The dissolution of a Nigerian lepidolite ore in sulphuric acid solution for its optimal industrial transformation was carried out. The degree of influence of the acid concentration, reaction temperature, particle diameter, and reaction time on the rate of the ore dissolution was investigated. These parameters were observed to enhance the rate of the dissolution as the acid concentration was increased from 0.1 to 1.5 mol/L, reaction temperature from room temperature (27 ± 2°C) to 75°C, particle diameter from 63 to 90 µm and reaction time from 5 to 120 min, respectively. The ore dissolution kinetics was studied using the shrinking core model, based on which the process was found to follow a diffusion-controlled mechanism as the rate-determining step. The activation energy of 18.1 kJ/mol lends support to this assertion. At optimal conditions, the formation of a pure lepidolite crystal (K2Li3Al3Si7O21F3: (96-900-0834)), recommended as a precursor for preparing industrial lithium sulphate was obtained.
AkintolaOF, AdekeyeJID.2008. Mineralization potentials of pegmatites in the Nasarawa area of Central Nigeria. Earth Sci Res J. 12(2):213–234.
2.
AmerAM.2008. The hydrometallurgical extraction of lithium from Egyptian montmorillonite-type clay. JOM-J Min Met Mat S. 60:55–57.
3.
BabaAA, BalogunAF, OlaoluwaDT, BaleRB, AdekolaFA, AlabiAGF.2017. Leaching kinetics of a Nigerian complex covellite ore by the ammonia-ammonium sulfate solution. Korean J Chem Eng. 34(4):1133–1140.
4.
BabaAA, OlaoluwaDT, AlabiAGF, BalogunAF, IbrahimAS, SanniRO, BaleRB.2018. Dissolution behaviour of a beryl ore for optimal industrial beryllium compound production. Can Metall Q. 57(2):210–218.
5.
BabaAA, OlaoluwaDT, AyinlaKI, IbrahimAS, BalogunAF, GirigisuS, AdebolaOM, FasikuJ.2022. Treatment of an indigenous lepidolite ore for sustainable energy considerations. In: TesfayeF, editor. REWAS 2022: energy technologies and CO2 management (Vol. II). The minerals, metals & materials series. Cham: Springer; p. 73–80.
6.
ChenJ, YangS, KeJ.1998. The studies and progress of metallurgy. Beijing: China Metallurgy Industry Press.
7.
ChenY, TianQ, ChenB, ShiX, LiaoT.2011. Preparation of lithium carbonate from spodumene by a sodium carbonate autoclave process. Hydrometallurgy. 109:43–46.
8.
ChiR, ZhuG, TianJ.2000. Leaching kinetics of rare earth from black weathering mud with hydrochloric acid. Trans Nonferr Metals Soc China. 10:531–533.
9.
GaoL, WangH, LiJ, WangM.2020. Recovery of lithium from lepidolite by sulfuric acid and separation of Al/Li by nanofiltration. Minerals. 10(11):1–17.
10.
GarbaI.2003. Geochemical discrimination of newly discovered rare-metal bearing and barren pegmatites in the Pan-African (600 ± 150Ma) basement of northern Nigeria. Appl Earth Sci (Trans Inst Min Metall). 112:287–292.
11.
GuH, GuoT, WenH, LuoC, CuiY, DuS, WangN.2020. Leaching efficiency of sulfuric acid on selective lithium leachability from bauxitic claystone. Miner Eng. 145:106076.
12.
GuanJ, ZhouZ, LiN, LiuZ, WenH, LiJ, HuL, LiuL, LuoC.2022. Extracting lithium from the H2SO4 leaching solution of bauxitic claystone via co-precipitation methods without addition of Al source. Chem Eng J Adv. 9:100223.
13.
GuoH, KuangG, LiH, PeiW, WangH.2021. Enhanced lithium leaching from lepidolite in continuous tubular reactor using H2SO4 H2SiF6 as lixiviant. Trans Nonferrous Met Soc China. 31:2165–2173.
14.
Hien-DinhTT, LuongVT, GieréR, TranT.2015. Extraction of lithium from lepidolite via iron sulphide roasting and water leaching. Hydrometallurgy. 153:154–159.
15.
JandováJ, DvořákP, VuHN.2010. Processing of Zinnwaldite waste to obtain Li2CO3. Hydrometallurgy. 103:12–18.
16.
JohnsonGD, UrganiMD, VinesNJ.2015. Recovery process. AU Patent A2014904050.
17.
KuangG, LiuY, LiH, XingS, LiF, GuoH.2018. Extraction of lithium from β-spodumene using sodium sulfate solution. Hydrometallurgy. 177:49–56.
18.
LeeJ.2015. Extraction of lithium from lepidolite using mixed grinding with sodium sulfide followed by water leaching. Minerals. 5:737–743.
19.
LiuJ, YinZ, LiX, HuQ, LiuW.2019. Recovery of valuable metals from lepidolite by atmosphere leaching and kinetics on dissolution of lithium. Trans Nonferrous Met Soc China. 29:641–649.
20.
LuongVT, KangDJ, AnJW, DaoDA, KimMJ, TranT.2014. Iron sulphate roasting for extraction of lithium from lepidolite. Hydrometallurgy. 141:8–16.
21.
LuongVT, KangDJ, AnJW, KimMJ, TranT.2013. Factors affecting the extraction of lithium from lepidolite. Hydrometallurgy. 134-135:54–61.
22.
MarcinčákováR, KadukováJ, MražíkováA.2015a. Bioleaching of lithium from lepidolite by the mixture of Rhodotorularubra and Acidithiobacillusferrooxidans. Inżynieria Mineralna J Pol Mineral Eng Soc. 1(35):85–88.
23.
MarcinčákováR, KadukováJ, MražíkováA, VelgosováO, VojtkoM.2015b. Lithium bioleaching from lepidolite using the yeast Rhodotorularubra. Inżynieria Mineralna J Pol Mineral Eng Soc. 1(35):1–6.
OlaoluwaDT.2022. Hydrometallurgical processing of Nigerian montebrasite and lepidolite ores as battery and drug delivery agents. PhD Seminar Report, Department of Industrial Chemistry, University of Ilorin, Unpublished.
26.
PeerawattukI, BobickiER.2018. Lithium extraction and utilization: a historical perspective. In: Boyd et al. editors. Extraction 2018. The minerals, metals and materials series. Cham: Springer; p. 2209–2224.
27.
RezzaI, SalinasE, CalventeV, BenuzziD, Sanz de TosettiMI.1997. Extraction of lithium from spodumene by bioleaching. Lett Appl Microbiol. 25(3):172–176.
28.
Sedlakova-KadukovaJ, MarcincakovaR, LuptakovaA, VojtkoM, FujdaM, PristasP.2020. Comparison of three different bioleaching systems for Li recovery from lepidolite. Sci Rep. 10:1–8.
29.
TianJ, YinJ, ChiR, RaoG, JiangM, OuyangK.2010. Kinetics on leaching rare earth from the weathered crust elution-deposited rare earth ores with ammonium sulfate solution. Hydrometallurgy. 101:166–170.
30.
USGS- US Geological Survey. 2022. Minerals commodity summaries – lithium. Virginia: USGS. ISBN 978–1–4113–3548–6, 94-95.
31.
VieceliN, NogueiraCA, PereiraMFC, DurãoFO, GuimarãesC, MargaridoF.2017. Optimization of lithium extraction from lepidolite by roasting using sodium and calcium sulfates. Miner Process Extr Metall Rev. 38(1):62–72.
32.
WangH, ZhongY, DuB, ZhaoY, WangM.2018. Recovery of both magnesium and lithium from high Mg/Li ratio brines using a novel process. Hydrometallurgy. 175:102–108.
33.
WangH, ZhouA, GuoH, LüM, YuH.2020. Kinetics of leaching lithium from lepidolite using mixture of hydrofluoric and sulfuric acid. J Cent South Univ. 27:27–36.
34.
YanQ, LiX, WangZ, WuX, GuoH, HuQ, PengW, WangJ.2012a. Extraction of valuable metals from lepidolite. Hydrometallurgy. 117-118:116–118.
35.
YanQ, LiX, WangZ, WuX, WangJ, GuoH, HuQ, PengW.2012b. Extraction of lithium from lepidolite by sulfation roasting and water leaching. Int J Miner Process. 110-111:1–5.
36.
ZhangL, ZhangY, ZhangX, TanX.2019a. Extraction of Li, Rb, Cs from lepidolite by sulfuric acid and water leaching. Nonferr Metals (Extr Metall). 04:39–42.