Aluminium is a commonly used metal in Mauritius. However, the tropical Mauritian atmosphere is quite corrosive with the highest measured corrosivity, according to ISO 9223, falling in the category C4. Hence, this study was performed to investigate the atmospheric corrosion behaviour of aluminium AA1050 in the island. The aluminium samples were exposed outdoors at three sites, according to ISO 8565. Upon removal after specific time intervals over a 1½ years period, pit depth, pit diameter and pit density of the samples were determined. The maximum pit depth varied with the time of exposure, according to the power law function. Pit diameter increased linearly with the time of exposure. Chart rating, according to ISO 11463, was also performed. It was found that the corrosivity of the Mauritian atmosphere falls in categories A4-B1-C1 and A5-B1-C1. Application of extreme value statistics showed that Gumbel type 1 distribution fits maximum pit depth data at the three sites.
SurnamBYR.Three years outdoor exposure of low carbon steel in Mauritius. Anti-Corros Methods Mater. 2015; 62 (4): 246–252. doi: 10.1108/ACMM-12-2013-1328
3.
SeenauthS.Climate classification for Mauritius I. using Koppen and Holdridge models [dissertation (B.Sc.)], University of Mauritius, Reduit, Mauritius2006. pp. 2–12.
4.
BlucherDBSvenssonJEJohanssonLG.The influence of CO2, AlCl3.6H2O, MgCl2.6H2O, Na2SO4 and NaCl on the atmospheric corrosion of aluminium. Corros. Sci. 2006; 48: 1848–1866. doi: 10.1016/j.corsci.2005.05.027
5.
HouskaC.Metals for corrosion resistance. Constr Specifier. 2000; 2: 23–30.
6.
BlackwoodDJChongASL.Pitting corrosion of aluminium in absence of chloride. Br Corros J. 1998; 33 (3): 219–224. doi: 10.1179/bcj.1998.33.3.219
7.
PorroAOteroTFElolaAS.Gravimetric corrosion monitoring and mathematical fitting of atmospheric corrosion data for carbon steel. Br Corros J. 1992; 27 (3): 231–235. doi: 10.1179/000705992798268611
8.
SurnamBYROletiCV.Atmospheric corrosion in Mauritius. Corros Eng Sci Technol. 2012; 47 (6): 446–455. doi: 10.1179/1743278212Y.0000000026
9.
SyedS.Influence of the environment on atmospheric corrosion of aluminium. Corros Eng Sci Technol. 2010; 45 (4): 282–287. doi: 10.1179/147842208X373182
10.
VargelC.Corrosion of aluminium. London: Elsevier; 2004.
11.
SoaresCGGarbatovYZayedA. Influence of environmental factors on corrosion of ship structures in marine atmosphere. Corros Sci. 2009; 51: 2014–2026. doi: 10.1016/j.corsci.2009.05.028
12.
XiaoJChaudhuriS.Predictive modeling of localized corrosion: an application to aluminium alloys. Electrochim Acta. 2011; 56: 5630–5641. doi: 10.1016/j.electacta.2011.04.019
13.
ShibataT.Evaluation of corrosion failure by extreme value statistics. ISIJ Int. 1991; 31 (2): 115–121. doi: 10.2355/isijinternational.31.115
14.
DavisJR.Corrosion of aluminium and aluminium alloys. New York, NY: ASM International; 1999. p. 45–46.
15.
JohnsonWK.Recent developments in pitting corrosion of aluminium. Br Corros J. 1971; 6: 200–204. doi: 10.1179/000705971798323694
16.
MelchersRE.Time dependent development of aluminium pitting corrosion. Adv Mater Sci Eng. 2015; 2015. doi: 10.1155/2015/215712
17.
TaoLSongSZhangX. Image analysis of atmospheric corrosion of field exposure high strength aluminium alloys. Appl Surf Sci. 2008; 254: 6870–6874. doi: 10.1016/j.apsusc.2008.04.088
18.
CordnerRJ.Atmospheric corrosion survey of New Zealand. Br Corros J. 1990; 25 (2): 115–118. doi: 10.1179/bcj.1990.25.2.115
19.
SunSZhengQLiD. Long-term atmospheric corrosion behaviour of aluminium alloys 2024 and 7075 in urban, coastal and industrial environments. Corros Sci. 2009; 51: 719–727. doi: 10.1016/j.corsci.2009.01.016
20.
BhandariJKhanFAbbassiR. Modelling of pitting corrosion in marine and offshore steel structures – A technical review. J Loss Prev Process Ind. 2015; 37: 39–62. doi: 10.1016/j.jlp.2015.06.008
21.
MelchersRE.Extreme value statistics and long-term marine pitting corrosion of steel. Probabilist Eng Mech. 2008; 23: 482–488. doi: 10.1016/j.probengmech.2007.09.003
22.
ShibataP.Corrosion probability and statistical evaluation of corrosion data. In: RevieRW, editor. Uhlig's corrosion handbook. New Jersey: Wiley; 2011. pp. 365–384.
23.
ISO 8565:2011. Metals and alloys – atmospheric corrosion testing – general requirements. Switzerland: International Organization for Standardization; 2011.
24.
ISO 9223:2012. Corrosion of metals and alloys – corrosivity of atmospheres – classification, determination and estimation. Switzerland: International Organization for Standardization; 2012.
25.
Vander VoortGF.Metallography: principles and practiceNew York: ASM International; 1984.
26.
ISO 11463:1995. Corrosion of metals and alloys – evaluation of pitting corrosion. Switzerland: International Organization for Standardization; 1995.
27.
De la FuenteDOtero-HuertaEMorcilloM.Studies of long-term weathering of aluminium in the atmosphere. Corros Sci. 2007; 49: 3134–3148. doi: 10.1016/j.corsci.2007.01.006
28.
MendozaARCorvoF.Outdoor and indoor atmospheric corrosion of non-ferrous metals. Corros Sci. 2000; 42: 1123–1147. doi: 10.1016/S0010-938X(99)00135-3
29.
MattssonELindgrenS.Metal corrosion in the atmosphere. Philadelphia: American Society for Testing and Materials; 1968.
30.
NatesanMVankatcchariGPalaniswamyN.Kinetics of atmospheric corrosion of mild steel, zinc, galvanized iron and aluminium at 10 exposure stations in India. Corros Sci. 2006; 48: 3584–3608. doi: 10.1016/j.corsci.2006.02.006
31.
HoeppnerDW.Pitting Corrosion: Morphology and Characterization, Invited Chapter 5 in AVT-140 Corrosion Fatigue and Environmentally Assisted Cracking in Aging Military Vehicles, NATO, RTO, NATO, France; 2011.
32.
OteroELizarbeRFeliuS.Behaviour of aluminium during 10 years’ exposure at a coastal test site at Alicante. Br Corros J. 1978; 13 (2): 82–84. doi: 10.1179/000705978798318800
33.
Mikhailovskii YN, Klark GB, Shuvakhina LA, Agafonov VV, Zhuravlena NI. Calculation of atmospheric corrosion rate of aluminum and its alloys in various climatic zones according to meteorological parameters. Prot. Met.1973; 9: 240–246.
34.
BudovGM.Third international congress on metallic corrosion; 1969; Moscow4: 445–453.
35.
BerukshtisGKKlarkGB.Atmospheric corrosion of steel, zinc, cadmium, copper and aluminium in different coastal and continental regions. In: TomashovND and MirolyubevEN, editors. Corrosion of metals and alloys. Jerusalem: Israel Program for Scientific; 1966. p. 281–297.
36.
ErnstPNewmanRC.Pit growth studies in stainless steel foils. I. Introduction and pit growth kinetics. Corro Sci. 2002; 44: 927–941. doi: 10.1016/S0010-938X(01)00133-0
37.
ErnstPNewmanRC.Pit growth studies in stainless steel foils. II. Effect of temperature, chloride concentration and sulphate addition. Corros Sci. 2002; 44: 943–954. doi: 10.1016/S0010-938X(01)00134-2
38.
SriramanMrPidapartiRM.Crack initiation life of materials under combined pitting corrosion and cyclic loading. J Mater Eng Perform. 2010; 19: 7–12. doi: 10.1007/s11665-009-9379-9