The joining of SiC ceramic using the liquid polyvinylphenylsiloxane at the high temperature was investigated. The characteristic evolution of polyvinylphenylsiloxane during heating process, shear strength and microstructure of joint were especially discussed. The results show that active groups Si-OH and CH=CH2 of polyvinylphenylsiloxane through cross-linking at low temperature (200°C) form the macromolecular structure, crosslinked polyvinylphenylsiloxane possess the higher ceramic yield and structure stability at high temperature. Shear strength of SiC joints increase with the joining temperature from 1000 to 1200°C, and then decrease when the joining temperature reaches to 1350°C. Combination with microstructure of fine grains of SiO2 and SiC dispersion in the Si–O–C ceramic of the join layer and new phase SiC formation on the joint interface through the gas–solid reactions, the shear strength of joint achieves the maximum at 1200°C. The defects of joint increase with temperature higher than 1200°C, and the shear strength of joint begin to decrease.
WangH, ZhouX, YuJ, Fabrication of SiCf/SiC composites by chemical vapor infiltration and vapor silicon infiltration. Mater Lett. 2010;64:1691–1693. doi: 10.1016/j.matlet.2010.05.013
2.
ColomboP, SglavoV, PippelE, Joining of reaction-bonded silicon carbide using a preceramic polymer. J Mater Sci. 1998;33:2405–2412. doi: 10.1023/A:1004312109836
3.
LewinsohnC, SinghM, ShibayamaT, Joining of silicon carbide composites for fusion energy applications. J Nucl Mater. 2000;283–287:1258–1261. doi: 10.1016/S0022-3115(00)00247-6
4.
ZhaoS, ZhouX, YuH, Compatibility of PIP SiCf/SiC with LiPb at 700°C. Fusion Eng Des. 2010;85:1624–1626. doi: 10.1016/j.fusengdes.2010.04.060
5.
WangZ, HuangJ, ZhangH, Reactive composite brazing of Cf/SiC composites to Ti alloy with (Ag-6Al)+Ti + C composite filler materials. Mater Sci Technol. 2011;27:49–52. doi: 10.1179/174328409X418955
6.
LinG, HuangJ, ZhangH, Microstructure and mechanical performance of brazed joints of Cf/SiC composite and Ti alloy using Ag–Cu–Ti–W. Sci Technol Weld Join. 2006;11:379–383. doi: 10.1179/174329306X113235
7.
RiccardiB, NannettiC, PetrisorT, Issues of low activation brazing of SiCf/SiC composites by using alloys without free silicon. J Nucl Mater. 2004;329–333:562–566. doi: 10.1016/j.jnucmat.2004.04.118
8.
HalbigM, SinghM, ShpargelT, Diffusion bonding of silicon carbide ceramics using titanium interlayers. Ceram Eng Sci Proc. 2006;27:133–143. doi: 10.1002/9780470291313.ch13
9.
JungY-I, KimSH, KimHG, Microstructures of diffusion bonded SiC ceramics using Ti and Mo interlayers. J Nucl Mater. 2013;441:510–513. doi: 10.1016/j.jnucmat.2013.07.008
10.
KhachatryanG, ArutyunyanA, KharatyanS.Activated combustion of a silicon–carbon mixture in nitrogen and SHS of Si3N4-SiC composite ceramic powders and silicon carbide. Combust Explos Shock Waves. 2006;42:543–548. doi: 10.1007/s10573-006-0086-7
11.
MasantaM, GaneshP, KaulR, Microstructure and mechanical properties of TiB2-TiC-Al2O3-SiC composite coatings developed by combined SHS, sol-gel and laser technology. Surf Coat Technol. 2010;204:3471–3480. doi: 10.1016/j.surfcoat.2010.04.018
12.
XuHB, ZhouBF, LuoQX, The microstructure and properties of joint interface of semisolid stirring brazing of composites. J Mater Sci Technol. 2012;28:1163–1168. doi: 10.1016/S1005-0302(12)60187-X
13.
ChenXG, XieRS, LaiZW, Interfacial structure and formation mechanism of ultrasonic-assisted brazed joint of SiC ceramics with Al-12Si filler metals in air. J Mater Sci Technol. 2017;33:492–498. doi: 10.1016/j.jmst.2016.03.016
14.
YajimaS, HayashiJ, OmoriM, Development of a silicon carbide fibre with high tensile strength. Nature. 1976;261:683–685. doi: 10.1038/261683a0
15.
KatohY, SneadLL, ChengT, Radiation-tolerant joining technologies for silicon carbide ceramics and composites. J Nucl Mater. 2014;448(1):497–511. doi: 10.1016/j.jnucmat.2013.10.002
16.
LiaoNB, XueW, ZhouHM, Molecular dynamics investigation of structure and high-temperature mechanical properties of SiBCO ceramics. J Alloy Compd. 2014;610:45–49. doi: 10.1016/j.jallcom.2014.04.189
17.
GreilP.Active-filler-controlled pyrolysis of preceramic polymers. J Am Ceram Soc. 1995;78(4):835–848. doi: 10.1111/j.1151-2916.1995.tb08404.x
18.
WangXZ, WangJ, WangH.Synthesis of a novel preceramic polymer (V-PMS) and its performance in heat-resistant organic adhesives for joining SiC ceramic. J Eur Ceram Soc. 2012;32:3415–3422. doi: 10.1016/j.jeurceramsoc.2012.03.032
19.
FangY, HuangM, YuZ, Synthesis, characterization, and pyrolytic conversion of a novel liquid polycarbosilane. J Am Ceram Soc. 2008;91:3298–3302. doi: 10.1111/j.1551-2916.2008.02603.x
20.
LiuHL, LiSJ, ChenZJ.Joining of reaction-bonded silicon carbide using a polysiloxane. Rare Metal Mater Eng. 2006;35(1):134–135.
21.
XiongHP, ChenB, KangYS, Wettability of Co-V, and PdNi-Cr-V system alloys on SiC ceramic and interfacial reactions. Scr Mater. 2007;56:173–176. doi: 10.1016/j.scriptamat.2006.08.067
22.
WeiQ, PippelE, WoltersdorfJ, Interfacial SiC formation in polysiloxane-derived Si-O-C ceramics. Mater Chem Phys. 2002;73:281–289. doi: 10.1016/S0254-0584(01)00395-9
23.
WangC, WangJ, ParkCB, Cross-linking behavior of a polysiloxane in preceramic foam processing. J Mater Sci. 2004;39:4913–4915. doi: 10.1023/B:JMSC.0000035335.92101.7c
24.
RenlundGM, ProchazkaS, DoremusRH.Silicon oxycarbide glasses: part II. Structures and properties. J Mater Res. 1991;6(12):2723–2734. doi: 10.1557/JMR.1991.2723
25.
LefebvreJ, MamleevV, Le BrasM, Kinetic analysis of pyrolysis of cross-linked polymers. Polym Degrad Stabil. 2005;88:85–91. doi: 10.1016/j.polymdegradstab.2004.02.020