Weldability of AL99—SiC Composites by CO2 Laser Welding

Abstract

In this study, Al99—SiC composites were produced using PM method. In the composites produced, the reinforcement rates of SiC were 0, 5, 10, and 20 (%wt). The matrix Al 99 powders were mechanically mixed with SiC particulates. These powders were compacted at room temperature at 500 MPa for 5 × 10 × 60 mm specimens and followed by sintering at 600 and 620°C for 1 h. Composite specimens were joined by CO₂ laser welding method. Rofin—Sinar SM2000 machine was used for the welding process. The microstructure of melted region was investigated by optical, scanning, and X-ray microchemical analysis techniques. The hardness test, tensile test, and three-point bend test results were presented. The effect to CO₂ laser welding method at different reinforcement rates and different sintering temperatures in Al 99 powder was investigated. Because of the lower thermal conductivity of Al99—SiC composites, melting zone is wide. It was observed that 0.5 m/min laser welding velocity was suitable for composites with low SiC rate (0% and 5% SiC), and with increasing SiC (10 and 20%), laser welding velocity of 0.3 m/min was suitable.

Keywords

Al99—SiC composite powder metallurgy method mechanical properties CO2 laser welding.

Get full access to this article

View all access options for this article.

References

Ceschini, L. , Minak, G. and Morri, A. (2006). Tensile and Fatigue Properties of the AA6061/20 vol.% Al2O3p and AA7005/10 vol.% Al2O3p Composites, Composites Science and Technology, 66(2): 333-342.

Torralba, J.M. , Costa, C.E. and Velasco, F. (2002). P/M Aluminum Matrix Composites: An Overview, Journal of Materials Processing Technology, 5822: 1-4.

Arik, H. , Aydin, M. , Kurt, A. and Turker, M. (2005). Weldability of Al4C3-Al Composites Via Diffusion Welding Technique, Materials and Design, 26: 555-560.

Tang, F. , Meeks, H. , Spowart, J.E. , Gnaeupel-Herold, T. , Prask, H. and Anderson, I.E. (2004). Consolidation Effects on Tensile Properties of an Elemental Al Matrix Composite, Materials Science and Engineering A, 386: 194-204.

Hascalik, A. and Orhan, N. (2007). Effect of Particle Size on the Friction Welding of Al2O3 Reinforced 6160 Al Alloy Composite and SAE 1020 Steel, Materials and Design, 28: 313-317.

Tang, F. , Anderson, I.E. , Gnaupel-Herold, T. and Prask, H. (2004). Pure Al Matrix Composites Produced by Vacuum Hot Pressing: Tensile Properties and Strengthening Mechanisms, Materials Science and Engineering A, 383: 362-373.

Kaczmar, J.W. , Pietrzak, K. and WøosinÂski, W. (2000). The Production and Application of Metal Matrix Composite Materials, Journal of Materials Processing Technology, 106: 58-67.

Uzun, H. (2007). Friction Stir Welding of SiC Particulate Reinforced AA2124 Aluminium Alloy Matrix Composite, Materials and Design , 28: 1440-1446.

Salazar, J.M.G. and Barrena, M.I. (2003). Dissimilar Fusion Welding of AA7020/MMC Reinforced with Al2O3 Particles: Microstructure and Mechanical Properties, Materials Science and Engineering A, 352: 162-168.

10.

Durmuş, H. (2006). CO2 Lazer Kaynağiyla Birleştirilmiş Aluminyum Matriksli Kompozitlerin Kaynak Bölgesinin Mekanik Özelliklerinin Incelenmesi, PhD Thesis, Celal Bayar University, Manisa, Türkiye.