The stirring of the molten material during CO2 laser welding with a dynamic polarised laser beam (DP) was studied. The key element of the set-up is a high power interference laser beam modulator for CW power rating up to 4 kW. Metallographic cross-sections and EDX analyses of the realised welds in St37 using the contrast material nickel proved the enhancement of melt pool stirring due to DP. Moreover, roughness measurements confirmed a smoothing of the top bead surface as well as a correlation between melt pool stirring and the formation of the top bead ripple structure.
MatsunawaA., KimJ.-D., SetoN., MizutaniM. and KatayamaS.: ‘Dynamics of keyhole and molten pool in laser welding’, J. Laser Appl., 1998, 10, 247–254.
2.
TzengY.-F.: ‘Effects of operating parameters on surface quality for the pulsed laser welding of zinc-coated steel’, J. Mater. Process. Technol., 2000, 100, 163–170.
3.
KuoT. Y. and JengS. L.: ‘Porosity reduction in Nd-YAG laser welding of stainless steel and inconel alloy by using a pulsed wave’, J. Phys. D, Appl. Phys., 2005, 38D, 722–728.
4.
BergmannJ.-P., HoltzR. and WildenJ.: ‘Modification of solidification conditions through the set of pulsed Nd:YAG lasers’, Proc. SPIE, 2007, 6346, 34612.
5.
BranschH. N., WeckmanD. C. and KerrH. W.: ‘Effects of pulse shaping on dimensions and quality of Nd:YAG spot welds in austenitic stainless steel’, Weld. J., 1994, 73, 141s–151s.
6.
VillafuerteJ. C. and KerrH. W.: ‘Electromagnetic stirring and grain-refinement in stainless-steel GTA welds’, Weld. J., 1990, 69, 1s–13s.
7.
KouS. and LeY.: ‘Grain structure and solidification cracking in oscillated arc welds of 5052 aluminium alloy’, Metall. Trans. A, 1985, 16A, 1345–1352.
8.
KouS.: ‘Welding metallurgy’, 2nd edn; 2003, New York, John Wiley & Sons.
9.
KernM., BergerP. and HügelH.: ‘Magneto-fluid dynamic control in CO2 laser beam welding’, Weld. J., 2000, 3, 72-s–78–s.
10.
ThomyC. and VollertsenF.: ‘Influence of magnetic fields on dilution during laser welding of aluminium’, Adv. Mater. Res., 2005, 6–8, 179–186.
11.
VollertsenF. and ThomyC.: ‘Magnetic stirring during laser welding of aluminium’, J. Laser Appl., 2006, 18, 28–34.
12.
ArzuovM. I., BarchukovA. I., BunkinF. V., KirichenkoN. A., KonovV. I. and LukyanchukB. S.: ‘Some features of laser heating of oxidizable metals in air by obliquely incident radiation’, Sov. J. Quant. Electron., 1979, 9, 1308–1310.
13.
GarashchukV. P., KirseiV. I. and ShinkarevV. A.: ‘Influence of the polarization of CO2 laser radiation on the geometric parameters of a molten region in welding of metals’, Sov. J. Quant. Electron., 1986, 16, 1660–1662.
14.
BeyerE., BehlerK. and HerzigerG.: ‘Influence of laser beam polarisation in welding’, Proc. 5th Int. Conf. on ‘Lasers in manufacturing’, Stuttgart, Germany, September 1988, IFS, 233–240.
15.
SatoS., KunimitsuT. and BülentM.: ‘Polarization effects of a high-power CO2 laser beam on aluminium alloy weldability’, J. Appl. Phys., 1996, 79, 8917–8919.
16.
HoC. Y. and WeiP. S.: ‘Absorption in a paraboloid of revolution-shaped welding or drilling cavity irradiated by a polarized laser beam’, Metall. Mater. Trans. B, 2001, 32B, 603–614.
17.
HoC. Y.: ‘Effects of polarizations of a laser on absorption in a paraboloid of revolution-shaped welding or drilling cavity’, J. Appl. Phys., 2004, 96, 5393–5401.
18.
BanovicS. W., DuPontJ. N. and MarderA. R.: ‘Dilution and microsegregation in dissimilar metal welds between super austenitic stainless steel and nickel base alloys’, Sci. Technol. Weld. Join., 2002, 7, 374–383.
19.
PhanikumarG., DuttaP. and ChattopadhyayK.: ‘Continuous welding of Cu-Ni dissimilar couple using CO2 laser’, Sci. Technol. Weld. Join., 2005, 10, 158–166.
20.
LuijendijkT.: ‘Welding of dissimilar aluminium alloys’, J. Mater. Process. Technol., 2000, 103, 29–35.
21.
MaiT. A. and SpowageA. C.: ‘Characteriszation of dissimilar joints in laser welding of steel-kovar, copper-steel and chopper–aluminium’, Mater. Sci. Eng. A, 2004, A374, 224–233.
22.
ZhaoL., SuginoT., ArakaneG. and TsukamotoS.: ‘Influence of welding parameters on distribution of wire feeding elements in CO2 laser GMA hybrid welding’, Sci. Technol. Weld. Join., 2009, 14, 457–467.
23.
StaupendahlG.: ‘Universeller Modulator für CO2-Laserstrahlung und seine Einsatzmoglichkeiten’, Laser Optoelektron., 1991, 23, 126–133.
24.
NarikiyoT., FujinagaS., TakenakaH., OhmoriA. and InoueK.: ‘Optimisation of welding using two Nd-YAG laser beams combined at workpiece surface’, Sci. Technol. Weld. Join., 2000, 5, 113–119.
25.
DausingerF., FaisstF., GlumannC. and HackR.: ‘Effiziente Strahladdition zum Laserstrahlschweissen’, Laser Optoelektron., 1995, 27, 45–50.
26.
ArataY., TomieM., AbeN. and YaoX.-Y.: ‘Observation of molten metal flow during EB welding’, Trans. JWRI, 1987, 16, 13–16.
27.
BeyerE.: ‘Schweissen mit Laser’; 1995, Berlin, Springer.
28.
SunZ. and IonJ. C.: ‘Laser welding of dissimilar metal combinations’, J. Mater. Sci., 1995, 30, 4205–4214.