Transparent Polycrystalline Alumina (PCA) optical ceramics were fabricated at a high heating rate and low temperature by spark plasma sintering (SPS). Maximum pressure (100 MPa) at dwell time keeps the grain size small irrespective of the dwell time. A heating and cooling rate of 100°C min−1 at the sintering temperature of 1150°C for a dwell time of 1 h at 100 MPa yielded highly densified samples with the good transparency of 63 and 83% in visible and infra-red region, respectively. Optoceramics yielded a mechanical hardness of (3000 Hv)/ 29.42 GPa and a thermal conductivity of 21 Wm−1 K−1.
ApetzR. and BruggenM. P. B.: ‘Transparent alumina: a light-scattering model’, J. Am. Ceram. Soc., 2003, 86, (3), 480–486. doi: 10.1111/j.1151-2916.2003.tb03325.x
2.
GrassoS., KimB.-N., HuC., MaizzaG. and SakkaY.: ‘Highly transparent pure alumina fabricated by high-pressure spark plasma sintering’, J. Am. Ceram. Soc., 2010, 93, (9), 2460–2462. doi: 10.1111/j.1551-2916.2010.03811.x
3.
LiuW., XieZ. and ChengL.: ‘Sintering kinetics window: an approach to the densification process during the preparation of transparent alumina’, Adv. Appl. Ceram., 2015, 114, (1), 33–38. doi: 10.1179/1743676114Y.0000000186
4.
NankoM. and DangK. Q.: ‘Two-step pulsed electric current sintering of transparent Al2O3 ceramics’, Adv. Appl. Ceram., 2014, 113, (2), 80–84. doi: 10.1179/1743676113Y.0000000109
5.
LiuW., BoT. Z., XieZ. P., WuY., and YangX. F.: ‘Fabrication of injection moulded translucent alumina ceramics via pressureless sintering’, Adv. Appl. Ceram., 2011, 110, (4), 251–254. doi: 10.1179/1743676111Y.0000000005
6.
ChaimR., LevinM., ShlayerA. and EstournesC.: ‘Sintering and densification of nanocrystalline ceramic oxide powders: a review’, Adv. Appl. Ceram., 2008, 107, (3), 159–169. doi: 10.1179/174367508X297812
7.
KrellA., BlankP., MaH., HutzlerT., BruggenM. P. B. and ApetzR.: ‘Transparent sintered corundum with high hardness and strength’, J. Am. Ceram. Soc., 2003, 86, (1), 12–18. doi: 10.1111/j.1151-2916.2003.tb03270.x
8.
MurotaniH., MitudaT., WakakiM. and KondouY.: ‘Optical characteristics of Al 2 O 3 ceramics doped with cr at high concentrations prepared by extrusion molding process’, Jpn. J. Appl. Phys., 2000, 39, (Part 1, No. 5A), 2748–2749. doi: 10.1143/JJAP.39.2748
9.
MurotaniH., WakakiM., KawabataS. and NakamotoK.: ‘Fabrication of microlens using CO2 laser and characterization of formation process’, Proc. SPIE 5525, Laser Beam Shaping V, 226 (September 29, 2004); available at: http://dx.doi.org/10.1117/12.560369; DOI:10.1117/12.560369.
10.
RisbudS. H., ShanC.-H., MukherjeeA. K., KimM. J., BowJ. S. and HollR. A.: ‘Retention of nanostructure in aluminum oxide by very rapid sintering at 1150 °C’, J. Mater. Res., 1995, 10, (2), 237–239. doi: 10.1557/JMR.1995.0237
11.
ShenZ., JohnssonM., ZhaoZ. and NygrenM.: ‘Spark plasma sintering of alumina’, J. Am. Ceram. Soc., 2002, 85, (8), 1921–1927. doi: 10.1111/j.1151-2916.2002.tb00381.x
12.
YiH., MaoX., ZhouG., ChenS., ZouX., WangS. and ShimaiS.: ‘Crystal plane evolution of grain oriented alumina ceramics with high transparency’, Ceram. Int., 2012, 38, (7), 5557–5561. doi: 10.1016/j.ceramint.2012.03.074
13.
GaoL., HongJ. S., MiyamotoH. and TorreS. D. D. L.: ‘Bending strength and microstructure of Al2O3 ceramics densified by spark plasma sintering’, J. Eur. Ceram. Soc., 2000, 20, (12), 2149–2152. doi: 10.1016/S0955-2219(00)00086-8
14.
ZhangH., KimB.-N., MoritaK., Keijiro HiragaH. Y. and SakkaY.: ‘Effect of sintering temperature on optical properties and microstructure of translucent zirconia prepared by high-pressure spark plasma sintering’, Sci. Technol. Adv. Mat., 2011, 12, (5), 055003–055009. doi: 10.1088/1468-6996/12/5/055003
15.
ZhangH., KimB.-N., MoritaK., YoshidaH., HiragaK. and SakkaY.: ‘Fabrication of transparent yttria by high-pressure spark plasma sintering’, J. Am. Ceram. Soc., 2011, 94, (10), 3206–3210. doi: 10.1111/j.1551-2916.2011.04789.x
16.
SchwarzS. and GuillonO.: ‘Two step sintering of cubic YSZ using field assisted sintering technique/ spark plasma sintering’, J. Eur. Ceram. Soc., 2013, 33, (4), 637–641. doi: 10.1016/j.jeurceramsoc.2012.10.002
17.
KimB.-N., HiragaK., MoritaK. and YoshidaH.: ‘Spark plasma sintering of transparent alumina’, Scripta Mater., 2007, 57, (7), 607–610. doi: 10.1016/j.scriptamat.2007.06.009
18.
MishraR. S. and MukherjeeA. K.: ‘‘Electric pulse assisted rapid consolidation of ultrafine grained alumina matrix composites’, Mater. Sci. Eng.: A, 2000, 287, (2), 178–182. doi: 10.1016/S0921-5093(00)00772-3
19.
MishraR. S., RisbudS. H. and MukherjeeA. K.: ‘Influence of initial crystal structure and electrical pulsing on densification of nanocrystalline alumina powder’, J. Mater. Res., 1998, 13, (1), 86–89. doi: 10.1557/JMR.1998.0013
20.
OhS.-T., TajimaK.-i., AndoM. and OhjiT.: ‘Strengthening of porous alumina by pulse electric current sintering and nanocomposite processing’, J. Am. Ceram. Soc., 2000, 83, (5), 1314–1316. doi: 10.1111/j.1151-2916.2000.tb01380.x
21.
PalmeroP., LocciA. M., TullianiJ. M., OrrùR., CaoG. and MontanaroL.: ‘Conventional and SPS Sintering of a nanocrystalline alumina: a comparative study’, Adv. Sci. Technol., 2006, 45, 957–962. doi: 10.4028/www.scientific.net/AST.45.957
22.
RousselN., LallemantL., Chane-ChingJ. Y., Guillemet-FristchS., DurandB., GarnierV., BonnefontG., FantozziG., BonneauL., TrombertS. and Garcia-GutierrezD.: ‘Highly dense, transparent α-Al 2 O 3 ceramics from ultrafine nanoparticles via a standard sps sintering’, J. Am. Ceram. Soc., 2013, 96, (4), 1039–1042. doi: 10.1111/jace.12255
23.
StuerM., ZhaoZ., AschauerU. and BowenP.: ‘Transparent polycrystalline alumina using spark plasma sintering: effect of Mg, Y and La doping’, J. Eur. Ceram. Soc., 2010, 30, (6), 1335–1343. doi: 10.1016/j.jeurceramsoc.2009.12.001
24.
WangS. W., ChenL. D., HiraiT. and KangY. S.: ‘Microstructure inhomogeneity in Al2O3 sintered bodies formed during the plasma-activated sintering process’, J. Mater. Sci. Lett., 1999, 18, (14), 1119–1121. doi: 10.1023/A:1006684631127
25.
ZhaoZ., BuscagliaV., BowenP. and NygrenM.: ‘Spark plasma sintering of nano-crystalline ceramics’, KEM, 2004, 264–268, 2297–2300. doi: 10.4028/www.scientific.net/KEM.264-268.2297
26.
FangJ., ThompsonA. M., HarmerM. P. and ChanH. M.: ‘Effect of yttrium and lanthanum on the final-stage sintering behavior of ultrahigh-purity alumina’, J. Am. Ceram. Soc., 1997, 80, (8), 2005–2012. doi: 10.1111/j.1151-2916.1997.tb03084.x
27.
JiangD., HulbertD. M., Anselmi-TamburiniU., NgT., LandD. and MukherjeeA. K.: ‘Optically transparent polycrystalline Al2O3 produced by spark plasma sintering’, J. Am. Ceram. Soc., 2007, 91, (1), 151–154. doi: 10.1111/j.1551-2916.2007.02086.x
28.
KimB.-N., HiragaK., GrassoS., MoritaK., YoshidaH., ZhangH. and SakkaY.: ‘High-pressure spark plasma sintering of MgO-doped transparent alumina’, J. Ceram. Soc. Jpn., 2012, 120, (1399), 116–118. doi: 10.2109/jcersj2.120.116
29.
ZhouY., HiraoK., YamauchiY. and KanzakiS.: ‘Densification and grain growth in pulse electric current sintering of alumina’, J. Eur. Ceram. Soc., 2004, 24, (12), 3465–3470. doi: 10.1016/j.jeurceramsoc.2003.10.013
30.
AmanY., GarnierV. and DjuradoE.: ‘Spark plasma sintering kinetics of pure α-Alumina’, J. Am. Ceram. Soc., 2011, 94, (9), 2825–2833. doi: 10.1111/j.1551-2916.2011.04424.x
31.
VeshchunovM. S.: ‘Modelling of grain growth kinetics in porous ceramic materials under normal and irradiation conditions’, Mater, 2009, 2, 1252–1287. doi: 10.3390/ma2031252
32.
WeiG. C., JeonS. J., SungC. and RhodesW. H.: ‘Characterization of second phases in translucent alumina by analytical TEM’ in ‘Ceramic microstructure control at the atomic level’, (ed. A. P. Tomsia and A. M. Glaeser), 311–322; 1998, New York, Plenum Press, ISBN 978-1-4613-7462-6.
KimB.-N., MoritaK., LimJ.-H., HiragaK. and YoshidaH.: ‘Effects of preheating of powder before spark plasma sintering of transparent MgAl2O4 spinel’, J. Am. Ceram. Soc., 2010, 93, (8), 2158–2160. doi: 10.1111/j.1551-2916.2010.03699.x
36.
LallemantL., FantozziG., GarnierV. and BonnefontG.: ‘Transparent polycrystalline alumina obtained by SPS: green bodies processing effect’, J. Eur. Ceram. Soc., 2012, 32, (11), 2909–2915. doi: 10.1016/j.jeurceramsoc.2012.02.041
37.
LangerJ., HoffmannM. J. and GuillonO.: ‘Direct comparison between hot pressing and electric field-assisted sintering of submicron alumina’, Acta Mater., 2009, 57, (18), 5454–5465. doi: 10.1016/j.actamat.2009.07.043
38.
Mata-OsoroG., MoyaJ. S. and PecharromanC.: ‘Transparent alumina by vacuum sintering’, J. Eur. Ceram. Soc., 2012, 32, (11), 2925–2933. doi: 10.1016/j.jeurceramsoc.2012.02.039
39.
SantanachJ. G., WeibelA., EstournèsC., YangQ., LaurentC. and PeigneyA.: ‘Spark plasma sintering of alumina: study of parameters, formal sintering analysis and hypotheses on the mechanism(s) involved in densification and grain growth’, Acta Mater., 2011, 59, (4), 1400–1408. doi: 10.1016/j.actamat.2010.11.002
Anselmi-TamburiniU., GarayJ. E. and MunirZ. A.: ‘Fast low-temperature consolidation of bulk nanometric ceramic materials’, Scripta Mater., 2006, 54, (5), 823–828. doi: 10.1016/j.scriptamat.2005.11.015
42.
ChakravartyD., BysakhS., MuraleedharanK., RaoT. N. and SundaresanR.: ‘Spark plasma sintering of magnesia-doped alumina with high hardness and fracture toughness’, J. Am. Ceram. Soc., 2007, 91, (1), 203–208. doi: 10.1111/j.1551-2916.2007.02094.x
43.
PoulierC., SmithD. S. and AbsiJ.: ‘Thermal conductivity of pressed powder compacts: tin oxide and alumina’, J. Eur. Ceram. Soc., 2007, 27, (2–3), 475–478. doi: 10.1016/j.jeurceramsoc.2006.04.068
44.
JiW., RehmanS. S., WangW., WangH., WangY., ZhangJ., ZhangF. and FuZ.: ‘Sintering boron carbide ceramics without grain growth by plastic deformation as the dominant densification mechanism’, Sci. Rep., 2015, 5, 15827–15835. doi: 10.1038/srep15827