On the Oxidative Degradation of Nadic Endcapped Polyimides: I. Effect of Thermocycling on Weight Loss and Crack Formation

Abstract

The effects of thermocycle frequency, aging temperature and post-cure conditions on weight loss, microhardness and crack formation of PMR-15 neat resins were investigated. Crack formation was monitored by metallography. The molecular level changes, occurring under the same conditions, were monitored by microscopic FT-IR in reflectance mode on the same samples. FT-IR analysis was carried out in zones 100 μm in diameter, allowing examination of different regions of the aged samples. It was found that weight loss, crack formation and microhardness were highly dependent on aging time and temperature, but not thermocycling frequency. Molecular level changes were also highly correlated to time and temperature of aging. Both the physical effects of aging and the chemical effects were isolated to a thin surface layer. No changes whatsoever to the interiors of the samples were evident by FT-IR, microhardness or microscopy.

Get full access to this article

View all access options for this article.

References

[1] Meador M A , Cavano P J and Malarik D C 1990 Proc. 6th Ann. ASM/ESD Advanced Composites Conf. pp 529–539

[2] Serafini T T , Delvigs P and Lightsey G R 1972 J. Appl. Polym. Sci. 16 905–915

[3] Alston W B 1981 SAMPE J. March/April 5–13

[4] Young P R and Chang A C 1988 Proc. 33rd Int. SAMPE Symp. pp 538–550

[5] Wilson D , Wells J K , Hay J N , Lind D , Owens G A and Johnson F 1987 SAMPE J. May/June 35–42

[6] Bowles K J , Jayne D and Leonhardt T A 1993 Sampe Q. 24 2–9

[7] Lady J H , Kesse I and Adams R E 1960 J. Appl. Polym. Sci. 71–76

[8] Kuroda S and Mita I 1989 Eur. Polym. J. 25 611–620

[9] Milhourat-Hammadi A , Gaudemer F , Merienne C and Gaudemer A 1994 J. Polym. Sci., Part A: Polym. Chem. 32 1593–1597

10.

[10] Frimer A A 1979 Chem. Rev. 79 363-363

11.

[11] Frimer A A , Cavano P J and Alston W B 1995 High Perform. Polym. 7 93–104

12.

[12] Hay J N , Boyle J D , Parker S F and Wilson D 1989 Polymer 30 1032–1040

13.

[13] Alston W B , Gluyas R E and Snyder W J 1992 NASA Technical Memorandum 105629-105629

14.

[14] Simpson M , Jacobs P M and Jones F R 1991 Composites 22 105–112

15.

[15] See for example, Sutter J K , Jobe J M and Crane E A 1995 J. Appl. Polym. Sci. 57 1491–1499