The evolution of atmospheric corrosion of 316 stainless steel subjected to a simulated marine atmosphere was investigated by scanning electron microscopy, optical microscopy, X-ray photoelectron spectroscopy, and electrochemical measurements. The results indicate that the initiation of pits is associated with the dissolution of MnS inclusion; the maximum pit depth of 316 stainless steel increased in linear relationship with the extension of corrosion time; the corrosion products possess more hydroxide; the ratio of [Cr]/{[Cr]+[Fe]} in the corrosion products gradually increases with increasing time. The protective ability of corrosion products formed on 316 stainless steel has also been discussed.
DongC. F.LuoH.XiaoK.LiP. H. and LiX. G.: ‘Evaluation of corrosion behavior of 316L stainless steel exposed in marine atmosphere of Xisha islands’J. Sichuan Univ., 201244179–184.
2.
LuoH.LiX. G.XiaoK. and DongC. F.: ‘Corrosion behavior of 304 stainless steel in the marine atmospheric environment of Xisha islands’J. Univ. Sci. Technol. Beijing201335332–338.
3.
LiangC. F.YuC. J. and HouW. T.: ‘A study of atmospheric corrosion of stainless steel: a summary of 12 year exposure testing’J. Chin. Soc. Corros. Prot., 199919227–232.
4.
ButtonH. E. and SimmD. W.: ‘The influence of particulate matter on the corrosion behavior of type 316 stainless steel’Anti-Corros. Methods Mater., 1985328–10. doi: 10.1108/eb020346
5.
WallinderD.WallinderI. O. and LeygrafC.: ‘Influence of surface treatment of type 304L stainless steel on atmospheric corrosion resistance in urban and marine environments’Corrosion200359220–227. doi: 10.5006/1.3277554
6.
AsamiK. and HashimotoK.: ‘Importance of initial surface film in the degradation of stainless steels by atmospheric exposure’Corros. Sci., 2003452263–2283. doi: 10.1016/S0010-938X(03)00047-7
7.
LuoH.LiX. G.DongC. F. and XiaoK.: ‘Degradation of austenite stainless steel by atmospheric exposure in tropical marine environment’Corros. Eng. Sci. Technol., 201348221–229. doi: 10.1179/1743278212Y.0000000070
8.
GuntherM.StevensN. P. C.McFiffansG. and CookA. B.: ‘Investigation into composition and deposition of artificially produced marine aerosols on austenitic stainless steels’Corros. Eng. Sci. Technol., 201449509–513. doi: 10.1179/1743278214Y.0000000179
9.
CookA. B.LyonS. B.StevensN. P. C.GuntherM.McFiffansG.NewmanR. C. and EngelbergD. L.: ‘Assessing the risk of under-deposit chloride-induced stress corrosion cracking in austenitic stainless steel nuclear waste containers’Corros. Eng. Sci. Technol., 201449529–534. doi: 10.1179/1743278214Y.0000000204
10.
LuoH.LiX. G.DongC. F. and XiaoK.: ‘Research on atmosphere exposure in tropical marine and accelerated corrosion test of 304 stainless steel’J. Chin. Soc. Corros. Prot., 201333193–198.
11.
WangJ.WangZ. Y. and KeW.: ‘Corrosion behavior of weathering steel in diluted Qinghai salt lake water in a laboratory accelerated test that involved cyclic wet/dry conditions’Mater. Chem. Phys., 2010124952–958. doi: 10.1016/j.matchemphys.2010.07.069
12.
PandaB.BalasubramaniamR. and DwivediG.: ‘On the corrosion behavior of novel high carbon rail steels in simulated cyclic wet-dry salt fog conditions’Corros. Sci., 2008501684–1692. doi: 10.1016/j.corsci.2008.02.021
13.
HanW.YuG. and WangZ.: ‘Characterization of initial atmospheric corrosion carbon steels by field exposure and laboratory simulation’Corros. Sci., 2007492920–2935. doi: 10.1016/j.corsci.2007.01.009
14.
KomazakiS.KobayashiK.MisawaT. and FukuzumiT.: ‘Environmental embrittlement of automobile spring steels caused by wet-dry cyclic corrosion in sodium chloride solution’Corros. Sci., 2005472450–2460. doi: 10.1016/j.corsci.2004.10.008
15.
WangB. B.WangZ. Y.HanW.WangC. and KeW.: ‘Effects of magnesium chloride-based multicomponent salts on atmospheric corrosion of aluminum alloy 2024’Trans. Nonferrous Met. Soc. China2013231199–1208. doi: 10.1016/S1003-6326(13)62584-4
16.
‘Standard Guide for Examination and Evaluation of Pitting Corrosion’, ASTM Standard G46-94, ASTM International, West Conshohocken, PA; 2005.
17.
PanC.LiuL.LiY. and WangF. H.: ‘Pitting corrosion of 304ss nanocrystalline thin film’Corros. Sci., 20137332–43. doi: 10.1016/j.corsci.2013.03.022
18.
ZhengS. J.WangY. J.ZhangB.ZhuY. L.LiuC.HuP. and MaX. L.: ‘Identification of MnCr2O4 nano-octahedron in catalyzing pitting corrosion of austenitic stainless steels’Acta Mater., 2010585070–5085. doi: 10.1016/j.actamat.2010.05.043
19.
SchmukiP.HildebrandH.FriedrichA. and VirtanenS.: ‘The composition of the boundary region of MnS inclusions in stainless steel and its relevance in triggering pitting corrosion’Corros. Sci., 2005471239–1250. doi: 10.1016/j.corsci.2004.05.023
20.
WebbE. G. and AlkireR. C.: ‘Pit initiation at single sulfide inclusions in stainless steel: ?’Mathematical model, J. Electrochem. Soc., 2002149B286–B295. doi: 10.1149/1.1474432
21.
TsutsumiY.NishikataA. and TsuruT.: ‘Pitting corrosion mechanism of Type 304 stainless steel under a droplet of chloride solutions’Corros. Sci., 2007491394–1407. doi: 10.1016/j.corsci.2006.08.016
22.
OkamotoG.: ‘Passive film of 18-8 stainless steel structure and its function’Corros. Sci., 197313471–489. doi: 10.1016/0010-938X(73)90031-0
23.
SaitoH.ShibataT. and OkamotoG.: ‘The inhibitive action of bound water in the passive film of stainless steel against chloride corrosion’Corros. Sci., 197919693–708. doi: 10.1016/S0010-938X(79)80141-9
24.
HaoL.ZhangS. X.DongJ. H. and KeW.: ‘Evolution of corrosion of MnCuP weathering steel submitted to wet/dry cyclic tests in a simulated coastal atmosphere’Corros. Sci., 201258175–180. doi: 10.1016/j.corsci.2012.01.017
25.
LiuY. Z.WangZ. Y. and KeW.: ‘Study on influence of native oxide and corrosion products on atmospheric corrosion of pure Al’Corros. Sci., 201480169–176. doi: 10.1016/j.corsci.2013.11.027
26.
LiQ. X.WangZ. Y.HanW. and HanE. H.: ‘Characterization of the rust formed on weathering steel exposed to Qinghai salt lake atmosphere’Corros. Sci., 200850365–371. doi: 10.1016/j.corsci.2007.06.020