This article presents the results of a current study on the influence of interlayer delaminations on the static and fatigue behavior of composite laminates. The composite was manufactured by a vacuum molding method using 12 balanced bi-directional carbon fiber layers and epoxy resin. Delaminations with different length were artificially introduced. The specimens with dog bone shape were cut from the original plates having 3 mm thickness and fiber weight fraction of 0.66. Static tests were performed in order to study the influence of delamination size on the laminate stiffness and strength. Complementary finite element analysis was carried out showing the influence of angular misalignments of fiber/matrix delaminations on the laminate stiffness. Fatigue tests were performed in load control for R = 0.05 and R = —1, with a loading frequency of 10 Hz, at room temperature. The artificial interlayer delaminations have a negligible influence on the fatigue strength for tensile cycle loadings, but produce significant decreases in strength for R = —1 fatigue loadings.
Shimokawa, T. and Hamaguchi , Y. (1983). Distribution of Fatigue Life and Fatigue Strength in Notched Specimens of a Carbon Eight-harness-satin Laminate, Journal Composite Materials , 17: 64-76.
2.
Adams, R.D. and Cawley, P.D. ( 1998). A Review of Defects Types and Non-destructive Testing Techniques for Composites and Bonded Joints, NDT International , 21: 208-222.
3.
Fuoss, E., Straznicky, P.V. and Poon, C. ( 1998). Effects of Stacking Sequence on the Impact Resistance in Composite Laminates-part I: Parametric Study, Composite Structures, 41: 67-77.
4.
Capriotti, R., Dati, E., Silvestri, P. and Trivisonno, G. ( 2000). NDT Techniques for the Evaluation of Impact Damage on Aeronautical Structures, In: 15 th WCNDT, Rome.
5.
Abrate, S. ( 1991). Impact on Laminated Composite Materials, Applied Mechanics Reviews, 44(4): 155-190.
6.
Caprino, G. ( 1984). Residual Strength Prediction of Impacted CFRP Laminates , Composites Materials, 18: 508-518.
7.
Cantwell, W.J. and Morton, J. (1989). Comparison of the Low and High Velocity Impact Response of CFRP, Composites , 20(6): 545-551.
8.
Prichard, J.C. and Hogg, P.J. (1990). The Role of Impact Damage in Post-impact Compression Testing, Composites , 21(6): 503-509.
9.
Davies, G.A.O. , Hitchings, D. and Zhou, G. (1996). Impact Damage and Residual Strengths of Woven Fabric Glass/Polyester Laminates , Composites Part A: Applied Sciences, 27A: 1147-1156.
10.
Zheng, S. and Sun, C. ( 1998). Delamination Interaction in Laminated Structures , Engineering Fracture Mechanics, 59: 225-240.
11.
de Moura, M.F.S.F. and Marques, A.T. (2002). Prediction of Low Velocity Impact Damage in Carbon-epoxy Laminates, Composites: Part. A, 33: 361-368.
12.
Collombet, F., Bonini, J. and Lataillade, J.L. (1996). A Three-dimensional Modelling of Low Velocity Impact Damage in Composite Laminates , International Journal for Numerical Methods in Engineering , 39: 1491-1516.
13.
Salekeen, S. and Jones, D.L. (2007). Fatigue Response of Thick Section Fiberglass/Epoxy Composites, Composite Structures , 79: 119-124.
14.
Hertzberg, R.W. (1980). Deformation and Fracture Mechanics of Engineering Materials, Wiley, New York.
15.
Hertzberg, R.W. and Manson, J.A. (1980). Fatigue of Engineering Plastics, Academic Press, New York .
16.
Kawai, M. ( 2004). A Phenomenological Model for off-axis Fatigue Behavior of Unidirectional Polymer Matrix Composites under Different Stress Ratios , Composites: Part A, 35: 955-963.
17.
Spearing, S.M. and Beaumont, P.W.R. (1992). The Fatigue Mechanics of Composite Materials, I: Experimental Measurement of Damage and Post-fatigue Properties, Composites Science and Technology , 44: 159-168.
18.
Echtermeyer, A.T., Engh, B. and Buene, L. (1995). Lifetime and Young’s Modulus Changes of Glass/phenolic and Glass/polyester Composite under Fatigue , Composites, 26(1): 10-16.
19.
Ferreira, J.A.M. , Costa, J.D.M., Reis, P.N.B. and Richardson , M.O.W. (1999 ). Analysis of Fatigue and Damage in Glass-fibre-reinforced polypropylene Composite Materials, Composites Science and Technology, 59: 1461-1467.
20.
Ferreira, J.A.M. , Costa, J.D.M. and Reis, P.N.B. (1999). Static and Fatigue Behaviour of Glass-fibre-reinforced polypropylene Composites , Theoretical Applied Fracture Mechanics, 31: 67-74.
21.
Reis, P.N.B. , Ferreira, J.A.M., Antunes, F.V. and Costa, J.D.M. ( 2007). Flexural Behaviour of Hybrid Laminated Composites, Composites: Part A, 38: 1612-1620.
22.
Reis, P.N.B. , Ferreira, J.A.M., Costa, J.D.M. and Richardson , M.O.W. ( 2009). Fatigue Life Evaluation for Carbon/Epoxy Laminate Composites under Constant and Variable Block LoadingComposites Science and Technology , 69: 154-160.
23.
ISO/FDIS 527-4 ( 1996). Plastics - Determination of Tensile Properties - Part 4: Test Conditions for Isotropic and Orthotropic Fibre-reinforced Plastic Composites, ISO International Standard.
24.
Yokozeki, T. , Ogasawara, T. and Ishikawa, T. ( 2005). Effects of the Fiber Nonlinear Properties on the Compressive Strength Prediction of Unidirectional Carbon-fiber Composites, Composites Science and Technology , 65: 2140-2147.
25.
van Dreumel, W.H.M. and Kamp, H.M. (1977). Non Hookean Behaviour in the Fibre Direction of Carbon-fibre Composites and the Influence of Fibre Waviness on the Tensile Properties, Journal of Composite Materials , 11: 461-469.
26.
Ishikawa, T. , Matsusima, M. and Hayashi, Y. (1985). Hardening Non-linear Behaviour in Longitudinal Tension of Unidirectional Carbon Composites, Journal of Material Science, 20: 4075-4083.
27.
Sun, C.T. and Tao, J. (1998). Prediction of Failure Envelopes and Stress/strain Behaviour of Composite Laminates, Composites Science and Technology, 58: 1125-1136.
28.
Johnson, P. and Chang, F.K. (2001). Characterization of Matrix Crack-induced Laminate Failure -I. Experiments, Journal of Composite Materials, 35: 2009-2035.
29.
Yokozeki, T. , Ogasawara, T. and Ishikawa, T. (2006). Nonlinear Behavior and Compressive Strength of Unidirectional and Multidirectional Carbon Fiber Composite Laminates, Composites: Part A, 37: 2069-2079.
30.
Mittelman, A. and Roman, I. (1990). Tensile Properties of Real Unidirectional Kevlar/Epoxy Composites, Composites , 21(1): 63-69.
31.
Zweben, C. ( 1968). Tensile Failure Analysis of Fibrous Composites , AIAA Journal, 6: 2325-2326.
32.
Ryder, J.T. and Crossman, F.M. ( 1983). A Study of Stiffness, Residual Strength and Fatigue Life Relationships for Composite Laminates, NASA CR-172211.
33.
O’Brien, T.K., Rigamonti, M. and Zanotti, C. (1989). Tension Fatigue Analysis and Life Prediction for Composite Laminates, International Journal of Fatigue, 11(6): 379-393.
34.
Berbinau, P. , Soutis, C. and Guz , I.A. (1999). Compressive Failure of 0° Unidirectional Carbon fibre-reinforced Plastic (CFRP) Laminates by Fibre Microbuckling, Composites Science and Technology , 59: 1451-1455.
35.
Creighton, C.J. and Clyne, T.W. (2000). The Compressive Strength of Highly-aligned Carbon Fibre/epoxy Composites Produced by Pultrusion , Composites Science and Technology, 60: 525-533.
36.
Welsh, J.S. and Adams, D.F. (1997). Testing of Angle-ply Laminates to Obtain Unidirectional Composite Compression Strengths , Composites: Part A, 28A: 387-396.