In this work, samples of zirconium alloys Zr1Nb and Zircaloy-4W were subjected to two-stage oxidation experiments – at first in H216O solution and then in H218O steam. Raman spectroscopy was used to analyse distribution of 18O isotope in corrosion layers of the alloys. Layered distribution of 18O was observed in case of Zr1Nb samples; Zircaloy-4W had 18O present only at metal/oxide interface. This observation is attributed to differing kinetic transitions, which influence transport of oxygen through oxide layer.
SteinbrückMPrestelSGerhardsU.High-temperature interaction of oxygen-preloaded Zr1Nb alloy with nitrogen. Nuclear Eng Techn. 2018; 50 (2): 237–245. doi: 10.1016/j.net.2017.12.017
2.
HuangJYaoMChenB. Oxidation behavior of Zr9S2 precipitates in Zr-0.8Sn-1.0Nb-0.3Fe-0.1Cr-xS alloys. Corros Sci. 2017; 120: 82–89. doi: 10.1016/j.corsci.2017.02.024
3.
RafiqueMChaeSKimY.Surface, structural and tensile properties of proton beam irradiated zirconium. Nucl Instrum Methods Phys Res Sect. B. 2016; 365: 120–128. doi: 10.1016/j.nimb.2015.12.001
4.
BojinovMKarastoyanovVKinnunenP. Influence of water chemistry on the corrosion mechanism of a zirconium–niobium alloy in simulated light water reactor coolant conditions. Corros Sci. 2010; 52 (1): 54–67. doi: 10.1016/j.corsci.2009.08.045
5.
LikhanskiiVVAlievTNKolesnikMY. Method of elastic energy minimization for evaluation of transition parameters in oxidation kinetics of Zr alloys alloy in simulated light water reactor coolant conditions. Corros Sci. 2012; 61: 143–147. doi: 10.1016/j.corsci.2012.04.035
6.
DaliYTupinMBossisP. Corrosion kinetics under high pressure of steam of pure zirconium and zirconium alloys followed by in situ thermogravimetry. J Nucl Mater. 2012; 426 (1-3): 148–159. doi: 10.1016/j.jnucmat.2012.03.030
7.
KimHGKimIHParkJY. In situ heating TEM analysis of oxide layer formed on Zr–1.5Nb alloy. J Nucl Mater. 2014; 451 (1-3): 189–197. doi: 10.1016/j.jnucmat.2014.03.050
8.
GouSZhouBChC. Investigation of oxide layers formed on Zircaloy-4 coarse-grained specimens corroded at 360 °C in lithiated aqueous solution. Corros Sci. 2015; 92: 237–244. doi: 10.1016/j.corsci.2014.12.012
9.
TupinMMartinFBisorC. Hydrogen diffusion process in the oxides formed on zirconium alloysduring corrosion in pressurized water reactor conditions. Corros Sci. 2017; 116: 1–13. doi: 10.1016/j.corsci.2016.10.027
10.
ZumpicchiatGPascalSTupinM. Finite element modelling of the oxidation kinetics of Zircaloy-4 with a controlled metal-oxide interface and the influence of growth stress. Corros Sci. 2015; 100: 209–221. doi: 10.1016/j.corsci.2015.07.024
11.
NiNHudsonDWeiJ. How the crystallography and nanoscale chemistry of the metal/oxide interface develops during the aqueous oxidation of zirconium cladding alloys. Acta Mater. 2012; 60 (20): 209–221. doi: 10.1016/j.actamat.2012.09.021
12.
PonzoniLMEMiezaJIHerasEDL. Comparison of delayed hydride cracking behavior of two zirconium alloys. J Nucl Mater. 2013; 439: 238–242. doi: 10.1016/j.jnucmat.2012.08.036
13.
BojinovMCaiWKinnunenP. Kinetic parameters of the oxidation of zirconium alloys in simulated WWER water – Effect of KOH content. J Nucl Mater. 2008; 378 (1): 45–54. doi: 10.1016/j.jnucmat.2008.04.014
14.
GongWZhangHWuC. The role of alloying elements in the initiation of nanoscale porosity in oxide films formed on zirconium alloys. Corros Sci. 2013; 77: 391–396. doi: 10.1016/j.corsci.2013.08.006
15.
KurpaskaLKozaneckiMJasinskiJJ. Stress analysis of zirconia studied by Raman spectroscopy at low temperatures. Spectrochim Acta Part A. 2014; 131: 691–695. doi: 10.1016/j.saa.2014.05.023
16.
KurpaskaLLesniakMJadachR. Shift in low-frequency vibrational spectra measured in-situ at 600°C by Raman spectroscopy of zirconia developed on pure zirconium and Zr-1%Nb alloy. J Mol Struct. 2016; 1126: 186–191. doi: 10.1016/j.molstruc.2016.03.001
17.
PlattPLuntDPolatidisE. In-situ digital image correlation for fracture analysis of oxides formed on zirconium alloys. Corros Sci. 2016; 111: 344–351. doi: 10.1016/j.corsci.2016.05.026
18.
HarlowWLangACDemaskeBD. Thickness-dependent stabilization of tetragonal ZrO2 in oxidized zirconium. Scr Mater. 2018; 145: 95–98. doi: 10.1016/j.scriptamat.2017.09.014
19.
HajAPeresVSerrisE. In situ high temperature oxidation analysis of Zircaloy-4 using acoustic emission coupled with thermogravimetry. J Nucl Mater. 2015; 461: 365–375. doi: 10.1016/j.jnucmat.2015.03.014
20.
MiHMikaelSAllenT. Monitoring of nuclear fuel cladding using Raman spectroscopy. J Nucl Mater. 2014; 445: 7–11. doi: 10.1016/j.jnucmat.2013.10.052
21.
BouvierPGodlewskiJLucazeauGA.Raman study of the nanocrystallite size effect on the pressure–temperature phase diagram of zirconia grown by zirconium-based alloys oxidation. J Nucl Mater. 2002; 300 (2-3): 118–126. doi: 10.1016/S0022-3115(01)00756-5
22.
CiszakCMermouxMMiroS. Micro-Raman analysis of the fuel-cladding interface in a high burnup PWR fuel rod. J Nucl Mater. 2017; 495: 392–404. doi: 10.1016/j.jnucmat.2017.08.038
23.
GuerainMMermouxMDuriezC.The use of micro-Raman imaging to measure 18O tracer distribution in thermally grown zirconia scales. Corros Sci. 2015; 98: 140–149. doi: 10.1016/j.corsci.2015.05.020
24.
KurpaskaLFavergeonJLahocheL. Raman spectroscopy analysis of air grown oxide scale developed on pure zirconium substrate. J Nucl Mater. 2015; 466: 460–467. doi: 10.1016/j.jnucmat.2015.06.005
25.
ASTM G2/G2M-06. e1Standard test method for corrosion testing of products of zirconium, hafnium, and their alloys in water at 680°F (360°C) or in steam at 750°F (400°C). West Conshohocken (PA): ASTM International; 2011.
26.
RenčiukováVMacák SajdlP. Corrosion of zirconium alloys demonstrated by using impedance spectroscopy. J Nucl Mater. 2018; 510: 312–321. doi: 10.1016/j.jnucmat.2018.08.005
27.
GarvieRCNicholsonPS.Phase analysis in zirconia system. J Am Ceram Soc. 1972; 55 (6): 303–305. doi: 10.1111/j.1151-2916.1972.tb11290.x
28.
KimTKimJChoiKJ. Phase transformation of oxide film in zirkonium alloy in high temperature hydrogenated water. Corros Sci. 2015; 99: 134–144. doi: 10.1016/j.corsci.2015.06.034
29.
GassMFenwickMHulmeH. Corrosion of Zircaloys: relating the microstructural observations to the corrosion kinetics. J Nucl Mater. 2018; 509: 343–354. doi: 10.1016/j.jnucmat.2018.07.017
30.
HutchinsonBLehtinenB.A theory of the resistance of Zircaloy to uniform corrosion. J Nucl Mater. 1994; 217: 243–249. doi: 10.1016/0022-3115(94)90373-5