Study of Load Ratio for Mode-I Fatigue Fracture of Wood-FRP-Bonded Interfaces

Abstract

This paper presents the fatigue behavior of interface bond between red maple wood and phenolic FRP substrates. Using linear elastic fracture mechanics concepts, the influence of load ratio on fatigue crack propagation rate is studied. A contoured double cantilever beam (CDCB) specimen is adopted in this study in order to obtain constant strain energy release rate independent of crack length. The compliance method is used for measuring the crack growth rate. A modified Paris Law equation based on strain energy release rate range, ΔG, and mean value of strain energy release rate, G_mean, is proposed in this study for efficient evaluation of load ratio effect on fatigue crack propagation of the bonded interfaces. Follow-up environmental effects are being examined by means of the same energy parameters of the present study and without the need to consider crack closure. The proposed approach can further be extended to characterization of other bonded interfaces for dissimilar materials.

Keywords

contoured double cantilever beam (CDCB) specimen crack propagation rate da/dN load ratio R crack opening displacement (COD)strain energy release rate

Get full access to this article

View all access options for this article.

References

1. Hernandez, R. , Davalos, J.F. , Sonti, S.S. , Kim, Y. and Moody, R.C. (1997). Strength and Stiffness of Reinforced Yellow-Poplar Glued-Laminated Beams, In: Research Paper FRLRP-554, Madison, WI, U. S. Dept. of Agriculture, Forest Service, Forest Products Laboratory, p. 28.

2. Qiao, P.Z. , Davalos, J.F. and Zipfel, M.G. (1998). Modeling and Optimal Design of Composite-Reinforced Wood Railroad Crosstie, Composite Structures, 41(1): 87-96.

3. Davalos, J.F. , Zipfel, M.G. and Qiao, P.Z. (1999). Feasibility Study of Prototype GFRP-Reinforced Wood Railroad Crosstie, ASCE Journal of Composites for Construction, 3(2): 92-99.

4. Kim, Y. , Davalos, J.F. and Barbero, E.J. (1997). Delamination Buckling of FRP Layer in Laminated Wood Beams, Composite Structures, 37(3-4): 311-320.

5. Davalos, J.F. , Madabhusi-Raman, P. and Qiao, P.Z. (1997). Characterization of Mode-I Fracture of Hybrid Material Interface Bonds by Contoured DCB Specimens, Engineering Fracture Mechanics, 58(3): 173-192.

6. Davalos, J.F. , Madabhusi-Raman, P. , Qiao, P.Z. , and Lang, E.M. (1998). Mode-I Fracture Toughness of Fiber Reinforced Composite-Wood Bonded Interfaces, Journal of Composite Materials, 32(10): 987-1013.

7. Davalos, J.F. , Madabhusi-Raman, P. , Qiao, P. and Wolcott, M.P. (1998). Compliance Rate Change of Tapered Double Cantilever Beam Specimen with Hybrid Interface Bonds, Theoretical and Applied Fracture Mechanics, 29(2): 125-139.

8. Davalos, J.F. , Qiao, P.Z. and Trimble, B.S. (2000). Fiber-Reinforced Composite and Wood Bonded Interface, Part 1 Durability and Shear Strength, ASTM Journal of Composites Technology and Research, 22(4): 224-231.

9. Davalos, J.F. , Qiao, P.Z. and Trimble, B.S. (2000). Fiber-Reinforced Composite and Wood Bonded Interface, Part 2 Fracture, ASTM Journal of Composites Technology and Research, 22(4): 232-240.

10.

10. Qiao, P.Z. and Davalos, F.J. , et al. (2000). Effect of Moisture on Fracture Toughness of Composite/Wood Bonded Interfaces. In: Halford, G.R. and Gallagher, J.P. (eds), Fatigue and Fracture Mechanics: 31st Vol., ASTM STP 1389, American Society for Testing and Materials, West Conshohocken, PA. p. 526-544.

11.

11. Suresh, S. (1998). Fatigue of Materials, 2nd edn, Cambridge University Press, Cambridge.

12.

12. Paris, P.C. , Gomez, M.P. and Anderson, W.E. (1961). Rational Analytical Theory of Fatigue, The Trend in Engineering, 13(1): 9-14.

13.

13. Paris, P.C. and Erdogan, F. (1963). Critical Analysis of Propagation Laws, Journal of Basic Engineering, 85: 528-534.

14.

14. Sutton, A.S. (1974). Fatigue Crack Propagation in an Epoxy Polymer, Engineering Fracture Mechanics, 6: 587-595.

15.

15. Ishiyama, S. , Eto, M. and Oku, T. (1987). Effect of Stress Ratio on Crack Extension Rate of Fine-Grained Isotropic Nuclear Graphite, Journal of Nuclear Science and Technology, 24(9): 719-723.

16.

16. Hojo, M. , Tanaka, K. and Hayashi, R. (1987). Effect of Stress Ratio on Near-Threshold Propagation of Delamination Fatigue Cracks in Unidirectional CFRP, Composite Science and Technology, 29: 273-292.

17.

17. Arad, S. , Radon, J.C. and Culver, L.E. (1971). Fatigue Crack Propagation in Polymethylmethacrylate, Journal Mechanical Engineering Science, 13(2): 75-81.

18.

18. Walker, K. (1970). The Effect of Stress Ratio during Crack Propagation and Fatigue for 2024-T3 and 7075-T6 Aluminum, In: Effects of Environment and Complex Load History on Fatigue Life, ASTM STP 462, American Society for Testing and Materials, p. 1-14.

19.

19. Sadamanda, K. , Vasudevan, A.K. and Holtz, R.L. (2001). Extension of the Unified Approach to Fatigue Crack Growth to Environmental Interactions, International Journal of Fatigue, 23: S277-S286.

20.

20. Elber, W. (1970). Fatigue Crack Closure under Cyclic Tension, Engineering Fracture Mechanics, 2:37-45.

21.

21. Elber, W. (1971). The Significance of Fatigue Crack Closure, Damage Tolerance in Aircraft Structures, ASTM STP 486, American Society for Testing and Materials, pp. 230-242.