The growth rate of pits formed on Alloy 800 in chloride solutions containing various thiosulphate concentrations was assessed by potentiostatic polarisation, in situ corrosion image observation, and image analysis. The pitting growth rate was a function of solution chemistry: in chloride solution pits were small but numerous, in chloride + thiosulphate solution, the pits were large. Competitive adsorption on Alloy 800 of chloride and thiosulphate ions affected the pitting potential and therefore the pitting growth rate on the metal. The reduction of thiosulphate to elemental sulphur accelerated the pitting growth rate in chloride + thiosulphate solutions.
FanHXiaDBehnamianYMemory effect and recoverability of passive film degradation of alloy 800 in simulated crevice chemistry. Nucl Eng Des. 2014; 280: 57–61. doi: 10.1016/j.nucengdes.2014.08.033
2.
ZhangWCarceaAGNewmanRC.Pitting of steam-generator tubing alloys in solutions containing thiosulfate and sulfate or chloride. Faraday Discuss.2015; 180: 233–249. doi: 10.1039/C5FD00008D
3.
XiaD-HBehnamianYChenX-YA mechanistic study of sulfur-induced passivity degradation of alloy 800 in a simulated alkaline crevice environment at 300°C. J Solid State Electrochem. 2015; 19: 3567–3578. doi: 10.1007/s10008-015-2822-y
4.
ZhuRKLuoJL.Investigation of stress-enhanced surface reactivity on alloy 800 using scanning electrochemical microscopy. Electrochem commun. 2010; 12 (12): 1752–1755. doi: 10.1016/j.elecom.2010.10.014
5.
LeeEHKimKMKimUC.Effects of reduced sulfur on the corrosion behavior of alloy 600 in high-temperature water. Mat Sci Eng: A. 2007; 449-451: 330–333. doi: 10.1016/j.msea.2006.02.424
6.
FangZStaehleRW.Effects of the valence of sulfur on passivation of alloys 600, 690, and 800 at 25 degrees C and 95 degrees C. Corrosion. 1999; 55 (4): 355–379. doi: 10.5006/1.3283997
7.
XiaD-HZhuR-KBehnamianYpH effect on sulfur-induced passivity degradation of alloy 800 in simulated crevice chemistries. J Electrochem Soc. 2014; 161 (4): C201–C214. doi: 10.1149/2.063404jes
8.
KappesMFrankelGSSridharNCorrosion behavior of carbon steel in acidified, thiosulfate-containing brines. Corrosion. 2012; 68 (10): 872–884. doi: 10.5006/0610
9.
WuSWangJSongSFactors influencing passivity breakdown on UNS N08800 in neutral chloride and thiosulfate solutions. J Electrochem Soc. 2017; 164 (4): C94–C103. doi: 10.1149/2.0541704jes
10.
TsaiW-TWuT-F.Pitting corrosion of alloy 690 in thiosulfate-containing chloride solutions. J Nucl Mater. 2000; 277 (2-3): 169–174. doi: 10.1016/S0022-3115(99)00209-3
11.
NaghizadehMNakhaieDZakeriMEffect of thiosulfate on pitting corrosion of 316SS I. Critical pitting temperature and pit chemistry. J Electrochem Soc. 2015; 162 (1): C71–C77. doi: 10.1149/2.0861501jes
12.
Duret-ThualCCostaDYangWThe role of thiosulfates in the pitting corrosion of Fe-17Cr alloys in neutral chloride solution: electrochemical and XPS study. Corros Sci. 1997; 39 (5): 913–933. doi: 10.1016/S0010-938X(97)81158-4
13.
NewmanRCWongWPEzuberHPitting of stainless steels by thiosulfate ions. Corrosion. 1989; 45 (4): 282–287. doi: 10.5006/1.3577855
14.
WangYWuGHeLEffect of thiosulfate on metastable pitting of 304L and S32101 in chloride- and thiosulfate-containing environment. Corrosion. 2016; 72 (5): 628–635. doi: 10.5006/1955
15.
XiaD-HZhuR-KBehnamianYUnderstanding the interaction of thiosulfate with alloy 800 in aqueous chloride solutions using SECM. J Electroanal Chem. 2015; 744: 77–84. doi: 10.1016/j.jelechem.2015.03.006
16.
XiaD-HFanH-QYangL-XSemiconductivity conversion of passive films on alloy 800 in chloride solutions containing various concentrations of thiosulfate. J Electrochem Soc. 2015; 162 (9): C482–C486. doi: 10.1149/2.0611509jes
17.
NewmanRCIsaacsHSAlmanB.Effects of sulfur compounds on the pitting behavior of type 304 stainless steel in near-neutral chloride solutions. Corrosion. 1982; 38 (5): 261–265. doi: 10.5006/1.3577348
18.
ChoudharyLMacdonaldDDAlfantaziA.Role of thiosulfate in the corrosion of steels: a review. Corrosion. 2015; 71 (9): 1147–1168. doi: 10.5006/1709
19.
WangYSinghPM.Corrosion behavior of austenitic and duplex stainless steels in thiosulfate-and chloride-containing environments. Corrosion. 2015; 71 (8): 937–944. doi: 10.5006/1694
20.
StaehleRWGormanJA.Quantitative assessment of submodes of stress corrosion cracking on the secondary side of steam generator tubing in pressurized water reactors: part 3. Corrosion. 2004; 60 (2): 115–180. doi: 10.5006/1.3287716
21.
NakhaieDZakeriMNaghizadehMEffect of thiosulfate on pitting corrosion of 316SS: II. Metastable pitting and transition to stability. J Electrochem Soc. 2015; 162 (4): C121–C127. doi: 10.1149/2.0041504jes