Modeling of dynamic mechanical properties of epoxy and epoxy-phenolic reinforced with multi-wall carbon nanotubes

Abstract

The viscoelastic properties of nanocomposites based on epoxy and epoxy-phenolic blend matrix reinforced with multi-wall carbon nanotubes were studied. The content of carbon nanotube (0.2 and 0.5 wt.%) and its surface state (pristine vs. oxidized) varied. The characterization of the nanocomposites was done by means of infrared spectroscopy and chemical methods. From the viscoelastic properties of nanocomposites, characteristic properties such as storage modulus (E₀), tan δ and damping peak (tan δ) were obtained. The void content was also determined. Also, Weibull statistics are used to represent the failure of secondary bonds during the relaxation processes that lead to stiffness change over the full range of use temperatures. The incorporation of phenolic resin to an epoxy matrix leads to an increase of the relaxation modulus. The glass transition temperature of the epoxy-phenolic nanocomposites decrease when it is incorporated carbon nanotubes, independently of its state (pristine or oxidized).

Keywords

Epoxy/MWCNT phenolic/epoxy/MWCNT dynamic mechanical properties relaxation modulus modeling

Get full access to this article

View all access options for this article.

References

Jin

Park

. Thermal and mechanical interfacial properties of epoxy composites based on functionalized carbon nanotubes. Mater Sci Eng A 2011; 528: 8517–8522.

Thostenson

Ren

Chou

. Advances in the science and technology of carbon nanotubes and their composites: a review. Compos Sci Technol 2001; 61: 1899–1912.

Montazeri

Javadpour

Khavandi

. Mechanical properties of multi-walled carbon nanotube/epoxy composites. Mater Des 2010; 31: 4202–4208.

Siddiqui

Marom

. Dispersion and functionalization of carbon nanotubes for polymer-based nanocomposites: a review. Compos A: Appl Sci Manuf 2010; 41: 1345–1367.

Montazeri

. Viscoelastic and mechanical properties of multi-walled carbon nanotube/epoxy composites with different nanotube content. Mater Des 2011; 32: 2301–2307.

Manfredi

Claro

Kenny

. Processing and properties of resol and epoxy blends for resin transfer molding. Polym Compos 1999; 20: 675–682.

Sturiale

Vázquez

Cisilino

. Enhancement of the adhesive joint strength of the epoxy–amine system via the addition of a resol-type phenolic resin. Int J Adhes Adhesives 2007; 27: 156–164.

Mahieux

Reifsnider

. Property modeling across transition temperatures in polymers: a robust stiffness-temperature model. Polym Sci USSR 1982; 24: 2953–2958.

Aklonis

MacKnight

. Introduction to polymer viscoelasticity, 2nd ed. New York: Wiley, 1983.

10.

Alvarez

Gibson

Vazquez

Modeling of dynamical-mechanical properties of vinyl-ester and unsaturated polyester with glass fibre reinforced composites. In: Moeller

(ed.) Progress in polymer degradation and stability research, New York: Nova Publishers, 2008, pp. 343–357.

11.

Shin

J-W

Jeun

J-P

Kang

P-H

. Fabrication and characterization of the mechanical properties of multi-walled carbon nanotube-reinforced epoxy resins by e-beam irradiation. J Ind Eng Chem 2009; 15: 555–560.

12.

Zhang

Zhao

Sun

. Performance enhancement for quasi-solid-state dye-sensitized solar cells by using acid-oxidized carbon nanotube-based gel electrolytes. Electrochem Acta 2012; 61: 185–190.

13.

Sheng

Shao

Ren

. Kinetics and thermodynamics of adsorption of ionizable aromatic compounds from aqueous solutions by as-prepared and oxidized multi-walled carbon nanotubes. J Hazard Mater 2010; 178: 505–516.

14.

Yang

Shao

. Adsorption of Ni(II) on oxidized multi-walled carbon nanotubes: effect of contact time, pH, foreign ions and PAA. J Hazard Mater 2009; 166: 109–116.

15.

Puglia

Manfredi

Vazquez

. Thermal degradation and fire resistance of epoxy–amine–phenolic blends. Polym Degrad Stab 2001; 73: 521–527.