The corrosion performances of X100 steels in the oilfield produced water with different temperature (30°C, 40°C, 60°C) under the simulated working conditions were studied by potentiodynamic polarization (PDP) and electrochemical impedance spectroscopy (EIS) test. Energy dispersive spectroscopy (EDS) was used to measure the element composition of the sample after corrosion. The phase and chemical compositions of the specimens were analyzed by X-ray diffraction (XRD) and Raman spectrometry. The electrochemical results showed that the corrosion resistance of the specimen exposed for 24 hours increased with the increase of the testing temperature, indicating the better protective effect due to the corrosion product film formed under high temperature despite the impact of turbulence. The corrosion products consist of Fe3O4, Fe2O3, α-FeOOH, and γ-FeOOH. The corrosion mechanism model of X100 steel was established and the corrosion behavior was analyzed under simulated working conditions.
GadalaIMAlfantaziA.A study of X100 pipeline steel passivation in mildly alkaline bicarbonate solutions using electrochemical impedance spectroscopy under potentiodynamic conditions and Mott–Schottky. Appl Surf Sci. 2015; 357: 356–368. doi: 10.1016/j.apsusc.2015.09.029
2.
EliyanFFMohammadiFAlfantaziA.An electrochemical investigation on the effect of the chloride content on CO2 corrosion of API-X100 steel. Corros Sci. 2012; 64: 37–43. doi: 10.1016/j.corsci.2012.06.032
3.
CuiZDWuSLZhuSL. Study on corrosion properties of pipelines in simulated produced water saturated with supercritical CO2. Appl Surf Sci. 2006; 252: 2368–2374. doi: 10.1016/j.apsusc.2005.04.008
4.
Fakhru'L-RaziAPendashtehAAbdullahLC. Review of technologies for oil and gas produced water treatment. J Hazard Mater. 2009; 170: 530–551. doi: 10.1016/j.jhazmat.2009.05.044
5.
HaHMGadalaIMAlfantaziA.Hydrogen evolution and absorption in an API X100 line pipe steel exposed to near-neutral pH solutions. Electrochim Acta. 2016; 204: 18–30. doi: 10.1016/j.electacta.2016.03.167
6.
MahdiERaufAEltaiEO.Effect of temperature and erosion on pitting corrosion of X100 steel in aqueous silica slurries containing bicarbonate and chloride content. Corros Sci. 2014; 83: 48–58. doi: 10.1016/j.corsci.2014.01.021
7.
YaroASAbdul-KhalikKRKhadomAA.Effect of CO2 corrosion behavior of mild steel in oilfield produced water. J Loss Prev Process Ind. 2015; 38: 24–38. doi: 10.1016/j.jlp.2015.08.003
8.
ZhuSDZhouGSMiaoJ. Mechanical properties of CO2 corrosion scale formed at different temperatures and their relationship to corrosion rate. Br Corros J. 2013; 47: 171–177.
9.
YuFGaoKWQiaoLJ. Effect of temperature on microstructure and mechanical properties of CO2 corrosion scale on N80 sreel. Corros Protect. 2009; 30(3):145-148+157.
10.
YinZFFengYRZhaoWZ. Effect of temperature on CO2 corrosion of carbon steel. Surf Interface Anal. 2009; 41: 517–523. doi: 10.1002/sia.3057
11.
WangYChengGLiY.Observation of the pitting corrosion and uniform corrosion for X80 steel in 3.5 wt.% NaCl solutions using in-situ and 3-D measuring microscope. Corros Sci. 2016; 111: 508–517. doi: 10.1016/j.corsci.2016.05.037
12.
EliyanFFAlfantaziA.Corrosion of API-X100 steel heat affected zones (HAZs) in CO2-saturated solutions - EIS investigations, European Corrosion Congress, Eurocorr; 2013.
13.
EliyanFFAlfantaziA.Influence of temperature on the corrosion behavior of API-X100 pipeline steel in 1-bar CO2-HCO3− solutions: an electrochemical study. Mater Chem Phys. 2013; 140: 508–515. doi: 10.1016/j.matchemphys.2013.03.061
14.
DongSLiuWZhangJ. Effect of oxygen on CO2 corrosion and erosion-corrosion behaviour of N80 steel under high temperature and high pressure, corrosion 2014. NACE Int. 2014: 4198–4211. Paper no. 4198.
15.
NešićS.Key issues related to modelling of internal corrosion of oil and gas pipelines – a review. Corros Sci. 2007; 49: 4308–4338. doi: 10.1016/j.corsci.2007.06.006
16.
de OliveiraESDda Costa PereiraRFde MeloIR. Corrosion behavior of API 5L X80 steel in the produced water of onshore oil recovery facilities. Mater Res. 2017; 20: 432–439. doi: 10.1590/1980-5373-mr-2016-0954
17.
DomingoCRodrı´guez-ClementeRBlesaM.Morphological properties of α-FeOOH, γ-FeOOH and Fe 3 O 4 obtained by oxidation of aqueous Fe(II) solutions. J Colloid Interface Sci. 1994; 165: 8. doi: 10.1006/jcis.1994.1225
18.
IslamMAFarhatZ.Erosion-corrosion mechanism and comparison of erosion-corrosion performance of API steels. Wear. 2017; 376-377: 533–541. doi: 10.1016/j.wear.2016.12.058
19.
OkonkwoPShakoorRBenamorA. Corrosion behavior of API X100 steel material in a hydrogen Sulfide environment. Metals (Basel). 2017; 7: 109. doi: 10.3390/met7040109
20.
GadalaIMAlfantaziA.Electrochemical behavior of API-X100 pipeline steel in NS4, near-neutral, and mildly alkaline pH simulated soil solutions. Corros Sci. 2014; 82: 45–57. doi: 10.1016/j.corsci.2013.12.020
21.
WangYChengGWuW. Effect of pH and chloride on the micro-mechanism of pitting corrosion for high strength pipeline steel in aerated NaCl solutions. Appl Surf Sci. 2015; 349: 746–756. doi: 10.1016/j.apsusc.2015.05.053
22.
MoiseevaNSRLS.Effect of pH value on corrosion behavior of steel in CO 2 -containing Aqueous Media. J Appl Chem. 2002; 75: 1659–1667.
23.
MalkaRNešićSGulinoDA.Erosion–corrosion and synergistic effects in disturbed liquid-particle flow. Wear. 2007; 262: 791–799. doi: 10.1016/j.wear.2006.08.029
24.
ZengLZhangGAGuoXP.Erosion–corrosion at different locations of X65 carbon steel elbow. Corros Sci. 2014; 85: 318–330. doi: 10.1016/j.corsci.2014.04.045
25.
ZhangGAZengLHuangHL. A study of flow accelerated corrosion at elbow of carbon steel pipeline by array electrode and computational fluid dynamics simulation. Corros Sci. 2013; 77: 334–341. doi: 10.1016/j.corsci.2013.08.022
26.
IslamMAAlamTFarhatZ.Construction of erosion mechanism maps for pipeline steels. Tribol Int. 2016; 102: 161–173. doi: 10.1016/j.triboint.2016.05.033
27.
XuGCaiLUllmannA. Experiments and simulation of water displacement from lower sections of oil pipelines. J Petrol Sci Eng. 2016; 147: 829–842. doi: 10.1016/j.petrol.2016.09.049
28.
SunGZhangJMaC. Start-up flow behavior of pipelines transporting waxy crude oil emulsion. J Petrol Sci Eng. 2016; 147: 746–755. doi: 10.1016/j.petrol.2016.10.007
29.
NamNDKimMJKimJG.Corrosion behavior of low alloy steels containing manganese in mixed chloride sulfate solution. Metall Mater Trans A. 2014; 45: 893–905. doi: 10.1007/s11661-013-2002-6
30.
LópezDASchreinerWHde SánchezSR. The influence of carbon steel microstructure on corrosion layers An XPS and SEM characterization. Appl Surf Sci. 2003; 207: 69–85. doi: 10.1016/S0169-4332(02)01218-7
31.
TanupabrungsunT.NACE international store - effect of pH on CO2 corrosion at elevated temperatures, corrosion 2013. NACE Int. 2013: 2348–2358. p. paper no. 2348.
32.
MohammadiFEliyanFFEliyanE. Internal corrosion of stabilized crude oil APIX100 steel pipelines, Rio Pipeline Conference & Exposition, NACE International, 2012. p. 11.
33.
EliyanFFMahdiE-SAlfantaziA.Electrochemical evaluation of the corrosion behaviour of API-X100 pipeline steel in aerated bicarbonate solutions. Corros Sci. 2012; 58: 181–191. doi: 10.1016/j.corsci.2012.01.015
34.
MohammadiFEliyanFFAlfantaziA.Corrosion of simulated weld HAZ of API X-80 pipeline steel. Corros Sci. 2012; 63: 323–333. doi: 10.1016/j.corsci.2012.06.014
35.
WuJWBaiDBakerAP. Electrochemical techniques correlation study of on-line corrosion monitoring probes. Mater Corros. 2015; 66: 143–151. doi: 10.1002/maco.201307175
36.
RichterSHilbertLRThorarinsdottirRI.On-line corrosion monitoring in geothermal district heating systems. I. General corrosion rates. Corros Sci. 2006; 48: 1770–1778. doi: 10.1016/j.corsci.2005.06.019
37.
RichterSThorarinsdottirRIJonsdottirF.On-line corrosion monitoring in geothermal district heating systems. II. Localized corrosion. Corros Sci. 2007; 49: 1907–1917. doi: 10.1016/j.corsci.2006.10.030
38.
VelázquezJCCruz-RamirezJCValorA. Modeling localized corrosion of pipeline steels in oilfield produced water environments. Eng Fail Anal. 2017; 79: 216–231. doi: 10.1016/j.engfailanal.2017.04.027
39.
TianHLiWHouB. Insights into corrosion inhibition behavior of multi-active compounds for X65 pipeline steel in acidic oilfield formation water. Corros Sci. 2017; 117: 43–58. doi: 10.1016/j.corsci.2017.01.010
Honarvar NazariMAllahkaramSRKermaniMB.The effects of temperature and pH on the characteristics of corrosion product in CO2 corrosion of grade X70 steel. Mater Des. 2010; 31: 3559–3563. doi: 10.1016/j.matdes.2010.01.038
42.
ZhuSDFuAQMiaoJ. Corrosion of N80 carbon steel in oil field formation water containing CO2 in the absence and presence of acetic acid. Corros Sci. 2011; 53: 3156–3165. doi: 10.1016/j.corsci.2011.05.059
43.
BauxJCausséNEsvanJ. Impedance analysis of film-forming amines for the corrosion protection of a carbon steel. Electrochim Acta. 2018; 283: 699–707. doi: 10.1016/j.electacta.2018.06.189
44.
WangZ-fYinF-xWuL-x. Corrosion resistance on high strength bainitic steel and 09CuPCrNi after wet-dry cyclic conditions. J Iron Steel Res Int. 2013; 20: 72–78. doi: 10.1016/S1006-706X(13)60060-6
45.
ZhangGALiuDLiYZ. Corrosion behaviour of N80 carbon steel in formation water under dynamic supercritical CO2 condition. Corros Sci. 2017; 120: 107–120. doi: 10.1016/j.corsci.2017.02.012
46.
LiuZYLiQCuiZY. Field experiment of stress corrosion cracking behavior of high strength pipeline steels in typical soil environments. Constr Build Mater. 2017; 148: 131–139. doi: 10.1016/j.conbuildmat.2017.05.058
47.
TewaryNKKunduANandiR. Microstructural characterisation and corrosion performance of old railway girder bridge steel and modern weathering structural steel. Corros Sci. 2016; 113: 57–63. doi: 10.1016/j.corsci.2016.10.004
48.
ZouYWangJZhengYY.Electrochemical techniques for determining corrosion rate of rusted steel in seawater. Corros Sci. 2011; 53: 208–216. doi: 10.1016/j.corsci.2010.09.011
49.
HongYLiZQiaoG. Numerical simulation and experimental investigation of the stray current corrosion of viaducts in the high-speed rail transit system. Constr Build Mater. 2017; 157: 416–423. doi: 10.1016/j.conbuildmat.2017.09.114
50.
GéninJ-MRRefaitPHAbdelmoulaM.Green rusts and their relationship to iron corrosion; a key role in microbially influenced corrosion. Hyperfine Interact. 2002; 139/140: 119–131. doi: 10.1023/A:1021219021919
51.
GéninaJ-MRRefaitaPBourriéG. Structure and stability of the Fe(II)–Fe(III) green rust ‘fougerite’ mineral and its potential for reducing pollutants in soil solutions. Appl Geochem. 2002; 16: 559–570. doi: 10.1016/S0883-2927(00)00043-3
52.
MaHGuYGaoH. Microstructure, chemical composition and local corrosion behavior of a friction stud welding joint. J Mater Eng Perform. 2018; 27: 666–676. doi: 10.1007/s11665-018-3182-4
53.
RamanAKubanBRazvanA.The application of infrared spectroscopy to the study of atmospheric rust systems—I. Standard spectra and illustrative applications to identify rust phases in natural. Corros Sci. 1991; 32: 1295–1306. doi: 10.1016/0010-938X(91)90049-U
54.
de FariaDLAVenâncio SilvaSde OliveiraMT.Raman microspectroscopy of some iron oxides and oxyhydroxides. J Raman Spectrosc. 1997; 28: 873–878. doi: 10.1002/(SICI)1097-4555(199711)28:11<873::AID-JRS177>3.0.CO;2-B
55.
LiPZhaoYLiuB. Experimental testing and numerical simulation to analyze the corrosion failures of single well pipelines in Tahe oilfield. Eng Fail Anal. 2017; 80: 112–122. doi: 10.1016/j.engfailanal.2017.06.014
56.
Dall'AcquaDBenucciMCorvaroF. Experimental results of pipeline dewatering through surfactant injection. J Petrol Sci Eng. 2017; 159: 542–552. doi: 10.1016/j.petrol.2017.08.068