Investigations were carried out on glass-epoxy composite specimens with varied fibre orientations (±2° to ±88°), prepared by both braided and filament winding techniques. The experimental strength and stiffness of these composites while exhibiting similar trends, correlated well with those predicted by classical laminate theory. The filament wound composites exhibited (20–40%) initial higher properties vis-a-vis the braided composites, while a correlation index between the experimental and theoretical values has been evolved.
LubinG. Handbook of composites, New York: van Nostrand Reinhold, 1982.
2.
RosatoDVGroveCS. Filament winding: its development, manufacturing and design, 2nd ed. New York: Inter science publishers, 1964.
3.
SandersLR. Braiding – a mechanical means of composite fabrication. SAMPE Q1977; 8(2): 38–44.
4.
PotluriPMananAFranckeM. Flexural and torsional behaviour of biaxial and triaxial braided composite structures. Compos Struct2006; 75(1–4): 377–386.
5.
CharleboisKMBoukhiliRZebdiO. Evaluation of the physical and mechanical properties of braided fabrics and their composites. J Reinf Plast Compos2005; 24(14): 1539–1554.
6.
CareyJMunroMFahimA. Regression based model for elastic constants of 2-D braided/woven open mesh angle ply composites. Polym Compos2005; 26(2): 152–164.
7.
ZebdiOBoukhiliRTrochuF. An inverse approach based on laminate theory to calculate the mechanical properties of braided composites. J Reinf Plast Compos2009; 28(23): 2911–2930.
8.
TakahashiKBanKSakaiT. Mechanical properties of FRP-FW pipes. Compos Struct1984; 2: 91–104.
9.
SodenPDKitchingRTsePC. Influence of winding angle on the strength and deformation of filament-wound composite tubes subjected to uniaxial and biaxial loads. Compos Sci Technol1993; 46: 363–378.
10.
SrikanthLRaoRMVGK. Concurrent studies on braided and filament wound carbon fibre composites – a comparative appraisal. J Reinf Plast Compos2011; 30(16): 1359–1365.
11.
ASTM D 2290-00. Apparent hoop tensile strength of plastic or reinforced plastic pipe by split disk method, 2000.
12.
ElkinRA. Compression testing of NOL rings. In: Symposium on standards for filament wound reinforced plastics, ASTM STP 327, Naval Ordnance Laboratory, 6–7 June 1962, White Oak, Silver Spring, MD66–80.
13.
ASTM D 3039/3039M-00. Standard Test Method for Tensile Properties of Polymer Matrix Composite Materials.
14.
ASTM D 3410/3410M-95. Standard Test Method for Compressive Properties of Polymer Matrix Composite Materials.
15.
ASTM D 3518/3518M-94. Standard Test Method for Inplane Shear Response of Polymer Matrix Composite Materials by Tensile Test of a ±45° Laminate.
16.
YoonSHKimCGChoWM. Measurement of tensile properties using filament wound ring specimens. J Reinf Plast Compos1997; 16(9): 810–824.
17.
NgY-C. Deriving composite lamina properties from laminate properties using classical lamination theory and failure criteria. J Compos Mater2005; 39(14): 1295–1306.
18.
LiuGHuHZhangP. An experimental investigation into the radial compressive properties of the biodegradable braided regeneration conduits for peripheral nerve repair. Autex Res J2005; 5(2): 106–112.
19.
JonesRM. Mechanics of composite materials, 2nd ed. New York: Taylor and Francis, 1999.
20.
HyerMW. Stress analysis of fibre reinforced composite materials, New York: WCB McGraw Hill Book Co, 1998.