Can the melt flow index be used to predict the success of fused deposition modelling of commercial poly(lactic acid) filaments into 3D printed materials?
The melt flow index (MFI) of seven commercial poly(lactic acid) (PLA) grades is investigated in view of 3D printing quality. A threshold value of 10 g (10 min)−1 (2.16 kg; ISO 1133) is put forward for a successful printing (190–220°C), enabling a fast and practical screening of PLA materials. It is however shown that a sole focus on MFI is insufficient, as the plasticiser type and crystallinity also play a role after the polymer melt deposition. The latter is supported by scanning electron micromorphology and differential scanning calorimetry measurements. In particular, blending with poly(hydroxyl butyrate) (PHB; 20 m%) allows to control both MFI and crystallinity without the need for annealing.
HwangS, ReyesEI, MoonK-S, Thermo-mechanical characterization of metal/polymer composite filaments and printing parameter study for fused deposition modeling in the 3D printing process. J. Electron Mater. 2015;44(3):771–777. doi: 10.1007/s11664-014-3425-6
2.
YuWW, ZhangJ, WuJR, Incorporation of graphitic nano-filler and poly(lactic acid) in fused deposition modeling. J Appl Polym Sci. 2017;134(15):44703. doi: 10.1002/app.44703
3.
SinghS, RamakrishnaS, SinghR.Material issues in additive manufacturing: a review. J Manuf Process2017;25:185–200. doi: 10.1016/j.jmapro.2016.11.006
4.
RochaCR, Torrado PerezAR, RobersonDA, Novel ABS-based binary and ternary polymer blends for material extrusion 3D printing. J Mater Res. 2014;29(17):1859–1866. doi: 10.1557/jmr.2014.158
5.
SerraT, Ortiz-HernandezM, EngelE, Relevance of PEG in PLA-based blends for tissue engineering 3D-printed scaffolds. Mater Sci Eng C Mater Biol Appl.2014;38:55–62. doi: 10.1016/j.msec.2014.01.003
6.
HafsaMN, IbrahimM, WahabMS, Evaluation of FDM pattern with ABS and PLA material. Appl Mech Mater. 2013;465–466:55–59. doi: 10.4028/www.scientific.net/AMM.465-466.55
SilvaALN, CiprianoTF, da SilvaAHMdFT, Thermal, rheological and morphological properties of poly (lactic acid) (PLA) and talc composites. Polímeros Ciência e Tecnol. 2014;24(3):276–282. doi: 10.4322/polimeros.2014.067
9.
DorganJR, LehermeierH, MangM.Thermal and rheological properties of commercial-grade poly (lactic acid) s. J Polym Environ. 2000;8(1):1–9. doi: 10.1023/A:1010185910301
10.
RaviP, ShiakolasPS, WelchTR.Poly-l-lactic acid: pellets to fiber to fused filament fabricated scaffolds, and scaffold weight loss study. Additive Manuf.2017;16:167–176. doi: 10.1016/j.addma.2017.06.002
11.
SunQ, RizviG, BellehumeurC, Effect of processing conditions on the bonding quality of FDM polymer filaments. Rapid Prototyp J. 2008;14(2):72–80. doi: 10.1108/13552540810862028
12.
RamanathHS, ChuaCK, LeongKF, Melt flow behaviour of poly-epsilon-caprolactone in fused deposition modelling. J Mater Sci Mater Med2008;19(7): 2541–2550. doi: 10.1007/s10856-007-3203-6
13.
ArmentanoI, FortunatiE, BurgosN, Processing and characterization of plasticized PLA/PHB blends for biodegradable multiphase systems. Express Polym Lett. 2015;9(7):583–596. doi: 10.3144/expresspolymlett.2015.55
14.
NikzadM, MasoodSH, SbarskiI, Rheological properties of a particulate-filled polymeric composite through fused deposition process. Mater Sci Forum. 2010;654–656:2471–2474. doi: 10.4028/www.scientific.net/MSF.654-656.2471
15.
ShenoyAV, SainiDR.Melt flow index: more than just a quality control rheological parameter. Part II Adv Polym Technol. 1986;6(2):125–145. doi: 10.1002/adv.1986.060060201
16.
WangL, GramlichWM, GardnerDJ.Improving the impact strength of poly(lactic acid) (PLA) in fused layer modeling (FLM). Polym.2017;114:242–248. doi: 10.1016/j.polymer.2017.03.011
17.
WautersG., Polylactic acid (PLA) filament development for extrusion-based additive manufacturing. Ghent (FL): Ghent University; 2015.
18.
KurusuRS, DemarquetteNR, GauthierC, Effect of ageing and annealing on the mechanical behaviour and biodegradability of a poly(3-hydroxybutyrate) and poly(ethylene-co-methyl-acrylate-co-glycidyl-methacrylate)blend. Polym Int. 2014;63(6):1085–1093. doi: 10.1002/pi.4616
LinK-W, LanC-H, SunY-M.Poly[(R)3-hydroxybutyrate] (PHB)/poly(l-lactic acid) (PLLA) blends with poly(PHB/PLLA urethane) as a compatibilizer. Polym Degrad Stab2016;134:30–40. doi: 10.1016/j.polymdegradstab.2016.09.017
21.
D'AmicoDA, Iglesias MontesML, ManfrediLB, Fully bio-based and biodegradable polylactic acid/poly(3-hydroxybutirate) blends: use of a common plasticizer as performance improvement strategy. Polym Test2016;49:22–28. doi: 10.1016/j.polymertesting.2015.11.004
GraupnerN, MüssigJ.A comparison of the mechanical characteristics of kenaf and lyocell fibre reinforced poly(lactic acid) (PLA) and poly(3-hydroxybutyrate) (PHB) composites. Compos A Appl Sci Manuf. 2011;42(12):2010–2019. doi: 10.1016/j.compositesa.2011.09.007
25.
SignoriF, ColtelliM-B, BroncoS.Thermal degradation of poly(lactic acid) (PLA) and poly(butylene adipate-co-terephthalate) (PBAT) and their blends upon melt processing. Polym Degrad Stab. 2009;94(1):74–82. doi: 10.1016/j.polymdegradstab.2008.10.004
26.
CarlsonD, NieL, NarayanR, Maleation of polylactide (PLA) by reactive extrusion. J Appl Polym Sci. 1999;72(4):477–485. doi: 10.1002/(SICI)1097-4628(19990425)72:4<477::AID-APP3>3.0.CO;2-Q
27.
BaiardoM, FrisoniG, ScandolaM, Thermal and mechanical properties of plasticized poly (L-lactic acid). J Appl Polym Sci. 2003;90(7):1731–1738. doi: 10.1002/app.12549
28.
GuoW, YangB, XiaR, Three-dimensional simulation of the shrinkage behavior of injection-molded poly lactic acid (PLA): effects of temperature, shear rate and part thickness. J Res Update Polym Sci. 2013;2(3):168–173.
29.
TontowiAE, ChildsT.Density prediction of crystalline polymer sintered parts at various powder bed temperatures. Rapid Prototyp J. 2001;7(3):180–184. doi: 10.1108/13552540110395637
30.
TorresJ, CoteloJ, KarlJ, Mechanical property optimization of FDM PLA in shear with multiple objectives. Jom. 2015;67(5):1183–1193. doi: 10.1007/s11837-015-1367-y
31.
PlymillA, MinneciR, GreeleyDA, Graphene and carbon nanotube PLA composite feedstock development for fused deposition modeling. 2016.
32.
ParkSD, TodoM, ArakawaK, Effect of crystallinity and loading-rate on mode I fracture behavior of poly (lactic acid). Polym. 2006;47(4):1357–1363. doi: 10.1016/j.polymer.2005.12.046
33.
TsujiH, IkadaY.Properties and morphologies of poly (L-lactide): 1. Annealing condition effects on properties and morphologies of poly (L-lactide). Polym. 1995;36(14):2709–2716. doi: 10.1016/0032-3861(95)93647-5