Effect of Fiber Surface Texture Created from Silane Blends on the Strength and Energy Absorption of the Glass Fiber/Epoxy Interphase

Abstract

Most of the research to date has focused on tailoring the interphase adhesion by controlling the degree of chemical bonding between fiber and resin. The interfacial shear strength (IFSS) has been increased as much as 40% by modified chemical surface bonding [1—3]. However, it is well known that increasing the interfacial strength of the fiber reinforced polymeric composite material often leads to a reduction in the fracture toughness and vice versa [4—12]. In this study, the effects of mechanical interlocking, in addition to chemical bonding on the strength and energy absorption of glass fiber/epoxy interphase, were studied by creating texture on the fiber surface through the phase separation of silane blends. A series of tetraethoxysilane (TEOS)/3-glycidoxypropyltrimethoxysilane (GPS) blends in solutions of ethanol and water was selected to treat the glass fiber surface. The fiber coated with different surface treatments shows the change in fiber surface morphology due to the addition of TEOS. X-ray photoelectron spectroscopy (XPS) analysis showed that the GPS preferentially migrates to the coating surface which suggests that phase separation induced by the silane blend was the primary mechanism for the texture formation. Atomic force microscopy (AFM) was used to scan the fiber surface after the coating and the fiber surface texture was quantified by the roughness values. In addition, a single-fiber Microdroplet shear test was conducted to assess the interfacial properties between the textured glass surface and an epoxy matrix. Traditionally, interfacial shear strength is the only quantity that was determined from the load vs. displacement curve after microdroplet test. In this study, a new data-reduction scheme was developed to determine the energy absorption due to different failure mechanisms by taking into consideration both machine compliance and fiber stretching in the energy calculation. The results show as much as a three-fold increase in specific sliding energy absorption without sacrificing interfacial shear strength. The examination of failure surfaces shows that failure mode propagates through the textured interphase in a more tortuous path, which results in greater degree of energy absorption during fiber—matrix pullout. This study shows the potential for using chemical bonding and mechanical interlocking effects to improve both strength and energy absorption in fiber reinforced composites.

Keywords

glass fiber silane blends sol-gel mechanical interlocking microdroplet interphase energy absorption.

Get full access to this article

View all access options for this article.

References

Chou, S. and Lin, L. -S. (2001). Effect of Colloidal Silica on Adhesion of Glass Fiber to Polypropylene , Polymers & Polymer Composites , 9(3): 175—183.

Chou, S. , Lin, L.-S. and Yeh, J.-T. (2000). Effect of Surface Treatment of Glass Fibers on Adhesion to Polypropylene Resin, Polymers & Polymer Composites , 8(2): 131—138.

Chou, S. , Lin, L.-S. and Yeh, J.-T. (1999). Effect of Surface Treatment of Glass Fiber on Adhesion to Phenolic Resin, Polymers & Polymer Composites , 7(1): 21—31.

Feih, S. , Wei, J. , Kingshott, P. and Sorensen, B.F. (2005). The Influence of Fibre Sizing on the Strength and Fracture Toughness of Glass Fibre Composites , Composites Part A: Applied Science and Manufacturing, 36(2): 245—255.

Bagwell, R.M. and Wetherhold, R.C. (2003). Improvement in Fracture Toughness of an Epoxy/Copper Composite Through the Use of Various End Shaped Fibers , Materials Science and Engineering A, 361(1—2): 294—301.

Piggott, M.R. (1997). Why Interface Testing by Single-fibre Methods can be Misleading , Composites Science and Technology, 57(8): 965—974.

Harris, B. , Beaumont, P.W.R. and De Ferran, E.M. (1997). Strength and Fracture Toughness of Carbon Fibre Polyester Composites , Journal of Material Science, 6(3): 238—251.

Khanna, S.K. and Shukla, A. (1994). Influence on Fiber Inclination and Interfacial Conditions on Fracture in Composite Materials , Experimental Mechanics, 34(2): 171—180.

Khanna, S.K. and Shukla, A. (1993). Energy Absorption Mechanisms During Dynamic Fracturing of Fibre-Reinforced Composites , Journal of Materials Science , 28(14): 3722—3730.

10.

Khanna, S.K. , Ranganathan, P. , Yedia, S.B. , Winter, R.M. and Paruchuri , K. (2003). Sample Preparation Techniques for Nano-mechanical Characterization of Glass Fiber Reinforced Polyester Matrix Composites , Composites Part A: Applied Science and Manufacturing, 34(1): 53—65.

11.

Wright, W.W. (1990). The Carbon Fiber/epoxy Resin Interphase — A Review — Part I , Composite Polymers, 3(4): 231—257.

12.

Tsai, H.C. , Arocho, A.M. and Gause, L.W. (1990). Prediction of Fiber—matrix Interphase Properties and Their Influence on Interface Stress, Displacement and Fracture Toughness of Composite Material , Materials Science and Engineering A , 126(1—2): 295—304.

13.

Kessler, A. and Bledzki, A. (2000). Correlation Between Interphase-Relevant Tests and The Impact-Damage Resistance of Glass/Epoxy Laminates with Different Fibre Surface Treatments , Composites Science and Technology , 60(1): 125—130.

14.

Hodzic, A. , Kalyanasundaram, S. , Kim, J.K. , Lowe, A.E. and Stachurski, Z.H. (2001). Application of Nano-indentation, Nano-scratch and Single Fiber Tests in Investigation of Interphases in Composite Materials , Micron, 32(8): 765—775.

15.

Mader, E. , Mai, K. and Pisanova, E. (2000). Interphase Characterization in Polymer Composites — Monitoring of Interphasial Behavior in Dependence on the Mode of Loading , Composite Interfaces, 7(3): 133—147.

16.

Drzal, L.T. (1990). The Role of the Fiber-matrix Interphase on Composite Properties , Vacuum, 41(7—9): 1615—1618.

17.

Drzal, L.T. (1983). Composite Interphase Characterization , Sampe Journal, 19(5): 7—13.

18.

Drzal, L.T. , Rich, M.J. and Hall, D.L. (1982). Structure-property Relationships at the Composite Interphase , Carbon, 20(2): 150 .

19.

Tanoglu, M. (2000). A New Technique to Characterize the Fiber/matrix Interphase Properties Under High Strain Rate , Composites Part A: Applied Science and Manufacturing, 31(10): 1127—1138.

20.

Plueddemann, E.P. (1983). Silane Coupling Agents , Plenum, New York.

21.

Blum, F.D. , Meesiri, W. , Kang, Hey-Jung and Gambogi, Joan E. (1991). Hydrolysis, Adsorption, and Dynamics of Silane Coupling Agents on Silica Surfaces , Journal of Adhesion Science and Technology, 5(6): 479—496.

22.

Pape, P.G. and Plueddemann, E. (1991). Methods for Improving the Performance of Silane Coupling Agents , Journal of Adhesion Science and Technology , 5(10): 831—842.

23.

Park, S.T. and Jin, J.S. (2000). Influence of Silane Coupling Agents on the Surface Energetics of Glass Fibers and Mechanical Interfacial Properties of Glass Fiber Reinforced Composites , Journal of Adhesion Science and Technology, 14(13): 1677—1689.

24.

Plueddemann, E.P. (1991). Reminiscing on Silane Coupling Agents , Journal of Adhesion Science and Technology , 5(4): 261—277.

25.

Foley, M.E. , Abu Obaid, A. , Huang , X. , Tanoglu, M. , Bogetti, T.A. , McKnight, S.H. and Gillespie Jr, J.W. ( 2002). Fiber/matrix Interphase Characterization using the Dynamic Interphase Loading Apparatus , Composites Part A: Applied Science and Manufacturing, 33(10): 1345—1348.

26.

Tanoglu, M. , McKnight, S.H. , Palmese, G.R. and Gillespie Jr, J.W. (2001). The Effects of Glass-fiber Sizings on the Strength and Energy Absorption of the Fiber/Matrix Interphase Under High Loading Rates , Composites Science and Technology , 61(2): 205—220.

27.

Tanoglu, M. , McKnight, S.H. , Palmese, G.R. and Gillespie Jr, J.W. (1998). Use of Silane Coupling Agents to Enhance the Performance of Adhesively Bonded Alumina to Resin Hybrid Composites , International Journal of Adhesion and Adhesives , 18(6): 431—434.

28.

Bagwell, R.M. and Wetherhold, R.C. (2005). Fiber Pullout Behavior and Impact Toughness of Short Shaped Copper Fibers in Thermoset Matrices , Composites Part A: Applied Science and Manufacturing, 36(5): 683—690.

29.

Walker, P.J. and Dobson, S. (2001). Pullout Tests on Deformed and Plain Rebars in Cement-Stabilized Rammed Earth , Journal of Materials in Civil Engineering, 13(4): 291—297.

30.

Wen, J. and Wilkes, G.L. (1996). Organic/Inorganic Hybrid Network Materials by the Sol-Gel Approach , Chemistry of Materials, 8(8): 1667—1681.

31.

Han, Y. , Lin, J. and Zhang, H. (2002). Photoluminescence of Organic—Inorganic Hybrid SiO2 Xerogels , Materials Letters, 54(5—6): 389—396.

32.

Zhu, H. , Ma, Y. , Fan , Y.G. and Shen, J.C. (2001). Fourier Transform Infrared Spectroscopy and Oxygen Luminescence Probing Combined Study of Modified Sol-gel Derived Film , Thin Solid Films, 397(1—2): 95—101.

33.

Bauer, F. , Glasel, H.-J. , Decker, U. , Ernst, H. , Freyer, A. , Hartmann, E. , Sauerland, V. and Mehnert, R. (2003). Trialkoxysilane Grafting Onto Nanoparticles for the Preparation of Clear Coat Polyacrylate Systems with Excellent Scratch Performance , Progress in Organic Coatings, 47(2): 147—153.

34.

Muroya, M. (1999). Correlation between the Formation of Silica Skeleton Structure and Fourier Transform Reflection Infrared Absorption Spectroscopy Spectra , Colloids and Surfaces A: Physicochemical and Engineering Aspects, 157(1—3): 147—155.

35.

Jensen, R.E. and McKnight, S.H. (2006). Inorganic—Organic Fiber Sizings for Enhanced Energy Absorption in Glass Fiber-Reinforced Composites Intended for Structural Applications , Composites Science and Technology, 66(3—4): 509—521.

36.

Park, J.-M. , Kim, D.-S. , Kong, J.-W. , Kim , M.Y. and Park, I.-S. (2002). Interfacial Adhesion and Microfailure Modes of Electrodeposited Carbon Fiber/Epoxy-PEI Composites by Microdroplet and Surface Wettability Tests , Journal of Colloid and Interface Science, 249(1): 62—77.

37.

Gaur, U. and Miller, B. (1989). Microbond Method for Determination of the Shear Strength of a Fiber/Resin Interface: Evaluation of Experimental Parameters , Composites Science and Technology, 34(1): 35—51.

38.

McDonough, W.G. , Antonucci, J.M. and Dunkers, J. (2001). Interfacial Shear Strengths of Dental Resin—Glass Fibers by the Microbond Test , Dental Materials, 17(6): 492—498.

39.

Dirand, X. , Hilaire, B. , Soulier, J.P. , Nardin, M. (1996). Interfacial Shear Strength in Glassfiber/Vinylester-resin Composites , Composites Science and Technology, 56(5): 533—539.

40.

Hoecker, F. and Karger-Kocsis , J. (1994). Effects of the Interface on the Mechanical Response of CF/EP Microcomposites and Macrocomposites , Composites, 25(7): 729—738.

41.

Pitkethly, M.J. (1996). The Use of Interfacial Test Methods in Composite Materials Development. Fiber, Matrix, and Interface Properties, Edited by C.J. Spragg and L.T. Drzal , ASTM STP 1290, pp. 34—46.

42.

Gao, X. (2006). Tailored Interphase Structure for Improved Strength and Energy Absorption of Composites, PhD dissertation, University of Delaware .

43.

Jensen, R. , Gao, P.M.X. , Chatterjee, A. and Deitzel, J. (2002). Glass Fiber Sizing Based Upon Inorganic—Organic Hybrid Silane Chemistry , In: Euradh 2002 6th European Adhesion Conference, University of Strathclyde, Glasgow, UK.

44.

Plueddemann, E.P. (1974). Interfaces in Polymer Matrix Composites, Academic Press, New York.

45.

Della Volpe, C. , Dire, S. and Pagani, E. (1997). A Comparative Analysis of Surface Structure and Surface Tension of Hybrid Silica Films , Journal of Non-Crystalline Solids, 209(1—2): 51—60.

46.

Daniels, M.W. , Sefcik, J. , Francis , L.F. and McCormick , A.V. (1999). Reactions of a Trifunctional Silane Coupling Agent in the Presence of Colloidal Silica Sols in Polar Media , Journal of Colloid and Interface Science, 219(2): 351—356.

47.

Underhill, P.R. , Goring, G. and DuQuesnay, D.L. (2000). The Effect of Humidity on the Curing of 3-Glycidoxypropyltrimethoxy Silane , International Journal of Adhesion and Adhesives, 20(3): 195—199.

48.

Daniels, M.W. and Francis, L.F. (1998). Silane Adsorption Behavior, Microstructure, and Properties of Glycidoxypropyltrimethoxysilane-Modified Colloidal Silica Coatings , Journal of Colloid and Interface Science, 205(1): 191—200.

49.

Yang, Q.-S. , Qin, Q.-H. and Peng, X.-R. (2003). Size Effects in the Fiber Pullout Test , Composite Structures, 61(3): 193—198.

50.

Beckert, W. and Lauke, B. (1997). Critical Discussion of the Single-Fibre Pull-Out Test: Does it Measure Adhesion? , Composites Science and Technology , 57(12): 1689—1706.

51.

Kessler, H. , Schuller, T. , Beckert , W. and Lauke, B. (1999). A Fracture-Mechanics Model of the Microbond Test with Interface Friction , Composites Science and Technology, 59(15): 2231—2242.

52.

Zhandarov, S. and Mader, E. (2005). Characterization of Fiber/matrix Interface Strength: Applicability of Different Tests , Approaches and Parameters, Composites Science and Technology, 65(1): 149—160.

53.

Zhandarov, S. , Pisanova, E. and Mader, E. (2000). Is There Any Contradiction Between the Stress and Energy Failure Criteria in Micromechanical Tests? Part II . Crack Propagation: Effect of Friction on Force—Displacement Curves, Composite Interfaces, 7(3): 149—175.

54.

Ash, J.T. , Cross, W.M. , Svalstad , D. , Kellar, J.J. and Kjerengtroen , L. (2003). Finite Element Evaluation of the Microbond Test: Meniscus Effect, Interphase Region, and Vise Angle , Composites Science and Technology , 63(5): 641—651.

55.

Liu, C.-H. and Nairn, J.A. (1999). Analytical and Experimental Methods for a Fracture Mechanics Interpretation of the Microbond Test Including the Effects of Friction and Thermal Stresses , International Journal of Adhesion and Adhesives, 19(1): 59—70.

56.

Piggott, M.R. (1995). A New Model for Interface Failure in Fibre-Reinforced Polymers , Composites Science and Technology, 55(3): 269—276.

57.

Hodzic, A. , Stachurski, Z.H. and Zbigniew, H. (2001). Droplet on a Fibre: Surface Tension and Geometry , Composite Interfaces, 8(6): 415—425.

58.

Hodzic, A. , Stachurski, Z.H. and Kim, J.K. (2001). An Analysis of Microdroplet Test: Effects of Specimen, Geometry, Matrix Type , Fiber Treatment and Water Aging, 9(8): 499—508.

59.

Gama, B. (2004). Energy Absorbing Damage Mechanisms in Quasi-static Punch Shear of Thick-section Composites , SAMPE Proceeding, Long Beach, CA, May 16—20, 2004, p. 13.