Wood is sensitive to photochemical degradation. The development of a wood surface protected against sun radiation remains a major challenge. Specimens from different species have been exposed to the outdoor environment and analysed at different depths and time steps by Fourier transform infrared spectroscopy. After 2 months of weathering, the peak representing the C=C aromatic bond disappeared on the surface. The radiation penetration depth in the latewood of softwoods is less than that in earlywood. The degradation of beech and oak is more gradual with depth and comparable to spruce and larch earlywood. The destruction of the anatomical structure begins with pits cracking. Then, the cracks proceed into the S2 layer, the middle lamella is degraded, leading to cells delamination and reduction of the surface mechanical strength. Treatment of the specimens with pressurised water vapour creates a cellulose layer on the surface, more obvious for hardwood than for softwood.
DawsonB. S., SinghA. P., KroeseH. W., SchwitzerM. A., GallagherS., RiddioughS. J. and WuS.2008a. Enhancing exterior performance of clear coatings through photostabilization of wood. Part 1: Treatment and characterization. Journal of Coatings Technology and Research. 5(2): 193–206. doi: 10.1007/s11998-008-9089-5
2.
DawsonB. S., SinghA. P., KroeseH. W., SchwitzerM. A., GallagherS., RiddioughS. J. and WuS.2008b. Enhancing exterior performance of clear coatings through photostabilization of wood. Part 2: coating and weathering performance. Journal of Coatings Technology and Research. 5(2): 207–219. doi: 10.1007/s11998-008-9090-z
3.
DerbyshireH. and MillerE. R.1981. The photodegradation of wood during solar irradiation Part I: effects on the structural integrity of thin wood strips. Holz als Roh- und Werkstoff. 39: 341–350. doi: 10.1007/BF02608404
4.
DerbyshireH., MillerE. R. and TurkulinH.1995. Investigations into the photodegradation of wood using microtensile testing. Part 1: the application of microtensile testing to measurement of photodegradation rates. Holz als Roh- und Werkstoff. 53: 339–345. doi: 10.1007/s001070050103
5.
DerbyshireH., MillerE. R. and TurkulinH.1997. Investigations into the photodegradation of wood using microtensile testing. Part 3: the influence of temperature on photodegradation rates. Holz als Roh- und Werkstoff. 55(5): 287–291. doi: 10.1007/s001070050229
6.
EvansP. D.1989. Structural changes in Pinus radiata during weathering. Journal of the Institute of Wood Science. 11(5): 172–181.
7.
EvansP. D., MichellA. J. and SchmalzlK. J.1992. Studies of the degradation and protection of wood surfaces. Wood Science and Technology. 26: 151–163. doi: 10.1007/BF00194471
8.
EvansP. D., ThayP. D. and SchmalzlK. J.1996. Degradation of wood surfaces during natural weathering. Effects on lignin and cellulose and on the adhesion of acrylic latex primers. Wood Science and Technology. 30: 411–422. doi: 10.1007/BF00244437
9.
EvansP. D., WallisA. F. A. and OwenN. L.2000. Weathering of chemically modified wood surfaces – natural weathering of Scots pine acetylated to different weight gains. Wood Science and Technology. 34(2): 151–165. doi: 10.1007/s002260000039
10.
FeistW. C. and HonD. N. S.1984. Chemistry of weathering and protection. In: American Chemical Society (ed.). Chemistry of Solid Wood, 401–451. Washington, DC: American Chemical Society.
11.
FengelD. and WegenerG.1984. Wood: Chemistry, Ultrastructure, Reactions. Berlin, New York: De Gruyter.
12.
FutoL. P.1976. Effects of temperature on the photochemical degradation of wood. I. Experimental presentation. Holz als Roh- und Werkstoff. 34(1): 31–36. doi: 10.1007/BF02610758
13.
Ganne-ChédevilleC., VolkmerT., LetschB. and LehmannM.2012. Measure for the maintenance of untreated wood facades. World Conference on Timber Engineering, Auckland, Poster presentation.
14.
GeorgeB., SuttieE., MerlinA. and DegliseX.2005. Photodegradation and photostabilisation of wood – the state of the art. Polymer Degradation and Stability. 88: 268–274. doi: 10.1016/j.polymdegradstab.2004.10.018
15.
Hazneza, S. and Evans, P. D.2016. End-grain erosion of Douglas fir wood during natural weathering. International Wood Products Journal. 7(1): 3–11.
16.
HillC. A. S., CetinN. S., QuinneyR. F., DerbyshireH. and EwenR. J.2001. An investigation of the potential for chemical modification and subsequent polymeric grafting as a means of protecting wood against photodegradation. Polymer Degradation and Stability. 72: 133–139. doi: 10.1016/S0141-3910(01)00007-6
17.
HonD.1991. Photochemistry of wood. In: HonD. and ShiraishiN. (eds.). Wood and Cellulosic Chemistry. New York: Marcel Decker, 525–556.
18.
HonD. N. S. and FeistW. C.1986. Weathering characteristics of hardwood surfaces. Wood Science and Technology. 20: 169–183.
19.
HonD. N. S. and GlasserW. G.1979. The effect of mechanical action on wood and fiber components. Tappi Journal. 62: 107–110.
20.
KalninsM. A.1966. Surface characteristics of wood as they affect durability of finishes. Part II. Photochemical degradation of wood. U.S. Forest Service Research Paper. FPL57, 23–57.
21.
KataokaY. and KiguchiM.2001. Depth profiling of photo-induced degradation in wood by FTIR microspectroscopy. Journal of Wood Science. 47: 325–327. doi: 10.1007/BF00766722
22.
KataokaY., KiguchiM., WilliamsR. S. and EvansP. D.2007. Violet light causes photodegradation of wood beyond the zone affected by ultraviolet light. Holzforschung. 61(1): 23–27. doi: 10.1515/HF.2007.005
23.
KuoM. L., McClellandJ. F., LuoS., ChienP.-L., WalkerR. D. and HseC.-Y.1988. Applications of infra-red photo-acoustic spectroscopy for wood samples. Wood and Fiber Science.20(1): 132–145.
24.
LearyG. J.1967. The yellowing of wood by light. Tappi. 50(1): 17–19.
25.
LearyG. J.1968. The yellowing of wood by light: Part II. Tappi. 51(6): 257–260.
26.
LearyG. J.1994. Recent progress in understanding and inhibiting the light-induced yellowing of mechanical pulps. Journal of Pulp and Paper Science. 20(6): 154–160.
27.
MüllerU., RätzschM. and SchwanningerM.2003. Yellowing and IR-changes of spruce wood as result of UV-irradiation. Journal of Photochemistry and Photobiology B: Biology. 69: 97–105. doi: 10.1016/S1011-1344(02)00412-8
28.
PaajanenL. M.1994. Structural changes in primed Scots pine and Norway spruce during weathering. Materials and Structures. 27: 237–244. doi: 10.1007/BF02473038
29.
PandeyK. K.2005. Study of the effect of photo-irradiation on the surface chemistry of wood. Polymer Degradation and Stability. 90: 9–20. doi: 10.1016/j.polymdegradstab.2005.02.009
30.
RaczkowskiJ.1980. Seasonal effects on the atmospheric corrosion of spruce micro-sections. Holz als Roh- und Werkstoff. 38(6): 231–234. doi: 10.1007/BF02607398
31.
SinghA. P. and DawsonB. S. W.2003. The mechanism of failure of clear coated wooden boards as revealed by microscopy. IAWA Journal. 24: 1–11. doi: 10.1163/22941932-90000316
32.
TurkulinH., ArnoldM., DerbyshireH. and SellJ.2001. Structural and fractographic SEM analysis of exterior coated wood. Surface Coatings International Part B: Coatings Transactions. 84: 67–75. doi: 10.1007/BF02699699
33.
TurkulinH., DerbyshireH. and MillerE. R.2004. Investigations into the photodegradation of wood using microtensile testing. Part 5: The influence of moisture on photodegradation rates. Holz als Roh- und Werkstoff. 62: 307–312. doi: 10.1007/s00107-004-0493-y
34.
WilliamsR. S.2005. Weathering of wood. In: RowellR. M. (ed.). Handbook of Wood Chemistry and Wood Composites. Boca-Raton: CRC Press, 139–187.
35.
WilliamsR. S., KnaebeM. T. and FeistW. C.2001. Erosion rates of wood during natural weathering. Part II. Earlywood and latewood erosion rates. Wood and Fiber Science. 33: 43–49.
36.
ZivkovicV., ArnoldM., PandeyK. K., RichterK. and TurkulinH.2013. Novel approach in analysis of light source effects to spectral sensitivity of Fir wood surfaces. Proceedings of the 6th European Weathering Symposium Natural and Artificial Ageing of Polymers, Bratislava, Slovak Republic.
37.
ZivkovicV., ArnoldM., RadmanovicK., RichterK. and TurkulinH.2014. Spectral sensitivity in the photodegradation of fir wood (Abies alba Mill.) surfaces: colour changes in natural weathering. Wood Science and Technology. 48: 239–252. doi: 10.1007/s00226-013-0601-4