Synergetic effect of crystal nucleating agent and melt self-enhancement of isotactic polypropylene on its rheological and microcellular foaming properties
Restricted accessResearch articleFirst published online January, 2021
Synergetic effect of crystal nucleating agent and melt self-enhancement of isotactic polypropylene on its rheological and microcellular foaming properties
Crystal nucleating agent Bis (3, 4- dimethylbenzylidene) sorbitol (DMDBS) was used to tune the melt strength and microcellular foaming properties of isotactic polypropylene (iPP) in this study. Rheological testing results reveal that the introduction of DMDBS could enhance the storage modulus and complex viscosity of iPP, obviously increase its crystallization onset temperature, compared to its counterparts without DMDBS. The addition of DMDBS could also significantly increase the cell nucleating ability of iPP, due to its large surface, cooperating with a thermal history control treatment. Quite fine microcellular iPP/DMDBS foams were fabricated with relatively small average cell sizes of nano to several micrometers, and cell densities up to 1011∼1012 cells/cm3, using the synergy effect of DMDBS and iPP’s melt self-enhancement. Under a comparatively low re-saturation pressure of 8 to 12 MPa, ideal microcellular foams could be generated, at a temperature zone of 158 to 162°C, which is slightly below to iPP’s original pellets nominal melting point.
WangYXuJZChenYH, et al.
Crystalline structure changes in preoriented metallocene-based isotactic polypropylene upon annealing. J Phys Chem B2013;
117: 7113–7122.
2.
LiD-CLiuTZhaoL, et al.
Foaming of linear isotactic polypropylene based on its non-isothermal crystallization behaviors under compressed CO2. J Supercrit Fluids2011;
60: 89–97.
3.
SoaresFANachtigallSMB.Effect of chemical and physical foaming additives on the properties of PP/wood flour composites. Polym Test2013;
32: 640–646.
4.
RizviAAndalibZKMParkCB.Fiber-spun polypropylene/polyethylene terephthalate microfibrillar composites with enhanced tensile and rheological properties and foaming ability. Polymer2017;
110: 139–148.
5.
NofarMMajithiyaKKubokiT, et al.
The foamability of low-melt-strength linear polypropylene with nanoclay and coupling agent. J Cellu Plast2012;
48: 271–287.
6.
HuangH-XWangJ-K.Improving polypropylene microcellular foaming through blending and the addition of nano-calcium carbonate. J Appl Polym Sci2007;
106: 505–513.
7.
LeeJWSParkCBKimSG.Reducing material costs with microcellular/fine-celled foaming. J Cellu Plast2007;
43: 297–312.
8.
AmeliANofarMParkCB, et al.
Polypropylene/carbon nanotube nano/microcellular structures with high dielectric permittivity, low dielectric loss, and low percolation threshold. Carbon2014;
71: 206–217.
9.
AmeliAKazemiYWangS, et al.
Process-microstructure-electrical conductivity relationships in injection-molded polypropylene/carbon nanotube nanocomposite foams. Composites Part A2017;
96: 28–36.
10.
KuoC-CLiuL-CLiangW-C, et al.
Preparation of polypropylene (PP) composite foams with high impact strengths by supercritical carbon dioxide and their feasible evaluation for electronic packages. Composites Part B2015;
79: 1–5.
11.
FuDChenFKuangT, et al.
Supercritical CO2 foaming of pressure-induced-flow processed linear polypropylene. Mater Des2016;
93: 509–513.
12.
BaoJ-BNyantakyi JuniorAWengG-S, et al.
Tensile and impact properties of microcellular isotactic polypropylene (PP) foams obtained by supercritical carbon dioxide. J Supercrit Fluids2016;
111: 63–73.
13.
LeePCKaewmesriWWangJ, et al.
Effect of die geometry on foaming behaviors of high-melt-strength polypropylene with CO2. J Appl Polym Sci2008;
109: 3122–3132.
14.
JiangX-LLiuTXuZ-M, et al.
Effects of crystal structure on the foaming of isotactic polypropylene using supercritical carbon dioxide as a foaming agent. J Supercrit Fluids2009;
48: 167–175.
15.
XuZ-MJiangX-LLiuT, et al.
Foaming of polypropylene with supercritical carbon dioxide. J Supercrit Fluids2007;
41: 299–310.
16.
ZhangXLDingWDZhaoN, et al.
Effects of compressed CO2 and cotton fibers on the crystallization and foaming behaviors of polylactide. Ind Eng Chem Res2018;
57: 2094–2104.
17.
ZhangXLLiBWWangXH, et al.
Modification of iPP microcellular foaming behavior by thermal history control and nucleating agent at compressed CO2. J Supercrit Fluids2018;
133: 383–392.
18.
LiaoXNawabyAVWhitfieldPS.Carbon dioxide-induced crystallization in poly(L-lactic acid) and its effect on foam morphologies. Polym Int2010;
59: 1709–1718.
KaewmesriWRachtanapunPPumchusakJ.Effect of solvent plasticization on polypropylene microcellular foaming process and foam characteristics. J Appl Polym Sci2008;
107: 63–70.
21.
ZhaiWWangHYuJ, et al.
Foaming behavior of isotactic polypropylene in supercritical CO2 influenced by phase morphology via chain grafting. Polymer2008;
49: 3146–3156.
22.
LiYYaoZChenZ-H, et al.
High melt strength polypropylene by ionic modification: preparation, rheological properties and foaming behaviors. Polymer2015;
70: 207–214.
23.
RapsDKöpplTAndaAR, et al.
Rheological and crystallization behaviour of high melt strength polypropylene under gas-loading. Polymer2014;
55: 1537–1545.
24.
LeungSNParkCBLiHB.Effects of nucleating agent’s shape and interfacial properties on cell nucleation. J Cellu Plast2010;
46: 441–460.
25.
ZhaiWParkCB.Effect of nanoclay addition on the foaming behavior of linear polypropylene-based soft thermoplastic polyolefin foam blown in continuous extrusion. Polym Eng Sci2011;
51: 2387–2397.
26.
LeeSHKontopoulouMParkCB.Effect of nanosilica on the co-continuous morphology of polypropylene/polyolefin elastomer blends. Polymer2010;
51: 1147–1155.
27.
ZhangZ-XChenD-LKwakK-H, et al.
Effects of compatibilizers on the physico-mechanical and foaming properties of polypropylene/wood-fiber composites. J Vinyl Addit Technol2013;
19: 250–257.
AmeliANofarMWangS, et al.
Lightweight polypropylene/stainless-steel fiber composite foams with low percolation for efficient electromagnetic interference shielding. ACS Appl Mater Interfaces2014;
6: 11091–11100.
30.
OkolieochaCRapsDSubramaniamK, et al.
Microcellular to nanocellular polymer foams: progress (2004–2015) and future directions – a review. Eur Polym J2015;
73: 500–519.
31.
ZhangPWangX-JYangY, et al.
Effect of dynamic shear on the microcellular foaming of polypropylene/high-density polyethylene blends. J Appl Polym Sci2009;
114: 1320–1328.
32.
RachtanapunPSelkeSEMMatuanaLM.Effect of the high-density polyethylene melt index on the microcellular foaming of high-density polyethylene/polypropylene blends. J Appl Polym Sci2004;
93: 364–371.
33.
WuQFParkCBZhouNQ, et al.
Effect of temperature on foaming behaviors of homo- and co-polymer polypropylene/polydimethylsiloxane blends with CO2. J Cellu Plast2004;
44: 1551–1560.
34.
ZhengWGLeeYHParkCB.Use of nanoparticles for improving the foaming behaviors of linear PP. J App Poly Sci2010;
117: 2972–2979.
35.
MiyamotoRYasuharaSShikumaH, et al.
Preparation of micro/nanocellular polypropylene foam with crystal nucleating agents. Polym Eng Sci2014;
54: 2075–2085.
36.
RizviAParkCBFavisBD.Tuning viscoelastic and crystallization properties of polypropylene containing in-situ generated high aspect ratio polyethylene terephthalate fibrils. Polymer2015;
68: 83–91.
37.
BalkanOEzdeşirA.Rheological behaviors of glass bead- and wollastonite-filled polypropylene composites modified with thermoplastic elastomers. Polym Compos2012;
33: 1162–1187.
38.
DingJMaWSongF, et al.
Effect of nano-calcium carbonate on microcellular foaming of polypropylene. J Mater Sci2013;
48: 2504–2511.
39.
HuangH-XXuH-F.Preparation of microcellular polypropylene/polystyrene blend foams with tunable cell structure. Polym Adv Technol2011;
22: 822–829.
40.
SreenivasKBasargekarRKumaraswamyG.Phase separation of DMDBS from PP: effect of polymer molecular weight and tacticity. Macromolecules2011;
44: 2358–2364.
41.
KristiansenMWernerMTervoortT, et al.
The binary system isotactic polypropylene DMDBS phase behavior nucleation and optical properties. Macromolecules2003;
36: 5150–5156.
42.
LippJShusterMFeldmanG, et al.
Oriented crystallization in polypropylene fibers induced by a sorbitol-based nucleator. Macromolecules2008;
41: 136–140.
43.
BalzanoLRastogiSPetersG-W-M.Flow induced crystallization in isotactic polypropylen-1, 3: 2, 4-bis(3,4-dimethylbenzylidene) sorbitol blends: implication on morphology of shear and phase separation. Macromolecules2008;
41: 399–408.
44.
ZhangBChenJBZhangXL, et al.
Crystal morphology and structure of the β-form of isotactic polypropylene under supercooled extrusion. J Appl Polym Sci2011;
120: 3255–3264.
45.
ZhangBChenJBJiFF, et al.
Y effects of melt structure on shear-induced β-cylindrites of isotactic polypropylene. Polymer2012;
53: 1791–1800.
46.
ZhuXYLiYJYanDY.Crystallization behavior of partially melting isotactic polypropylene. Polymer2001;
22: 9217–9222.
47.
CavalloDAzzurriFBalzanoL, et al.
Flow memory and stability of shear-induced nucleation precursors in isotactic polypropylene. Macromolecules2010;
43: 9394–9400.
48.
MartinsJAZhangWBritoAM.Origin of the melt memory effect in polymer crystallization. Polymer2010;
51: 4185–4194.
49.
ZhangXLWangXHSunBJ, et al.
Broadened foaming scope of iPP adjusted by its self-enhancement and nucleating agent under compressed CO2. Mater Today Commun2018;
17: 501–510.
50.
BalzanoLPortaleGPetersG-W-M, et al.
Thermoreversible DMDBS phase separation in iPP: the effects of flow on the morphology. Macromolecules2008;
41: 5350–5355.
51.
NofarMAmeliAParkCB.Development of polylactide bead foams with double crystal melting peaks. Polymer2015;
69: 83–94.
52.
NaguibHEParkCBSongSW.Effect of supercritical gas on crystallizaiton of linear and banched polypropylene resins with foaming additives. Ind Eng Chem Res2005;
44: 6685–6691.