Poly (lactic acid)/maleic-anhydride-grafted-polypropylene (PLA/MAPP) blends were prepared by melt blending method. The effect of MAPP content on the dispersion morphology, thermal properties, and rheological behavior of PLA/MAPP blends was studied. Then PLA/MAPP blends were foamed using supercritical CO2 as physical blowing agent; and the cellular structure, cell size, as well as cell density were investigated. The results showed that of MA reacted with PLA, and thus a small amount of branched polymer would be formed. The branching structure strongly affected the rheological behavior, as well as the thermal properties of PLA. The blending morphology of PLA/MAPP blends also had a significant effect on the cell density of all the samples. The results indicated that homogeneous and finer cellular morphology for PLA/MAPP foams with high expansion ratio could be achieved with a proper content of MAPP in the blends.
DorganJRLehermeierHJPaladeLI. Polylactides: properties and prospects of an environmentally benign plastic from renewable resources. J Macromol Sympos2001; 175: 55–66.
ByunYKimYTWhitesideS. Characterization of an antioxidant polylactic acid (PLA) film prepared with α-tocopherol, BHT and polyethylene glycol using film cast extruder. J Food Eng2010; 100: 239–244.
4.
GarlottaD. A literature review of poly (lactic acid). J Polym Environ2001; 100: 63–68.
5.
AurasRASinghSPSinghJJ. Performance evaluation of PLA against existing PET and PS containers. J Test Eval2006; 34: 530–536.
6.
SawyerDJ. Bioprocessing – no longer a field of dreams. Macromol Sympos2003; 201: 271–282.
7.
LiuWWangXLiH. Study on rheological and extrusion foaming behaviors of chain-extended poly (lactic acid)/clay nanocomposites. J Cell Plast2013; 49: 535–554.
8.
PaviaFCLa CarrubbaVBrucatoV. Morphology and thermal properties of foams prepared via thermally induced phase separation based on polylactic acid blends. J Cell Plast2012; 48: 399–407.
9.
CuénoudMBourbanPEPlummerCJG. Plasticization of polylactide foams for tissue engineering. J Cell Plast2012; 48: 409–432.
10.
BoissardCIRBourbanPEPlummerCJG. Cellular biocomposites from polylactide and microfibrillated cellulose. J Cell Plast2012; 48: 445–458.
11.
WangLJingXChengH. Blends of linear and long-chain branched poly(L-lactide)s with high melt strength and fast crystallization rate. Ind Eng Chem Res2012; 51: 10088–10099.
12.
DiYWIannaceSDi MaioE. Reactively modified poly (lactic acid): properties and foam processing. J Macromol Mater Eng2005; 290: 1083–1090.
13.
LiuWLiHWangX. Effect of chain extension on the rheological property and thermal behaviour of poly (lactic acid) foams. Cell Polym2013; 32(6): 343–367.
14.
WangLMaWGrossRA. Reactive compatibilization of biodegradable blends of poly(lactic acid) and poly(ɛ-caprolactone). Polym Degrad Stab1998; 59: 161–168.
15.
WangXLiuWZhouH. Study on the effect of dispersion phase morphology on porous structure of poly (lactic acid)/poly (ethylene terephthalate glycol-modified) blending foams. Polymer2013; 54(21): 5839–5851.
16.
De RooverBSclavonsMCarlierV. Molecular characterization of maleic anhydride‐functionalized polypropylene. J Polym Sci Part A Polym Chem1995; 33(5): 829–842.
17.
JaponSBooghLLeferrierY. Reactive processing of poly(ethylene terephthalate) modified with multifunctional epoxy-based additive. Polymer2000; 41: 5809–5818.
18.
UpadhyayDMohantySNayakSK. Impact modification of poly (trimethylene terephthalate)/polypropylene blend nanocomposites: fabrication and characterization. J Appl Polym Sci2011; 120: 932–943.
19.
MarcoCEllisGGomezMA. Rheological properties, crystallization, and morphology of compatibilized blends of isotactic polypropylene and polyamide. J Appl Polym Sci1997; 65: 2665–2677.
20.
KimHSLeeBHChoiSW. The effect of types of maleic anhydride-grafted polypropylene (MAPP) on the interfacial adhesion properties of bio-flour-filled polypropylene composites. Compos Part A Appl Sci Manuf2007; 38: 1473–1482.
ZhaiWKoYZhuW. A study of the crystallization, melting, and foaming behaviors of polylactic acid in compressed CO2. Int J Mol Sci2009; 10: 5381–5397.
23.
Lee ST, Park CB and Ramesh NS. Polymeric foams: science and technology. vol. 3. Florida, United States: CRC press, 2006.
24.
TakadaMHasegawaSOhshimaM. Crystallization kinetics of poly(L-lactide) in contact with pressurized CO2. Polym Eng Sci2004; 44: 186–196.
25.
MihaiMHuneaultMAFavisBD. Crystallinity development in cellular poly(lactic acid) in the presence of supercritical carbon dioxide. J Appl Polym Sci2009; 113: 2920–2932.
26.
FischerEWSterzelJHWegnerG. Investigation of the structure of solution grown crystals of lactide copolymers by means of chemical reactions. Coll Polym Sci1973; 251: 980–990.
27.
MengQHeuzeyMCCarreauPJ. Control of thermal degradation of polylactide/clay nanocomposites during melt processing by chain extension reaction. Polym Degrad Stab2012; 97: 2010–2020.
28.
WangLYJingXBHuangYB. Blends of linear and long-chain branched poly(L-lactide)s with high melt strength and fast crystallization rate. Ind Eng Chem Res2012; 51: 10088–10099.
29.
WangJZhuWZhangH. Continuous processing of low-density, microcellular poly (lactic acid) foams with controlled cell morphology and crystallinity. Chem Eng Sci2012; 75: 390–399.
30.
YuFZhangHLiaoR. Flow induced crystallization of long chain branched polypropylenes under weak shear flow. Eur Polym J2009; 45: 2110–2118.
31.
HingmannRMarczinkeBL. Shear and elongational flow properties of polypropylene melts. J Rheol1994; 38: 573–588.
32.
NaguibHEParkCBReicheltN. Strategies for achieving ultra low-density polypropylene foams. Polym Eng Sci2002; 42: 1481–1492.
33.
Hartland S (ed.) Surface and interfacial tension: measurement, theory, and applications. vol. 119. Florida, United States: CRC press, 2004.