Hydrostatic Pressure Effect on the Fracture Toughness of Unidirectional (0-deg) Graphite/Epoxy Laminated Composites

Abstract

Previous studies show that hydrostatic pressure affects elastic modulus, strength, and strain of fiber-reinforced composites. However, no work has been done to understand the compressive fracture behavior of laminated composites under hydrostatic pressure. This work is an experimental study of the hydrostatic pressure effects on the compressive fracture behavior of fiber-reinforced composites. Compressive fracture tests were conducted under various hydrostatic pressures from 0.1 MN/m² (atmospheric pressure) to 200 MN/mi² (2 Kbar). Test specimens used were unidirectional (0-deg) graphite/epoxy laminated composites with a single delamination at the center of specimen. First, compression load-displacement curves were determined as a function of hydrostatic pressure and delamination length. Second, the compressive fracture toughness was determined from the compliance method based on the load-displacement curves as a function of hydrostatic pressure.

The results showed that compliance, fracture load, and fracture toughness were significantly influenced by hydrostatic pressure. The fracture load increases as hydrostatic pressure increases. The compliance decreases linearly with increasing pressure. Particularly, fracture toughness increased from 3.45 N-mm/mm² to 4.53 N-mm/mm² (32% increase) as hydrostatic pressure increased from 0.1 MN/mm² to 200 MN/mm². Apparently the increase of fracture toughness is due to the suppression of local delamination with increasing hydrostatic pressure.

Keywords

composite laminates hydrostatic pressure delamination fracture toughness compliance method

Get full access to this article

View all access options for this article.

References

1. O'Brien, T.K. and Martin, R.H. , 1993, "Round robin testing for mode I interlaminar fracture toughness of composite materials," J. of Composites Technology & Research, Vol. 15, pp. 269-281.

2. Kageyama, K. , Kimpara, I. , Ohsawa, I. , Hojo, M. and Kabashima, S. , 1995, "Mode I and mode II delamination growth of interlayer toughened carbon/epoxy (T800H/3900-2) composite system," ASTM STP 1230, pp. 19-37.

3. Benzeggagh, M.L. and Kenane, M. , 1996, "Measurement of mixed-mode delamination fracture toughness of unidirectional glass/epoxy composites with mixed-mode bending apparatus," Composite Science and Technology, Vol. 56, pp. 439-449.

4. Alif, N. , Carlsson, L.A. and Gillespie, Jr., J.W. , 1997, "Mode I, mode II and mixed mode interlaminar fracture of woven fabric carbon/epoxy," ASTM STP 1242, pp. 82-1006.

5. Russell, A.J. and Street, K.N. , 1989, "Moisture and temperature effects on the mode I and mode II interlaminar fracture of graphite/epoxy composites," Key Engineering Materials, Vol. 37, pp. 199-208.

6. Hooper, S.J. and Subramanian, R. , 1993, "Effects of water and jet fuel absorption on mode I and mode II delamination of graphite/epoxy," ASTM STP 1156, pp. 31-340.

7. Uematsu, Y. , Kitamur, T. and Ohtani, R. , 1995, "Delamination behavior of a carbon-fiber-reinforced thermoplastic polymer at high temperature," Composite Science and Technology, Vol. 53, pp. 333-342.

8. Parry, T.V. and Wronski, A.S. , 1981, "The effect of hydrostatic pressure on the tensile properties of pultruded CFRP," J. of Materials Science, Vol. 17, pp. 2141-2147.

9. Wronski, A.S. and Parry, T.V. , 1982, "Compressive failure and kinking in the uniaxially aligned glass-resin composite under superimposed hydrostatic pressure," J. of Materials Science, Vol. 20, pp. 3656-3662.

10.

10. Shin, E.S. and Pae, K.D. , 1992, "Effects of hydrostatic pressure on the torsional behavior of graphite/epoxy composites," J. of Composite Materials, Vol. 26, pp. 462-485.

11.

11. Pae, K.D. and Rhee, K.Y. , 1995, "Effects of hydrostatic pressure on the compressive behavior of laminated 450 and 90° unidirectional behavior of graphite fiber/epoxy matrix thick composites," Composite Science and Technology, Vol. 53, pp. 281-287.

12.

12. Pae, K.D. and Carlson, K.S. , 1998, "The combined effects of hydrostatic pressure and strain-rate on the compressive properties of a laminated, multi-directional graphite/epoxy thick composites," J. of Composite Materials, Vol. 32, pp. 49-67.

13.

13. Griffith, A.A. , 1920, "The phenomena of rupture and flaw in solids," Transactions, Royal Society of London, A-221.