This study presents a novel approach for surface repairs of high-strength, cold-worked aluminium (Al) alloys, without negatively affecting the base material strength. Low-pressure cold spraying was used to fabricate Al–Al2O3 metal matrix composite overlays, with varying concentrations of Al2O3 deposited on an Al alloy. Friction stir processing (FSP) was employed to disperse and consolidate the overlay coating on the base material. The FSP was found to improve the Al2O3 particle distribution in the coating and reduce the mean free path between Al2O3 particles. The coating hardness increased after FSP. The post-FSPed overlays also exhibited lower wear rates compared to the as-sprayed condition. Remarkable improvement was observed in the tensile properties of the coatings, which were attributed to the improved dispersion of Al2O3 particles in the matrix, while the enhanced ductility was attributed to the possible grain refinement that occurred due to the recrystallisation of Al during FSP.
MishraRS, MaZY, CharitI.Friction stir processing: a novel technique for fabrication of surface composite. Mater Sci Eng A. 2003;341(1–2):307–310. doi:10.1016/S0921-5093(02)00199-5.
2.
YangK, LiW, NiuP, . Cold sprayed AA2024/Al2O3 metal matrix composites improved by friction stir processing: microstructure characterization, mechanical performance and strengthening mechanisms. J Alloys Compd; 2018(736):115–123.
3.
NoltingAE, LaroseS, CaoX, . Localized strength restoration of aluminum 5083 with ceramic particles via friction stir processing. Proceedings of the NATO-STO AVT-267 work. future addit. manuf. mil. hardw.; 2018; p. 1–18.
4.
LiuFC, MaZY.Achieving exceptionally high superplasticity at high strain rates in a micrograined Al-Mg-Sc alloy produced by friction stir processing. Scr Mater. 2008;59:882–885. doi:10.1016/j.scriptamat.2008.06.035
5.
ChampagneV, HelfritchD.Critical assessment 11: structural repairs by cold spray. Mater Sci Technol. 2015;31(6):627–634. doi:10.1179/1743284714Y.0000000723
6.
SunW, ChuX, LanH, . Current implementation status of cold spray technology: a short review. J Therm Spray Tech. 2022;31(4):848–865. doi:10.1007/s11666-022-01382-4
7.
LeeYTR, AshrafizadehH, FisherG, . Effect of type of reinforcing particles on the deposition efficiency and wear resistance of low-pressure cold-sprayed metal matrix composite coatings. Surf Coat Technol. 2017;324:190–200. doi:10.1016/j.surfcoat.2017.05.057
8.
MundayG, HoganJ, McDonaldA.On the microstructure-dependency of mechanical properties and failure of low-pressure cold-sprayed tungsten carbide-nickel metal matrix composite coatings. Surf Coat Technol. 2020;396:125947. doi:10.1016/j.surfcoat.2020.125947
9.
HodderKJ, IzadiH, McDonaldAG, . Fabrication of aluminum-alumina metal matrix composites via cold gas dynamic spraying at low pressure followed by friction stir processing. Mater Sci Eng A. 2012;556:114–121. doi:10.1016/j.msea.2012.06.066
10.
PeatT, GallowayA, ToumpisA, . The erosion performance of cold spray deposited metal matrix composite coatings with subsequent friction stir processing. Appl Surf Sci. 2017;396:1635–1648. doi:10.1016/j.apsusc.2016.10.156
11.
CharitI, MishraRS.High strain rate superplasticity in a commercial 2024 Al alloy via friction stir processing. Mater Sci Eng A. 2003;359:290–296. doi:10.1016/S0921-5093(03)00367-8
12.
RaoD, HuberK, HeerensJ, . Asymmetric mechanical properties and tensile behaviour prediction of aluminium alloy 5083 friction stir welding joints. Mater Sci Eng A. 2013;565:44–50. doi:10.1016/j.msea.2012.12.014
13.
PeatT, GallowayA, ToumpisA, . Enhanced erosion performance of cold spray co-deposited AISI316 MMCs modified by friction stir processing. Mater Des. 2017;120:22–35. doi:10.1016/j.matdes.2017.01.099
14.
HuangC, LiW, ZhangZ, . Modification of a cold sprayed SiCp/Al5056 composite coating by friction stir processing. Surf Coat Technol. 2016;296:69–75. doi:10.1016/j.surfcoat.2016.04.016
15.
LiW, FengY, PlancheMP, . Microstructural evolution and mechanical properties enhancement of a cold-sprayed Cu[sbnd]Zn alloy coating with friction stir processing. Mater Charact. 2017;125:76–82. doi:10.1016/j.matchar.2017.01.027
16.
TravitzkyN.Processing of ceramic–metal composites. Adv Appl Ceram. 2012;111(5-6):286–300. doi:10.1179/1743676111Y.0000000073
KocksUF, MeckingH.Physics and phenomenology of strain hardening: the FCC case U.F. Prog Mater Sci. 2002;48:171–273. doi:10.1016/S0079-6425(02)00003-8
19.
ASTM International. G65-16: standard test method for measuring abrasion using the dry sand / rubber wheel. ASTM Stand. 2013;04(Reapproved 2010):1–12. doi:10.1520/G0065-04R10.2
20.
ASTM International. ASTM b611 standard test method for determining the high stress abrasion resistance of hard. ASTM B611. 2017;13(Reapproved 2018):1–6. doi:10.1520/B0611-13.2
21.
ASTM E8. ASTM e8/E8M standard test methods for tension testing of metallic materials 1. Annu B ASTM Stand.2010;4(C):1–27. doi:10.1520/E0008
SpencerK, FabijanicDM, ZhangMX.The use of Al-Al2O3 cold spray coatings to improve the surface properties of magnesium alloys. Surf Coat Technol. 2009;204:336–344. doi:10.1016/j.surfcoat.2009.07.032
24.
XieX, ChenC, ChenZ, . Achieving simultaneously improved tensile strength and ductility of a nano-TiB2/AlSi10Mg composite produced by cold spray additive manufacturing. Compos B Eng. 2020;202:108404-1–108404-11. doi:10.1016/j.compositesb.2020.108404.