Fracture Behavior of Woven Composites Containing Various Cracks Geometry

Abstract

Recently, polymeric composite materials are widely used in automotive applications for reducing structural weight, saving fuel, and improving performance. Accidentalimpact damage is an important issue in the use of these composite materials as body components. The damages or cracks in the present work were represented by notched specimens. The test specimens were fabricated from polyester resin reinforced by woven E-glass fiber. A series of tests were conducted to measure the notched strength of composite laminates with various types of through-the-thickness cracks such as central normal notch (CNN), center inclined notch (CIN), single edge notch (SEN) and double edge notch (DEN). A Modified Point Stress Criterion (MPSC) was proposed for predicting the tensile strength of composite laminates with various aspect ratio (a/w), that is, notch length to specimen width ratio.

The results show that the load–elongation diagrams of notched and unnotched glass fiber reinforced polyester (GFRP) specimens have a nonlinear behavior, with clear “Knee”, associated with audible noises. For the same notch length, the notched strength of GFRP specimens with symmetric cracks (CNN, CIN and DEN) is quite consistent. The lowest notched strength is for SEN specimens. An excellent agreement is found between the experimentalresults of centralnotched specimens (CNN and CIN) and the predicted values using the MPSC than the reviewed published theories. The critical stress intensity factor (K _IC) was determined from the centralnotched specimens and used to predict the notched strength of edge notched specimens (SEN and DEN). The type of the central notch (inclined or normal) insignificantly affects the values of the stress intensity factor, K _IC.

Keywords

woven composites notched strength central normal notch central inclined notch single edge notch double edge notch aspect ratio

Get full access to this article

View all access options for this article.

References

1. Xiao, J. and Bathias, C. (1994). Damage and Fracture of Notched Non-Woven and Woven Composite Laminates, Composites Science and Technology, 52: 99–108.

2. Lu Gong, X. , Gong, X.J. , Laksimi, A. and Benzeggagh, M.L. (2000). Applied of Tsai-Wu Criterion to Notched and Unnotched Composite Laminates under Torque Loading, J. Composite Materials, 34(6).

3. Green, E.R. , Morrison, C.J. and Luo, R.K. (2000). Simulation and Experimental Investigation of Impact Damage in Composite with Holes, J. Composite Materials, 34(6).

4. Waddoups, M.E. , Eisenmann, J.R. and Kaminski, B.E. (1971). Macroscopic Fracture Mechanics of Advanced Composite Materials, J. Composite Materials, 5: 446–454.

5. Brinson, H.F. and Yeow, Y.T. (1977). An Experimental Study of the Fracture Behavior of Laminated Graphite/Epoxy Composites, Composite Materials: Testing and Design, ASTM STP 617: 18–38.

6. Marissen, R. , Brouwer, H.R. and Linsen, J. (1995). Notched Strength of Thermoplastic Woven Fabric Composites, J. Composite Materials, 29(12): 1544–1580.

7. Brinson, H.F. and Yeow, Y.T. (1977). An Experimental Study of the Fracture Behavior of Laminated Graphite/Epoxy Composites, ASTM STP 617: 18–38.

8. Whitney, J.M. and Nuismer, R.J. (1974). Stress Fracture Criteria for Laminated Composites Containing Stress Concentrations, J. Composite Materials, 8: 253–265.

9. Kim, J.K. , Kim, D.S. and Takeda, N. (1995). Notched Strength and Fracture Criterion in Fabric Composite Plats Containing a Circular Hole, J. Composite Materials, 29(7): 982–998.

10.

10. Afaghi-Khatibi, A. , Ye, L. and Mai, Y.W. (1996). Effective Crack Growth and Residual Strength of Composite Laminates with a Sharp Notch, J. Composite Materials, 30(3).

11.

11. Khashaba, U.A. and Ali-Eldin, S.S. (2001). Behavior of Unidirectional GFR/Epoxy Composites under Tension-Torsion Biaxial Loading. In: Proceedings of the Seventh Int. Conf. on Prod. Eng., Design and Control, Vol. 3, pp. 1977–1993, Alexandria University, Egypt.

12.

12. Rhodes, M.D , Mikulas, M.M. and McGowan, P.E. (1984). Effect of Orthotropy and Width on the Compression Strength of Graphite-Epoxy Panels with Holes, J. AIAA, 22(91): 1283–1292.

13.

13. Tan, S.C. (1988). Finite-Width Correction Factors for Anisotropic Plate Containing a Central Opening, J. Composite Materials, 22: 1080–1097.

14.

14. Nuismer, R.J. and Labor, J.D. (1978). Applications of the Average Stress Failure Criterion: Part I–Tension, J. Composite Materials, 12: 239–249.

15.

15. Satish, G. and Broutman, L.J. (1975). Crack Growth Resistance of Random Fiber Composites, J. Composite Materials, 9: 217–227.

16.

16. Liao, K. (1999). In-Situ Strength Degradation of Glass Fibers in a Pultruded Composite by Environmental Aging, J. Materials Science Letters, 18: 763–765. http://147.46.94.112/e_journals/pdf_full/journal_j/j13_199910_181005.pdf.

17.

17. Masters, J.E. (1997). Translaminar Fracture Toughness of a Composite Wing Skin Made of Stitched Warp-Knit Fabric, Langley Research Center, NASA. http://techreports.larc.nasa.gov/ltrs/cit.html.

18.

18. Owen, M.J. and Bishop, P.T. (1973). Critical Stress Intensity Factors Applied to Glass Reinforced Polyester Resin, J. Composite Materials, 7: 146–1159.

19.

19. Agarwal, B.D. and Broutman, L.J. (1980). Analysis and Performance of Fiber Composites, A Wilew-Interscience Publication, New York.

20.

20. Hyer, M.W. (1998). Stress Analysis of Fiber-Reinforced Composite Materials, McGraw-Hill, Inc.