Dynamic mechanical analysis (DMA) was used to investigate the viscoelastic behaviour of four species of wood, Scots pine, Gmelina, Obeche and Alstonia. Three frequencies (0.1, 1.0 and 10 Hz) were used over a temperature range of −150°C to +150°C. All the wood species showed tan δ peaks corresponding with secondary relaxations in the expected range. The low temperature (γ peak) was seen at −115°C to −83°C, differing between species and with frequency. β peaks relating to hemicellulose relaxations in association with water molecules were observed, at two locations for Scots pine and three locations in hardwoods. The α peak for lignin lay outside the temperature range studied. Differences in β peaks are proposed to relate to the composition of hemicellulose, and be influenced by structure and level of heterogeneity in the amorphous polymer domains; differing between the wood species studied, which is in-line with currently proposed cell wall polymer models.
ÅkerholmM, SalménL.2001. Interaction between wood polymers studied by dynamic FT-IR spectroscopy. Polymer. 42:963–969. doi: 10.1016/S0032-3861(00)00434-1
2.
ÅkerholmM, SalménL.2003. The oriented structure of lignin and its viscoelastic properties studied by static and dynamic FT-IR spectroscopy. Holzforschung. 57:459–465. doi: 10.1515/HF.2003.069
3.
ÅkerholmM, SalménL.2004. Softening of wood polymers induced by moisture studied by dynamic FTIR spectroscopy. J Appl Polym Sci. 94:2032–2040. doi: 10.1002/app.21133
4.
AshadduzamanM, HaleMD, TverezovskiyV, OrmondroydGA.2013. Effect of bio-resin from cashew nut shell liquid (CNSL) on decay resistance properties of wood. IRG working paper, 44th Annual Meeting of the International Research Group on Wood Protection, Stockholm, Sweden, 16–20 June 2013. IRG/WP 13-40649, 15pp.
5.
BackEL, SalménL.1982. Glass transitions of wood components hold implications for molding and pulping processes. TAPPI. 65(7):107–110.
6.
BackmanAC, LindbergKAH.2001. Differences in wood material responses for radial and tangential direction as measured by dynamic mechanical thermal analysis. J Mat Sci. 36:3777–3783. doi: 10.1023/A:1017986119559
7.
BeckerH, NoackD.1968. Studies in dynamic torsional viscoelasticity of wood. Wood Sci Technol. 2:213–230.
8.
BirkinshawC, BuggyM, HennGG.1986. Dynamic mechanical analysis of wood. J Mater Sci Lett. 5:898–900. doi: 10.1007/BF01729266
9.
BjörkmanA, SalménL.2000. Studies on solid wood. II The influence of chemical modifications on viscoelastic properties. Cellul Chem Technol. 34:7–20.
10.
CarpitaNC, GibeautDM.1993. Structural models of primary cell walls in flowering plants: consistency of molecular structure with the physical properties of the walls during growth. Plant J. 3(1):1–30. doi: 10.1111/j.1365-313X.1993.tb00007.x
11.
CosgroveDJ, JarvisMC.2012. Comparative structure and biomechanics of plant primary and secondary cell walls. Front Plant Sci. 3:204. doi:10.3389/fpls.2012.00204.
12.
EbrahimzadehPR, KubatDG.1993. Effects of humidity changes on damping and stress relaxation in wood. J Mater Sci. 28:5668–5674. doi: 10.1007/BF00367845
13.
EbringerovaA, HeinzeT.2000. Xylan and xylan derivatives – biopolymers with valuable properties, I, naturally occurring xylans, structures, isolation procedures and properties. Macromol Rapid Commun. 21(9):542–546. doi: 10.1002/1521-3927(20000601)21:9<542::AID-MARC542>3.0.CO;2-7
14.
EngelundET, ThygesenLG, SvenssonS.2013. A critical discussion of the physics of wood-water interactions. Wood Sci Technol. 47:141–161. doi: 10.1007/s00226-012-0514-7
15.
EntwistleKM.2005. Mechanosorptive effect in Pinus radiata D. Don. Holzforschung. 59:552–558. doi: 10.1515/HF.2005.091
16.
FabiyiJS, FuwapeJA, OlufemiB.2011. Surface chemistry and thermos-mechanical analysis of some Nigerian wood species. Thermochim Acta. 524:80–87. doi: 10.1016/j.tca.2011.06.018
17.
GerhardsCC.1982. Effect of moisture content and temperature on the mechanical properties of wood: an analysis of immediate effects. Wood Fiber. 14(1):4–36.
18.
HadiYS, NurhayatiT, JasniYH, KamiyaN.2012. Resistance of smoked wood to subterranean and dry-wood termite attack. Int Biodeterior Biodegrad. 70:79–81. doi: 10.1016/j.ibiod.2011.06.010
19.
HavimoM.2009. A literature-based study on the loss tangent of wood in connection with mechanical properties. Wood Sci Technol. 43:627–642. doi: 10.1007/s00226-009-0271-4
20.
HeijboerJ.1977. Secondary loss peaks in glassy amorphous polymers. Int J Polym Mater. 6(1-20):11–37. doi: 10.1080/00914037708075218
21.
HoffmanG, PoliszkoS, HilczerT.1990. Model approach to dielectric – thermal analysis of wood modified with polymer. J Appl Polym Sci. 39(1):153–167. doi: 10.1002/app.1990.070390113
22.
HolzerSM, LoferskiJR, DillardDA.1989. A review of creep in wood: concepts relevant to develop long-term behaviour predictions for wood structures. Wood Fiber Sci. 21(4):376–392.
IslamMS, HamdanS, JusohI, RahmanMR, AhmedAS.2012a. The effect of alkali pretreatment on mechanical and morphological properties of tropical wood polymer composites. Mater Des. 33:419–424. doi: 10.1016/j.matdes.2011.04.044
25.
IslamMS, HamdanS, TalibZA, AhmedAS, RahmanMR.2012b. Tropical wood polymer nanocomposite (WPNC): the impact of nanoclay on dynamic mechanical thermal properties. Compos Sci Technol. 72:1995–2001. doi: 10.1016/j.compscitech.2012.09.003
26.
JiangJL, LuJX.2008. Dynamic viscoelasticity of wood after various drying processes. Drying Technol. 26:537–543. doi: 10.1080/07373930801944671
27.
KelleySS, RialsTG, GlasserWG.1987. Relaxation behaviour of the amorphous components of wood. J Mater Sci. 22(2):617–624. doi: 10.1007/BF01160778
28.
KimKY, KimNH, NishinariK.1991. Dielectric and viscoelastic properties of cellulose derivatives. Carbohydr Polym. 16:189–198. doi: 10.1016/0144-8617(91)90102-I
29.
KulasinskiK, SalménL, DeromeD, CarmelietJ.2016. Moisture adsorption of glucomannan and xylan hemicelluloses. Cellulose. 23:1629–1637. doi: 10.1007/s10570-016-0944-8
30.
LaineC.2005. Structures of hemicelluloses and pectins in wood and pulp [Doctoral thesis]. Helsinki University of Technology.
31.
LaversGM.1969. The strength properties of timbers. Forest Products Research Bulletin No 50, HMSO.
32.
LiZ, JiangJ, LuJ.2018. Moisture-dependent orthotropic viscoelastic properties of Chinese fir wood in low temperature environment. J Wood Sci. 64:515–525. doi: 10.1007/s10086-018-1738-4
33.
MaedaH, FukadaE.1987. Effect of bound water on piezoelectric, dielectric and elastic properties of wood. J Appl Polym Sci. 33:1187–1198. doi: 10.1002/app.1987.070330411
34.
MenardKP, MenardKK.2015. Dynamic mechanical analysis in the analysis of polymers and rubbers. In: Encyclopedia of polymer science and technology. Wiley. doi:10.1002/0471440264.pst102.pub2.
ObatayaE, NorimotoM, TomitaB.2001. Mechanical relaxation processes of wood in the low temperature range. J Appl Polym Sci. 81:3338–3347. doi: 10.1002/app.1790
38.
OlssonAM, SalménL.1992. Viscoelasticity of in situ lignin as affected by structure softwood vs hardwood. ACS Symp Series USA. 489:133–149. doi: 10.1021/bk-1992-0489.ch009
39.
PettersenRC.1984. The chemical composition of wood. In: RowellR., editor. Chemistry of solid wood. ACS Advances in Chemistry Series 207; p. 57–126.
40.
PlacetV, PassardJ, PerréP.2007. Viscoelastic properties of green wood across the grain measured by harmonic tests in the range 0–95°C: hardwood vs. softwood and normal wood vs. reaction wood. Holzforschung. 61:548–557. doi: 10.1515/HF.2007.093
41.
RoigF, DantrasE, DandurandJ, LacabanneC.2001. Influence of hydrogen bonds on glass transition and dielectric relaxations of cellulose. J Phys D – Appl Phys. 44(4):045403. doi: 10.1088/0022-3727/44/4/045403
42.
RoigF, RamanatsizehenaG, RazafindramisaFL, DantrasE, DandurandJ, HoyetH, BernesA, LacabaneC.2017. Dielectric and mechanical properties of various species of Madagascan woods. Wood Sci Technol. 51:1389–1404. doi: 10.1007/s00226-017-0936-3
43.
SalménL.1984. Viscoelastic properties of in situ lignin under water saturated conditions. J Mater Sci. 19:3090–3096. doi: 10.1007/BF01026988
44.
SalménL, BurgertI.2009. Cell wall features with regard to mechanical performance. A review. Holzforschung. 63:121–129. doi: 10.1515/HF.2009.011
45.
Se GolpayeganiA, BrémaudI, GrilJ, ThevenonM-F, ArnouldO, PourtahmasiK.2011. Effect of extractions on dynamic mechanical properties of white mulberry (Morus alba). J Wood Sci. 58:153–162. doi: 10.1007/s10086-011-1225-7
ShinoudaHG, MotelebMMA.2005. Dielectric spectroscopy and relaxation phenomena of moistened and dry polysaccharides. J Appl Polym Sci. 98:571–582. doi: 10.1002/app.22021
48.
SimmonsTJ, MortimerJC, BernardinelliOD, PöpplerA-C, BrownSP, deAzevedoER, DupreeR, DupreeP.2016. Folding of xylan onto cellulose fibrils in plant cell walls revealed by solid-state NMR. Nat Commun. 7:13902. doi:10.1038/ncomms13902.
49.
SjöströmE.1981. Wood chemistry: fundamentals and applications. New York: Academic Press.
50.
StartsevOV, MakhonkovA, ErofeevV, GudojnikovS.2017. Impact of moisture content on dynamic mechanical properties and transition temperatures of wood. Wood Mat Sci Eng. 12(1):55–62. doi: 10.1080/17480272.2015.1020566
51.
StartsevOV, SalinBN, SkuridinYG, UtemesovRM, NasonovAD.1999. Physical properties and molecular mobility of new wood composite plastic. Wood Sci Technol33:73–83. doi: 10.1007/s002260050100
52.
SugiyamaM, NorimotoM.1996. Temperature dependence of dynamic viscoelasticities of chemically treated woods. Mokuzai Gakkaishi. 42(11):1049–1056.
53.
SugiyamaM, ObatayaE, NorimotoM.1998. Viscoelastic properties of the matrix substance of chemically treated wood. J Mater Sci. 33:3505–3510. doi: 10.1023/A:1004678506822
54.
SunN, DasS, FrazierCE.2007. Dynamic mechanical analysis of dry wood: linear viscoelastic response region and effects of minor moisture changes. Holzforschung. 61(1):28–33. doi: 10.1515/HF.2007.006
55.
Turi. 1997. TA Thermal Solutions Sheet 62.
56.
WertCA, WellerM, CaulfieldD.1984. Dynamic loss properties of wood. J Appl Phys. 56:2453–2458. doi: 10.1063/1.334306
57.
ZhanT, JiangJ, LuJ, PengH.2015. Dynamic viscoelastic properties o f Chinese fir under cyclical relative humidity variation. J Wood Sci. 61:465–473. doi: 10.1007/s10086-015-1491-x
58.
ZhaoH, ChenZ, DuX, ChenL.2019. Contribution of different state of absorbed water to the sub-Tg dynamics of cellulose. Carbohydr Polym. 210:322–331. doi: 10.1016/j.carbpol.2019.01.087