Effect of polymer foam anisotropy on energy absorption during combined shear-compression loading

Abstract

Polymeric foams are extensively used in applications such as packaging, sports goods and sandwich structures. Since in-service loading conditions are often multi-axial, characterisation of foams under multi-axial loading is essential. In this article, quasi-static combined shear-compression behaviour of isotropic expanded polystyrene foam and anisotropic polyethersulfone foam was studied. For this, a testing apparatus which can apply combined compression and transverse shear loads was developed. The results revealed that the shear and compression energy absorption, yield stress and stiffness of foams are dependent on deformation angle. The total energy absorption of the anisotropic polyethersulfone foam is shown to be direction dependent in contrast to isotropic expanded polystyrene. Furthermore, for similar relative density, polyethersulfone foam absorbs more energy than expanded polystyrene foam, regardless of deformation angle. This study highlights the importance of correct positioning of foam cells in anisotropic foams with respect to loading direction to maximise energy absorption capability.

Keywords

Polymer foam anisotropy combined shear-compression biaxial loading energy absorption

Get full access to this article

View all access options for this article.

References

Gibson LJ and Ashby MF. Cellular solids: Structure and properties. 2nd ed. Cambridge, UK: Cambridge University Press, 1997.

Reignier

Gendron

. Mechanical anisotropy of PS/CO2 microcellular foam sheet prepared by foaming extrusion. J Cell Plast 2016; 0: 1–15.

Tissandier

González-Núñez

Rodrigue

. Asymmetric microcellular composites: Mechanical properties and modulus prediction. J Cell Plast 2016; 52: 365–398.

Kuboki

. Mechanical properties and foaming behavior of injection molded cellulose fiber reinforced polypropylene composite foams. J Cell Plast 2014; 50: 129–143.

Arcan

Hashin

Voloshin

. A method to produce uniform plane-stress states with applications to fiber-reinforced materials. Exp Mech 1978; 18: 141–146.

Gdoutos

Daniel

. Failure of cellular foams under multiaxial loading. Compos Part A-Appl S 2002; 33: 163–176.

Mines

RAW

Birch

. The crush behaviour of Rohacell-51WF structural foam. Int J Solids Struct 2000; 37: 6321–6341.

Doyoyo

Wierzbicki

. Experimental studies on the yield behavior of ductile and brittle aluminum foams. Int J Plast 2003; 19: 1195–1214.

Mohr

Doyoyo

. Experimental investigation on the plasticity of hexagonal aluminum honeycomb under multiaxial loading. J Appl Mech 2004; 71: 375–385.

10.

Benderly

Putter

. Characterization of the shear/compression failure envelope of Rohacell foam. Polym Test 2004; 23: 51–57.

11.

Kintscher

Kärger

Wetzel

et al.

Stiffness and failure behaviour of folded sandwich cores under combined transverse shear and compression. Compos Part A-Appl S 2007; 38: 1288–1295.

12.

Hong

Pan

Tyan

et al.

Dynamic crush behaviors of aluminum honeycomb specimens under compression dominant inclined loads. Int J Plast 2008; 24: 89–117.

13.

Taher

Thomsen

Dulieu-Barton

et al.

Determination of mechanical properties of PVC foam using a modified Arcan fixture. Compos Part A-Appl S 2012; 43: 1698–1708.

14.

Hou

Ono

Abdennadher

et al.

Impact behavior of honeycombs under combined shear-compression. Part I: experiments. Int J Solids Struct 2011; 48: 687–697.

15.

Hou

Pattofatto

et al.

Impact behavior of honeycombs under combined shear-compression. Part II: analysis. Int J Solids Struct 2011; 48: 698–705.

16.

Tounsi

Markiewicz

Haugou

et al.

Dynamic behaviour of honeycombs under mixed shear-compression loading: experiments and analysis of combined effects of loading angle and cells in-plane orientation. Int J Solids Struct 2016; 80: 501–511.

17.

Ashab

ASM

Dong

et al.

Quasi-static and dynamic experiments of aluminum honeycombs under combined compression-shear loading. Mater Design 2016; 97: 183–194.

18.

Zhou

Wang

Zhao

et al.

Experimental investigation on the yield behavior of Nomex honeycombs under combined shear-compression. Lat Am J Solids Struct 2012; 9: 515–530.

19.

Zhang

Jin

Wang

et al.

Experimental investigation on yield behavior of PMMA under combined shear–compression loading. Results Phys 2016; 6: 265–269.

20.

Magkiriadis

Harrigan

. Compressive strain at the onset of densification of cellular solids. J Cell Plast 2006; 42: 371–392.