. Damage initiation and propagation in composite shells subjected to impact. Compos Struct 2007; 78: 91–100.

16.

Maimí

Camanho

Mayugo

. A continuum damage model for composite laminates: part I – constitutive model. Mech Mater 2007; 39: 897–908.

17.

Buchanan

Gosse

Wollschlager

. Micromechanical enhancement of the macroscopic strain state for advanced composite materials. Compos Sci Technol 2009; 69: 1974–1978.

18.

Pipes

Gosse

. An onset theory for irreversible deformation in composite materials, Edinburgh: ICCM-17, 2009, pp. 27–31.

19.

Song

Zhang

. Micromechanical analysis for microscopic damage initiation in fiber/epoxy composite during interference-fit pin installation. Mater Design 2016; 89: 36–49.

20.

Wei

Jiao

Jia

. The effect of interference fit size on the fatigue life of bolted joints in composite laminates. Compos B Eng 2013; 53: 62–68.

21.

Kim

Hennigan

Kim

. Fatigue enhancement by interference-fit in a pin-loaded glass fibre-reinforced plastics laminate. Proc Inst Mech Eng C J Mech Eng Sci 2012; 226: 1437–1446.

22.

Kim

Shim

. An experimental and numerical study on the interference-fit pin installation process for cross-ply glass fiber reinforced plastics (GFRP). Compos B Eng 2013; 54: 153–162.

23.

Song

Zhang

. Stress distribution modeling for interference-fit area of each individual layer around composite laminates joint. Compos B Eng 2015; 78: 469–479.

24.

Muskhelishvili

. Some basic problems of the mathematical theory of elasticity, Berlin: Springer Netherlands, 1977.

25.

Jones

. Mechanics of composite materials, 2nd ed. Boca Raton, FL: CRC Press, 1998.

26.

Kim

Hwang

Kim

. Progressive failure analysis of pin-loaded laminated composites using penalty finite element method. AIAA J 1998; 36: 75–80.

27.

Soni

. A comparative study of failure envelopes in composite laminates. J Reinf Plast Comp 1983; 2: 34–42.

28.

Swanson

. Introduction to design and analysis with advanced composite materials, 1st ed. Upper Saddle River, NJ: Prentice Hall, 1997.