Although carbon fiber-reinforced silicon carbide matrix composites fabricated using the liquid silicon infiltration method exhibit high thermal and oxidation resistances, their physical characteristics are limited because of the presence of unreacted, free Si within the materials. To resolve this problem, ingots prepared by alloying Cr with Si in ratios of 0, 5, 10, 25, and 50 at% were melted and made to infiltrate the composite, resulting in the formation of CrSi2 in the unreacted, free Si region without degrading the composite’s properties. The CrSi2 in the composite material reduced the amount of free Si and caused minimal variation in the flexural strength while significantly improving the fracture toughness of the composite. The results of scanning electron microscopy and transmission electron microscopy analyses indicated that the improvement in the fracture toughness was due to the presence of an amorphous interlayer between the Si and CrSi2 phases, as well as because of a stress field surrounding the CrSi2 phase.
KrenkelWBerndtF. C/C–SiC composites for space applications and advanced friction systems. Mater Sci Eng A2005; 412: 177–181.
2.
XuYZhangYChengL. Preparation and friction behavior of carbon fiber reinforced silicon carbide matrix composites. Cera Inter2007; 33: 439–445.
3.
EsfehanianMGuensterJHeinrichJG. High-temperature mechanical behavior of carbon–silicide–carbide composites developed by alloyed melt infiltration. J Euro Cera Soc2008; 28: 1267–1274.
4.
JangBKSakkaY. Influence of microstructure on the thermophysical properties of sintered SiC ceramics. J Allo Comp2008; 463: 493–497.
5.
LeeSPKatohYKohyamaA. Microstructure analysis and strength evaluation of reaction sintered SiC/SiC composites. Scr Mater2001; 44: 153–157.
6.
KochendörferR. Ceramic matrix composites from space to earth: the move from prototype to serial production. Cera Eng Sci Proc2001; 22: 11–22.
7.
Schulte-FischedickJZernAMayerJ. The morphology of silicon carbide in C/C–SiC composites. Mater Sci Eng2002; A332: 146–152.
8.
ZhangYXiaoZWangJ. Effect of pyrocarbon content in C/C preforms on microstructure and mechanical properties of the C/C–SiC composites. Mater Sci Eng2009; A502: 64–69.
9.
Gadow R. Die Silizierung des Kohlenstoffs. PhD Thesis, University of Karlsruhe, GER, 1986.
10.
Braue W, Pleger R and Weiss R. The nanoscale microstructure of 2D C/C–SiC ceramic composites processed via silicon capillary impregnation. Proc 2nd Int Conf High Temp Cera Matrix Comp 1995: 275–280.
11.
Gern F. Capillary infiltration behavior of liquid silicization from C/C composite. PhD Thesis, University of Stuttgart, GER, 1995.
12.
Schulte-FischedickJSeizSLűtzenburgerN. The crack development on the micro- and mesoscopic scale during the pyrolysis of carbon fibre reinforced plastics to carbon/carbon composites. Compos: Part A2007; 38: 2171–2181.
13.
BulauJR. AE monitoring for control of carbon-carbon pyrolysis. Proc IEEE Ultra Symp1988, pp. 1057–1063.
14.
FischerDSSchuhCA. Microstructure and fracture of anomalous eutectic silicon-disilicide composites. Intermetallics2011; 19: 1661–1673.
15.
Fischer DS. Development of in-situ toughened silicon-rich alloys: a new class of castable engineering ceramics. PhD Thesis, Massachusetts Institute of Technology, USA, 2005.
16.
GilmanJJ. Direct measurements of the surface energies of crystals. J App Phys1960; 31: 2208–2208.
17.
JaccodineRJ. Surface energy of germanium and silicon. J Elec Soc1963; 110: 524–527.
18.
GadowRFitzerE. Fiber-reinforced silicon carbide. Am Cer Soc Bull1986; 65: 326–335.
19.
Forrest CW, Kennedy P and Shennan JV. The fabrication and properties of self-bonded silicon carbide bodies. In: Proceedings of the fifth Symposium on Special Ceramics, The British Ceramic Research Association 1972: 99–123.
20.
TrantinaGGMehanRL. High-temperature time-dependent strength of a Si/SiC composite. J Am Cer Soc1977; 60: 177–178.
21.
XuaSQiaoGLiD. Reaction forming of silicon carbide ceramic using phenolic resin derived porous carbon preform. J Eur Cer Soc2009; 29: 2395–2402.
22.
EsfehanianMGuensterJHeinrichJG. High-temperature mechanical behavior of carbon–silicide–carbide composites developed by alloyed melt infiltration. J Eur Cer Soc2008; 28: 1267–1274.
ItoKMoriwakiMNakatomoT. Plastic-deformation of single-crystals of transition-metal disilicide. Mat Sci Eng A-Str Mat Prop Micro Proc1997; 233: 33–43.
25.
NakamuraM. Elastic constants of some transition-metal-disilicide single crystals. Metal Mat Trans A1994; 25A: 331–340.
26.
Hansson T and Warren R. Particle and whisker reinforced brittle matrix composites. In: Comprehensive composite material vol 4. Oxford, UK: Elsevier Science Ltd., Cambridge University Press, 2000, pp. 579–609.
27.
EomJHKimYWJungBJ. Effect of alkaline earth additives on the flexural strength of silicon oxycarbide-bonded silicon carbide ceramics. Cer Int2013; 39: 2083–2091.
28.
DengZYSheJInagakiY. Reinforcement by crack-tip blunting in porous ceramics. J Eur Cer Soc2004; 24: 2055–2059.
29.
Lawn B. Fracture of brittle solids. New York, NY: Cambridge University Press, 1993, pp. 194–206.
30.
KulikovskyVVorlíčekVBoháčP. Mechanical properties of amorphous and microcrystalline silicon films. Thin Solid Films2008; 516: 5368–5375.