Improvement of Cell Opening by Maintaining a High Temperature Difference in the Surface and Core of a Foam Extrudate

Abstract

This article presents an extrusion-based, open-cell foaming process using thermoplastic polymers such as polystyrene (PS) and polycarbonate (PC) with supercritical CO₂. Our previous studies have indicated that a cell opening can be promoted by inducing: (i) a nonhomogeneous melt structure by cross-linking, polymer blending, or filler compounding, (ii) cell-wall thinning by a high volume expansion ratio while maintaining soft cell walls, (iii) cell-wall thinning by a high cell-population density, and (iv) plasticization of the soft region of the cell walls with a secondary blowing agent. Until now, the foam extrudate temperature across the cross-section was maintained uniformly for the simplicity of the experiments. In this study, the significant temperature difference between the core and surface of the foam extrudate was induced by surface cooling method. This method increased the chance of cell opening by: (i) increasing the core temperature of the foam extrudate and thereby softening the cell walls, and (ii) decreasing the foam surface temperature to prevent gas loss and thereby increasing the internal gas pressure within the cells. The effects of CO₂ content, surface quenching, die geometry, and temperature on foam morphologies were investigated. Low-density, microcellular, open-cell foams were successfully produced. The large intercellular pores were observed from micrographs for both PS and PC foams at optimum processing conditions.

Keywords

low-density microcellular foam cell opening polymer blending pressure drop rate CO2.

Get full access to this article

View all access options for this article.

References

Klempner, D. and Frisch, K.C. (1991). Handbook of Polymeric Foams and Foam Technology , Hanser Publishers, Munich, Vienna, New York, Barcelona .

Thomas, C.R. (1965). Br. Plastics Moulded Prod . Trader , 38: 552—558.

Chaudhary, B.I. and Barry, R.P. (1999). Extruded Noncrosslinked Foams Made From Ethylene-Stylene Interpolymer, Foams, 99: 19—33.

Kaji, K. , Hatada, M. , Yoshizawa, I. and Kohara, C. (1989). Preparation of Hydrophilic Polyethylene Foam of Open Cell Type by Radiation Grafting of Acrylic Acid, J. Appl. Polym. Sci., 37: 2153—2164.

Kozma, M.L., Bambara, J.D. and Hurley, R.F. (1999). U.S. Patent 5,859,076.

Chaudhary, B.I. and Malone, B.A. (1999). U.S. Patent 5,962,545.

Abe, S. (2002). U.S. Patent 6,414,047 B1.

Browers, S.D. and Wiegand, D.E. (1980). U.S. Patent 4,183,984.

Hale, W.R. , Dohrer, K.K. , Tant, M.R. and Sand, I.D. (2001). A Diffusion Model For Water Vapor Transmission Through Microporous Polyethylene/ CaCO3 Films, Colloids Surf. A, 187: 483.

10.

Huang, Q. , Seibig, B. and Paul, D. (1999). Polycarbonate Hollow Fiber Membranes by Melt Extrusion , J. Membrane Sci., 161: 287—291.

11.

Huang, Q. , Seibig, B. and Paul, D. (2000). Melt Extruded Open-Cell Mircocellular Foams for Membrane Separation: Processing and Cell Morphology Relationship, J. Cellular Plast., 36: 112—125.

12.

Park, C.B. , Padareva, V. , Lee, P.C. and Naguib, H.E. (2005). Extruded Open-Celled LDPE and LDPE/PS Foams Using Non-Homogeneous Melt Structure, J. Polym. Eng., 25: 239—260.

13.

Lee, P.C. , Naguib, H.E. , Park , C.B. and Wang, J. (2005). Increase of Open-Cell Content by Introducing a Secondary Blowing Agent, Polym. Eng. Sci., 45: 1445—1451.

14.

Lee, P.C. , Wang, J. and Park, C.B. (2006). Extruded Open-Cell Foams Using Two Semicrystalline Polymers with Different Crystallization Temperatures , Ind. Eng. Chem. Res., 45: 175—181.

15.

Lee, P.C. , Wang, J. and Park, C.B. (2006). Extrusion of Microcellular Open-Cell LDPE-Based Sheet Foams, J. Appl. Polym. Sci., 102: 3376—3384.