High density polyethylene pipes exposed in fire spot need to be assessed properly to assure safety operation. In this essay, thermal aging experiments were conducted to gain specimen containing thermal damage. Changes in mechanical properties and microstructure have been investigated by means of various characterisation analyses. The effect of exposure temperature, heat duration time, and cooling method on the mechanical properties were studied, respectively. Analysis results revealed that the effect on the mechanical properties is the consequence of interaction between annealing and heat damage. The results of oxidative induction time experiments, in accordance with attenuated total reflectance Fourier transform infrared spectroscopy analysis, indicated the consumption and migration of antioxidants. On the basis of practice and research, safety assessment procedure and method of high density polyethylene pipe after fire was proposed.
RosatoDV, RosatoMG. Concise encyclopedia of plastics. New York: Springer Science & Business Media; 2012.
4.
FrankA, PinterG, LangR. Prediction of the remaining lifetime of polyethylene pipes after up to 30 years in use. Polym Test.2009;28:737–745. doi: 10.1016/j.polymertesting.2009.06.004
5.
ElmeguenniM, Naït-AbdelazizM, ZaïriF, Fracture characterization of high-density polyethylene pipe materials using the J-integral and the essential work of fracture. Int J Fract.2013;183:119–133. doi: 10.1007/s10704-013-9848-x
6.
ChaouiK, KhelifR, ZeghibN, Failure analysis of polyethylene gas pipes. In: Safety, reliability and risks associated with water, oil and gas pipelines. Dordrecht: Springer; 2008. p. 131–163.
7.
DmytrakhI. Corrosion fatigue cracking and failure risk assessment of pipelines. In: Safety, reliability and risks associated with water, oil and gas pipelines. Dordrecht: Springer; 2008. p. 99–113. DOI:10.1007/978-1-4020-6526-2_6.
API 579. Recommended practice for fitness-for-service.
10.
AndersonTL, OsageDA. API 579: a comprehensive fitness-for-service guide. Int J Pressure Vessels Pip. 2000;77:953–963. doi: 10.1016/S0308-0161(01)00018-7
11.
KikuchiT, KuriharaT, NishikawaT, FFS Assessment for material degradation due to fire damage of pressure equipment. In: ASME 2013 pressure vessels and piping conference. American Society of Mechanical Engineers; 2013. V007T007A029-V007T007A029.
12.
ChenX, AiZ, FanZ, Integrity assessment of pressure vessels and pipelines under fire accident environment. In ASME 2012 Pressure vessels and piping conference. American Society of Mechanical Engineers; 2012. p. 497–505.
13.
IfwarsonM. Life-time of polyethylene pipes under pressure and exposure to high temperatures. Kunstst Ger Plast.1989;79:525–529.
14.
CelinaM, GillenKT, AssinkR. Accelerated aging and lifetime prediction: review of non-Arrhenius behaviour due to two competing processes. Polym Degrad Stab.2005;90:395–404. doi: 10.1016/j.polymdegradstab.2005.05.004
15.
HoàngEM, LoweD. Lifetime prediction of a blue PE100 water pipe. Polym Degrad Stab.2008;93:1496–1503. doi: 10.1016/j.polymdegradstab.2008.05.008
16.
LiM, HsuanYG. Temperature and pressure effects on the degradation of polypropylene tape yarns – depletion of antioxidants. Geotextiles Geomembr. 2004;22:511–530. doi: 10.1016/j.geotexmem.2004.06.001
17.
MasciaL. Polymers in industry from A to Z: a concise encyclopedia. Weinheim: John Wiley & Sons; 2012.
18.
MarkJE. Physical properties of polymers handbook. New York: Springer; 2007.
19.
ISO 527. Plastics – Determination of tensile properties.
20.
ISO 179. Plastics – Determination of charpy impact properties.
21.
RaviS, TakahashiK. Toughening mechanisms in annealed high density polyethylene under impact. Polym Eng Sci.2002;42:2146–2155. doi: 10.1002/pen.11104
22.
KrishnaswamyRK. Analysis of ductile and brittle failures from creep rupture testing of high-density polyethylene (HDPE) pipes. Polymer. 2005;46:11664–11672. doi: 10.1016/j.polymer.2005.09.084
23.
YoungRJ, LovellPA. Introduction to polymers. London: Chapman & Hall; 1991.
24.
NittaK-H, KuriyagawaM. Application of catastrophe theory to neck initiation of metallocene-catalyzed high-density polyethylene. Polym J.2012;44:245–251. doi: 10.1038/pj.2011.119
25.
PainterPC, ColemanMM. Fundamentals of polymer science: an introductory text. Florida: Technomic; 1994.
26.
MillsN. Plastics: microstructure and engineering applications. London: Butterworth-Heinemann; 2005.
BellamyL. The infra-red spectra of complex molecules. London: Springer Science & Business Media; 2013.
29.
FanconiBM, DeVriesKL, SmithRH. Free radicals and new end groups resulting from chain scission: 2. Mechanical degradation of polyethylene. Polymer. 1982;23:1027–1033. doi: 10.1016/0032-3861(82)90403-7
30.
ZanasiT, FabbriE, PilatiF. Qualification of pipe-grade HDPEs: Part I, development of a suitable accelerated ageing method. Polym Test.2009;28:96–102. doi: 10.1016/j.polymertesting.2008.11.006
31.
GeddeU, TerseliusB, JanssonJ-F. A new method for the detection of thermal oxidation in polyethylene pipes. Polym Test.1981;2:85–101. doi: 10.1016/0142-9418(81)90027-1
32.
BrownR. Handbook of plastics test methods. Longman Scientific & Technical. New York: Wiley; 1988.
33.
KüpperL, GulmineJ, JanissekP, Attenuated total reflection infrared spectroscopy for micro-domain analysis of polyethylene samples after accelerated ageing within weathering chambers. Vib Spectrosc. 2004;34:63–72. doi: 10.1016/j.vibspec.2003.05.002
34.
LundbäckM, HedenqvistM, MattozziA, Migration of phenolic antioxidants from linear and branched polyethylene. Polym Degrad Stab.2006;91:1571–1580. doi: 10.1016/j.polymdegradstab.2005.09.008
35.
HedesiuC, DemcoDE, KleppingerR, The effect of temperature and annealing on the phase composition, molecular mobility and the thickness of domains in high-density polyethylene. Polymer. 2007;48:763–777. doi: 10.1016/j.polymer.2006.12.019
36.
SeguelaR. Critical review of the molecular topology of semicrystalline polymers: the origin and assessment of intercrystalline tie molecules and chain entanglements. J Polym Sci Part B: Polym Phys.2005;43:1729–1748. doi: 10.1002/polb.20414
37.
HannonM. Microscopic aspects of brittle failure of polyethylene at stress below the yield stress. J Appl Polym Sci.1974;18:3761–3767. doi: 10.1002/app.1974.070181221