In this work, the influence of sand impingements on cathodic protection (CP) of marine carbon steel in natural sea water was studied in comparison with the CP performances in static and flowing sea water without sand particles. Results show that the propagation of local active anodic dissolution at the steel inclusions could be totally inhibited by providing sufficient cathodic current in the sea water free of sand particles. However, the local ‘CP shielding’, potential fluctuation and sand impingements would enhance the anodic dissolution at inclusions, thus leading to the occurrence of erosion-corrosion under CP. The negative shift of the CP potential could not retard the propagation of erosion-corrosion pits under sand impingements. The synergy of erosion and corrosion might result in long-term failure of local CP.
JeffreyRMelchersRE.The changing topography of corroding mild steel surfaces in seawater. Corros Sci. 2007; 49: 2270–2288.
2.
PengZZhaoHLiX.New ductile fracture model for fracture prediction ranging from negative to high stress triaxiality. Int J Plast. 2021; 145: 103057.
3.
XiaDDengCMacdonaldD. Electrochemical measurements used for assessment of corrosion and protection of metallic materials in the field: a critical review. J Mater Sci Technol. 2022; 112: 151–183.
4.
XuYZhouQLiuL. Exploring the corrosion performances of carbon steel in flowing natural sea water and synthetic sea waters. Corros Eng Sci Tech. 2020; 55: 579–588.
5.
ZakowskiKIglinskiPOrlikowskiJ. Modernized cathodic protection system for legs of the production rig-evaluation during ten years of service. Ocean Eng. 2020; 218: 108074.
XuLXinYMaL. Challenges and solutions of cathodic protection for marine ships. Corros Commun. 2021; 2: 33–40.
8.
ISO. 12473 General principles of cathodic protection of seawater, International Organization for Standardization (ISO) (2017).
9.
DaiMLiuJHuangF. Effect of cathodic protection potential fluctuations on pitting corrosion of X100 pipeline steel in acidic soil environment. Corros Sci. 2018; 143: 428–437.
10.
LiuZYLiXGChengYF.Electrochemical state conversion model for occurrence of pitting corrosion on a cathodically polarized carbon steel in a near-neutral pH solution. Electrochim Acta. 2011; 56: 4167–4175.
11.
LiuZYLiXGChengYF.Understand the occurrence of pitting corrosion of pipeline carbon steel under cathodic polarization. Electrochim Acta. 2012; 60: 259–263.
12.
GuptaRKTanMYJEsquivelJ. Occurrence of anodic current and corrosion of steel in aqueous media under fluctuating cathodic protection potentials. Corrosion. 2016; 72: 1243–1251.
13.
XuMLamCNCWongD. Evaluation of the cathodic disbondment resistance of pipeline coatings-a review. Prog Org Coat. 2020; 146: 105728.
14.
MahdaviFForsythMTanMYJ.Techniques for testing and monitoring the cathodic disbondment of organic coatings: an overview of major obstacles and innovations. Prog Org Coat. 2017; 105: 163–175.
15.
LiZGanFMaoX.A study on cathodic protection against crevice corrosion in dilute NaCl solutions. Corros Sci. 2002; 44: 689–701.
16.
SliemMHFayyadEMAbdullahAM. Monitoring of under deposit corrosion for the oil and gas industry: a review. J Petrol Sci Eng. 2021; 204: 108752.
17.
LiuCRevillaRILiX. New insights into the mechanism of localised corrosion induced by TiN-containing inclusions in high strength low alloy steel. J Mater Sci Technol. 2022; 124: 141–149.
18.
XuYZhangQZhouQ. Flow accelerated corrosion and erosion-corrosion behavior of marine carbon steel in natural seawater. Npj Mater Degrad. 2021; 5: 1–13.
19.
LiuLXuYXuC. Detecting and monitoring erosion-corrosion using ring pair electrical resistance sensor in conjunction with electrochemical measurements. Wear. 2019; 428-429: 328–339.
20.
XuYTanMY.Probing the initiation and propagation processes of flow accelerated corrosion and erosion corrosion under simulated turbulent flow conditions. Corros Sci. 2019; 151: 163–174.
21.
ChenZXHuHXGuoXM. Effect of groove depth on the slurry erosion of V-shaped grooved surfaces. Wear. 2022; 488-489: 204133.
22.
LiuLXuYWangZ. Probing and separating corrosion and erosion of pipeline steel using electrical resistance method in conjunction with electrochemical measurements. Measurement. 2021; 183: 109797.
23.
XuYZhangQGaoS. Exploring the effects of sand impacts and anodic dissolution on localized erosion-corrosion in sand entraining electrolyte. Wear. 2021; 478-479: 203907.
24.
GuoHXLuBTLuoJL.Interaction of mechanical and electrochemical factors in erosion-corrosion of carbon steel. Electrochim Acta. 2005; 51: 315–323.
25.
BrownlieFGiourntasLHodgkiessT. Effect of cathodic protection methods on ferrous engineering materials under corrosive wear conditions. Corros Eng Sci Tech. 2020; 55: 480–486.
26.
GiourntasLHodgkiessTGallowayAM.Enhanced approach of assessing the corrosive wear of engineering materials under impingement. Wear. 2015; 338-339: 155–163.
27.
XuYLiuLZhouQ. An overview of major experimental methods and apparatus for measuring and investigating erosion-corrosion of ferrous-based steels. Metals. 2020; 10: 180.
28.
BirkinPRLearRWebsterL. In-situ detection of single particle impact, erosion/corrosion and surface roughening. Wear. 2021; 464-465: 203527.
29.
LiLLWangZBHeSY. Correlation between depassivation and repassivation processes determined by single particle impingement: its crucial role in the phenomenon of critical flow velocity for erosion-corrosion. J Mater Sci Technol. 2021; 89: 158–166.
30.
WhartonJAWoodRJK.Influence of flow conditions on the corrosion of AISI 304L stainless steel. Wear. 2004; 256: 525–536.
31.
WalczakMSharifiSStackMM.On a multiphysics approach to modelling the erosion-enhanced corrosion of low-alloy carbon steel in chloride containing environments. Corros Sci. 2020; 176: 109045.
32.
LiuLXuYZhuY. The roles of fluid hydrodynamics, mass transfer, rust layer and macro-cell current on flow accelerated corrosion of carbon steel in oxygen containing electrolyte. J Electrochem Soc. 2020; 167: 141510.
33.
ZhengRZhaoXDongL. On the cavitation erosion-corrosion of pipeline steel at different locations of Venturi pipe. Eng Fail Anal. 2022; 138: 106333.
34.
XuYLiuLZhouQ. Understanding the influences of pre-corrosion on the erosion-corrosion performance of pipeline steel. Wear. 2020; 442-443: 203151.
35.
WangYChengGWuW. Role of inclusions in the pitting initiation of pipeline steel and the effect of electron irradiation in SEM. Corros Sci. 2018; 130: 252–260.
36.
HornusEWangKPabbruweM. A new experimental method to simulate dynamic crevice corrosion in modular hip arthroplasty. Corros Sci. 2021; 190: 109704.
37.
GuoHLuBLuoJ.Response of surface mechanical properties to electrochemical dissolution determined by in situ nanoindentation technique. Electrochem Commun. 2006; 8: 1092–1098.
38.
IslamMAFarhatZ.Erosion-corrosion mechanism and comparison of erosion-corrosion performance of API steels. Wear. 2017; 376-377: 533–541.
39.
XieJAlpasATNorthwoodDO.Mechano-electrochemical effect between erosion and corrosion. J Mater Sci. 2003; 38: 4849–4856.
40.
WangLLiangJLiH. Quantitative study of the corrosion evolution and stress corrosion cracking of high strength aluminum alloys in solution and thin electrolyte layer containing Cl−. Corros Sci. 2021; 178: 109076.
41.
XiaDQinZSongS. Combating marine corrosion on engineered oxide surface by repelling, blocking and capturing Cl−: a mini review. Corros Commun. 2021; 2: 1–7.