Failure Modes of Foam Core Sandwich Beams under Static and Impact Loads

Abstract

In recent times, sandwich structures have been widely used in load bearing structures due to their high specific stiffness and high specific strength. Some sandwich structures, such as those used in high speed transportations, are required to have high impact energy absorption characteristics also. Since sandwich structures can fail in various modes, in this article, the static failure modes and load capabilities of foam core composite sandwich beams composed of E-glass/Epoxy and PVC foam were investigated by both experimental and analytic methods. The static load capabilities and failure modes predicted by the theory of beam on elastic foundation showed good agreement with the three-point bending test results. Using the experimental and analytic results, the static failure mode map was constructed. Also, the impact failure modes and the impact energy absorption characteristics of the sandwich beams were studied by the impact test and the finite element analysis. From the test result, it was found that the face failure mode was favorable for the high impact energy absorption. Using the experimental and finite element analysis results, the impact failure mode map was constructed.

Keywords

composite sandwich structures failure mode map three-point bending test impact test elastic foundation theory

Get full access to this article

View all access options for this article.

References

1. Zenkert, D. (1997). The Handbook of Sandwich Construction, Engineering Materials Advisory Service, Ltd., West Midlands, UK.

2. Vinson, J.R. (1999). The Behavior of Sandwich Structures of Isotropic and Composite Materials, Technomic Publication Co., Inc., Pennsylvania, USA.

3. Triantafillou, T.C. and Gibson, L.J. (1987). Failure Mode Maps for Foam Core Sandwich Beams, Materials Science and Engineering, 95: 37–53.

4. Petras, A. and Sutcliffe, M.P.F. (1999). Failure Mode Maps for Honeycomb Sandwich Panels, Composite Structures, 44: 237–252.

5. McCormack, T.M. , Miller, R. , Kesler, O. and Gibson, L.J. (2001). Failure of Sandwich Beams with Metallic Foam Cores, International Journal of Solids and Structures, 38: 4901–4920.

6. Yoon, K.J. , Kim, C.K. and Park, H.C. (2002). Nonlinear Flexural Deflection of Thermoplastic Foam Core Sandwich Beam, Journal of Composite Materials, 36: 1529–1540.

7. Thomsen, O.T. (1995). Theoretical and Experimental Investigation of Local Bending Effects in Sandwich Plates, Composite Structures, 30: 85–101.

8. Shenhar, Y. , Frosting, Y. and Altus, E. (1996). Stresses and Failure Patterns in the Bending of Sandwich Beams with Transversely Flexible Cores and Laminated Composite Skins, Composite Structures, 35: 143–152.

9. Petras, A. and Sutcliffe, M.P.F. (2000). Indentation Failure Analysis of Sandwich Beams, Composite Structures, 50: 311–318.

10.

10. Lee, S.M. and Tsotsis, T.K. (2000). Indentation Failure Behavior of Honeycomb Sandwich Panels, Composites Science and Technology, 60: 1147–1159.

11.

11. Kim, J. and Swanson, S.R. (2001). Design of Sandwich Structures for Concentrated Loading, Composite Structures, 52: 365–373.

12.

12. Yang, J. , Shen, H. and Zhang, L. (2001). Nonlinear Local Response of Foam-filled Sandwich Plates with Laminated Faces Under Combined Transverse and In-plane Loads, Composite Structures, 52: 137–148.

13.

13. Mines, R.A.W. and Alias, A. (2002). Numerical Simulation of the Progressive Collapse of Polymer Composite Sandwich Beams Under Static Loading, Composites: Part A, 33: 11–26.

14.

14. Shih, W.K. and Jang, B.Z. (1989). Instrumented Impact Testing of Composite Sandwich Panels, Journal of Reinforced Plastics and Composites, 8: 270–298.

15.

15. Kim, C.G. and Jun, E.J. (1992). Impact Resistance of Composite Laminated Sandwich Plates, Journal of Composite Materials, 26: 2247–2261.

16.

16. Mines, R.A.W. , Worrall, C.M. and Gibson, A.G. (1998). Low Velocity Perforation Behavior of Polymer Composite Sandwich Panels, International Journal of Impact Engineering, 21: 855–879.

17.

17. Anderson, T. and Madenci, E. (2000). Experimental Investigation of Low-Velocity Impact Characteristics of Sandwich Composites, Composite Structures, 50: 239–247.

18.

18. Hazizan, M.A. and Cantwell, W.J. (2002). The Low Velocity Impact Response of Foam-Based Sandwich Structures, Composites: Part B, 33: 193–204.

19.

19. DIAB group (1992). Divinycell Technical Manual, DIAB group.

20.

20. Kassapoglou, C. , Fantle, S.C. and Chou, J.C. (1995). Wrinkling of Composite Sandwich Structures Under Compression, Journal of Composite Technology and Research, 17: 308–316.