Experimental Investigation of E/M Impedance Health Monitoring for Spot-Welded Structural Joints

Abstract

Health monitoring results obtained during fatigue testing of a spot-welded lap-shear structural-joint specimen using the electromechanical (E/M) impedance technique are presented. The test specimens were instrumented with piezoelectric wafer transducers, and the base E/M impedance signature was recorded in the 200-1,100 kHz frequency range. Fatigue testing was applied to initiate and propagate crack damage of controlled magnitude. Calibration tests using plain specimens were first performed to correlate stiffness decrease with damage progression and remaining life. During the subsequent health-monitoring tests, the decrease in structural stiffness was used to assess damage progression in the specimen. As damage progressed, the E/M impedance signatures were recorded at predetermined intervals. Signature data were processed, and the RMS impedance change was calculated. Damage index values were observed to increase as crack damage increases. The initiation and propagation of damage was successfully correlated with the E/M impedance measurements. Sensing and the localization principles of E/M impedance method were confirmed, and the rejection of spurious information was verified. These experiments demonstrated that the E/M impedance technique is a potentially powerful tool for damage detection, health monitoring, and NDE of spot-welded structural joints.

Get full access to this article

View all access options for this article.

References

Giurgiutiu, V. and Rogers, C. A. , 1997, "The Electro-Mechanical (E/M) Impedance Method for Structural Health Monitoring and Non-Destructive Evaluation," International Workshop on Structural Health Monitoring, Stanford University, CA, September 18-20, 1997.

Giurgiutiu, V. , Rogers, C. A. , Chao, Y. J. , Sutton, M. A. and Deng, X. , 1997, "Adaptive Health Monitoring Concepts for Spot-Welded and Weld-bonded Structural Joints," Proceedings of the ASME Aerospace Division, AD-Vol. 54, ASME, November 1997, pp. 99-104.

Liang, C. , Sun, F. P. and Rogers, C. A. , 1993, "An Impedance Method for Dynamic Analysis of Active Material Systems," Proceedings, 34th AIAA/ASME/ASCE/AHS/ASC SDM Conference, La Jolla, CA, 19-21 April 1993; pp. 3587-3599.

Liang, C. , Sun, F. P. and Rogers, C. A. , 1996, "Electro-mechanical Impedance Modeling of Active Material Systems," Smart Materials and Structures, Vol. 5, pp. 171-186.

Razvan, A., Reifsnider, K. L. and Elahi, M., 1994, "Dynamic Characterization of Material Strength and Life under Cyclic Loading." Patent No. 5,305,645, April 26, 1994, Durability, Inc., Blacksburg, VA.

Rogers, C. A. and Giurgiutiu, V. , 1997. "Electro-Mechanical (E/M) Impedance Technique for Structural Health Monitoring and Non-Destructive Evaluation," Invention Disclosure No. 97162, University of South Carolina Office of Technology Transfer, July 1997.

Salvini, P. , Scardecchai, E. and Demfonti, G. , "A Procedure for Fatigue Life Prediction of Spot Welded Joints," Fatigue and Fracture of Engineering Materials and Structures, vol. 20, No. 8, pp. 1117-1128, 1997.