A Comparison of Oven-cured and Induction-cured Adhesively Bonded Composite Joints

Abstract

The advantages of using adhesives for joining composite structures are now well accepted. Adhesive joints may offer, over bolted joints, advantages such as a lower assembly weight, a superior stress transfer and an improved fatigue resistance. However, in some applications the above advantages may be offset by the processingconditions required to cure the adhesive. Indeed, in the conventional oven curing process the thermal energy must diffuse through the composite layers to heat the joint interfaces, resultingin longand expensive processingtime as well as wasted energy. A novel method of achieving adhesive bonds is addressed in the present study. The method of electromagnetic heating is well suited for rapid and efficient localized heatingof adhesive bond lines, provided suitable susceptors are used at the interfaces. This paper presents the results of a study on the use of induction heating for bondingcomposite adherends. Single-lap shear tests and double-cantilever beam fracture experiments were performed on oven-cured and induction-cured adhesively bonded joints made from woven-fabric composites. The feasibility of usingthe induction-heatingtechnique for the hardeningof adhesives in composite bonded joints was demonstrated. It was found that the strength of single-lap shear joints was not significantly affected by the choice of the hardening method of the adhesive. Furthermore, the critical fracture energy of the oven-cured and induction-cured double-cantilever beams was found to be only dependent on the adhesive type. Induction-cured specimens were found to be as tough as corresponding oven-cured specimens.

Keywords

adhesive bonded joints induction fabrication

Get full access to this article

View all access options for this article.

References

1. Bourban, P. E. , Karamuk, E. , Don, R. C. and Gillespie, Jr., J. W. (1994). Induction Heatingfor Rehabilitation of Steel Structures UsingComposites, In: Proceedings of the ASCE Materials Engineering Conference, New Materials and Methods for Repair, San Diego.

2. Lawless, G. W. and Reinhart, T. J. (October 1992). Study of the Induction Heatingof Organic Composites, International SAMPE Conference, Toronto, Canada.

3. Benatar, A. and Gutowski, T. G. (October 1986). Methods for Fusion BondingThermoplastic Composites, SAMPE Quarterly.

4. Buckley, J. D. and Fox, R. L. (1988). Rapid Electromagnetic Induction Bonding of Composites, Plastics and Metals, Materials Research Society Symposium, Vol. 124.

5. Buckley, J. D. , Fox, R. L. and Tyeryar, J. R. (1986). Seam Bondingof Graphite Reinforced Composite Panels, NASA Advanced Composites Conference.

6. Fink, B. K. , McCullough, R. L. and Gillespie, Jr., J. W. (1996). Experimental Verification of Models for Induction Heatingof Continuous-Carbon-Fiber Composites, Polymer Composites, 17(2): 198–209.

7. Fink, B. K. , Gillespie, Jr., J. W. and McCullough, R. L. (1992). Induction Heating of Cross-Ply Carbon Fiber Thermoplastic Composites, In: Proceedings of ANTEC 92, Society of Plastics Engineers, Brookfield, CT.

8. Yarlagadda, S. , Gillespie, Jr., J. W. and Fink, B. K. (July 1998). Resistive Susceptor Design for Uniform HeatingDuringInduction Bondingof Composites, Journal of Thermoplastic Composite Materials, 11(4): 321–337.

9. Firko, J. , Yarlagadda, S. , Fink, B. K. and Gillespie Jr., J. W. (1998). Optimisation of Heat Generation in Induction BondingUsingMetal Mesh Susceptors, In: Vizzini, A. J. (Ed.), Proceedings of the American Society for Composites Thirteenth Technical Conference (CDROM), pp. 468–480, published by American Society for Composites, Los Angeles, CA, and distributed by Composites Research Laboratory, University of Maryland, College Park, MD.

10.

10. Tay, T. E. , Fink, B. K. , McKnight, S. H. , Yarlagadda, S. and Gillespie, J. W. (1997). Accelerated Curingof Adhesives in Bonded Joints by Induction Heating, Journal of Composite Materials, 33(17): 1643–1664.

11.

11. Lauri, C. (2001). A Study of Composite Integral Armor: Processing, Repair and Mechanical Performance, Master Thesis, University of Lulea, Sweden.

12.

12. Yarlagadda, S. , Kim, H. J. , Gillespie, J. W. , Shevchenko, N. B. and Fink, B. K. (2002). A Study on the Induction Heatingof Conductive Fiber Reinforced Composites, Journal of Composite Materials, 36(4): 401–422.

13.

13. Mahdi, S. , Gama, B. A. , Yarlagadda, S. and Gillespie Jr., J. W. (2003). Effect of the ManufacturingProcess on the Interfacial Properties and Structural Performance of Multifunctional Composite Structures, Composites Part A: Applied Science and Manufacturing, Accepted for publication.

14.

14. Loctite Aerospace (2001). Dexter Hysol Paste Adhesive and Specialty Resins Selector Guide, http://www.loctiteaero.com.

15.

15. Guess, T. R., Reedy, E. D. and Stavig, M. E. (1995). Mechanical Properties of Hysol EA-9394 Structural Adhesive, SANDIA REPORT SAND95-0229 o UC-704, 29pp.

16.

16. Kadioglu, F. , Ozel, A. and Adams, R. D. (2001). The Strength in the Weakness, In: Proceedings of the International SAMPE Symposium and Exhibition, (4-I): 61–71.

17.

17. Kinloch, A. J. (1987). Adhesion and Adhesives: Science and Technology, (ed.) Chapman and Hall .

18.

18. Williams, J. G. (1989). Fracture Mechanics of Anisotropic Materials, In: K Friedrich (ed.), In: Application of Fracture Mechanics to Composite Materials, pp. 3–38. Elsevier, The Netherlands.

19.

19. Adams, R. D. , Wake, W. C. and Comyn, J. (1997). Structural Adhesive Joints in Engineering, 2nd edn., Chapman & Hall.

20.

20. Adams, R. D. , Atkins, R. W. , Harris, J. A. and Kinloch, A. J. (1986). Stress Analysis and Failure Properties of CFRP/Steel Double-Lap Joints, Journal of Adhesion, 20: 29–53.

21.

21. Tomblin, J. S , Yang, C. and Harter, P. (2001). Investigation of Thick Bondline Adhesive Joints, FAA REPORT DOT/FAA/AR-01/33, 106pp.

22.

22. Frostig, Y. , Thomsen, O. T. and Mortensen, F. (1999). Analysis of Adhesive Bonded Joints, Square-end and Spew-fillet, Closed-form High Order Theory Approach, Journal of Engineering Mechanics, 125(11): 1298–1307, 1999-1999.

23.

23. Fleck, N. A. , Huntchinson, J. W. and Suo, Z. (1991). Crack Path Selection in a Brittle Adhesive Layer, International Journal of Solids and Structures, 27(13): 1683–1703.

24.

24. Forte, M. S. , Whitney, J. M. and Schoeppner, G. A. (2000). The Influence of Adhesive Reinforcement on the Mode-I Fracture Toughness of a Bonded Joint, Composites Science and Technology, 60: 2389–2405.