In this study, the refill friction stir processing (RFSP) method was utilised to repair a exit-hole defect located at the end of the friction stir welding (FSW) joints in 7475 aluminium alloy plate. The morphology, macroscopic defects, and mechanical properties of the repaired joints were investigated. The results demonstrate that the exit-hole was successfully refilled after RFSP. Material flow caused the refill voids, annular grooves, and un-stirred material defects. The maximum strength reached 415 Mpa, equal to 105% of the base defect-free weld. The mechanical properties of repaired joint were largely influenced by the stir zone (SZ) boundary and un-stirred material defects.
ThomasWM, NicholasED.Friction stir welding for the transportation industries. Mater Des. 1997;18(4):269–273. doi:10.1016/S0261-3069(97)00062-9
2.
SezhianMV, GiridharanK, PushpanathanDP, . Microstructural and mechanical behaviors of friction stir welded dissimilar AA6082-AA7075 joints. Adv Mater Sci Eng. 2021;2021:1–13. doi:10.1155/2021/4113895
3.
NavukkarasanAPR, SundaramKS, SastryCC, . Experimental investigation of dry and cryogenic friction stir welding of AA7075 aluminium alloy. Adv Mater Sci Eng. 2021;2021:1–21. doi:10.1155/2021/9961590
4.
LezaackMB, SimarA.Avoiding abnormal grain growth in thick 7XXX aluminium alloy friction stir welds during T6 post heat treatments. Mater Sci Eng A-Struct Mater Prop Microstruct Process. 2021;807:140901. doi:10.1016/j.msea.2021.140901
5.
AgilanM, PhanikumarG, SivakumarD.Tensile behaviour and microstructure evolution in friction stir welded 2195–2219 dissimilar aluminium alloy joints. Weld World. 2022;66(2):227–237. doi:10.1007/s40194-021-01217-w
ParidaB, PalS.An investigation to find an appropriate starting position and elimination of pin hole defect in FSW for maximizing the joint length. Int J Adv Manuf Technol. 2016;87(9–12):2889–2900. doi:10.1007/s00170-016-8555-y
8.
LiDF, WangXJ, ZhaoZL.Grain orientation and texture analysis of 6082 aluminum alloy friction plug welded joints. J Mater Res Technol-JMRT. 2022;18:1763–1771. doi:10.1016/j.jmrt.2022.03.085
9.
LiDF, WangXJ.The effect of plug rotation speed on micro-structure of nugget zone of friction plug repair welding joint for 6082 aluminum alloy. Materials (Basel). 2021 Sep;14(18):5287. doi:10.3390/ma14185287
10.
SunZP, YangXQ, LiSX.Characteristics of friction plug joints for AA2219-T87 FSW welds. Materials (Basel). 2022;15(4):1525. doi:10.3390/ma15041525
11.
HuangYX, HanB, TianY, . New technique of filling friction stir welding. Sci Technol Weld Joining. 2011;16(6):497–501. doi:10.1179/1362171811Y.0000000032
12.
HuangYX, HanB, LvSX, . Interface behaviours and mechanical properties of filling friction stir weld joining AA 2219. Sci Technol Weld Joining. 2012 Apr;17(3): 225–230. doi:10.1179/1362171811Y.0000000100
13.
GhavimiAH, AboutalebiMR, SeyedeinSH.Exit-hole repairing in friction stir welding of AA5456 pipe using consumable pin. Mater Manuf Process. 2020;35(11): 1240–1250. doi:10.1080/10426914.2020.1772491
14.
DengL, LiS, KeL, . Microstructure and fracture behavior of refill friction stir spot welded joints of AA2024 using a novel refill technique. Metals (Basel). 2019;9(3):286. doi:10.3390/met9030286
15.
JiS, MengX, ZengY, . New technique for eliminating keyhole by active-passive filling friction stir repairing. Mater Des. 2016;97:175–182. doi:10.1016/j.matdes.2016.02.088
16.
JiSD, MengXC, . Microstructures and mechanical properties of 7N01-T4 aluminum alloy joints by active-passive filling friction stir repairing. Mater Sci Eng A. 2016;664:94–102. doi:10.1016/j.msea.2016.03.131
17.
MugadaKK, AdepuK.Influence of tool shoulder end features on friction stir weld characteristics of Al-Mg-Si alloy. Int J Adv Manuf Technol. 2018;99(5–8): 1553–1566. doi:10.1007/s00170-018-2602-9
18.
JacquinD, GuillemotG.A review of microstructural changes occurring during FSW in aluminium alloys and their modelling. J Mater Process Technol. 2021;288: 116706. doi:10.1016/j.jmatprotec.2020.116706
19.
ZhangC, HuangG, CaoY, . Characterizations of microstructure, crystallographic texture and mechanical properties of dissimilar friction stir welding joints for AA2024 and AA7075 under different tool shoulder end profiles. Mater Today Commun. 2020;25:101435. doi:10.1016/j.mtcomm.2020.101435
20.
MehtaK, AstaritaA, CarloneP, . Investigation of exit-hole repairing on dissimilar aluminum-copper friction stir welded joints. J Mater Res Technol. 2021;13: 2180–2193. doi:10.1016/j.jmrt.2021.06.019
21.
MehtaKP, PatelR, VyasH, . Repairing of exit-hole in dissimilar Al-Mg friction stir welding: process and microstructural pattern. Manuf Lett. 2020;23:67–70. doi:10.1016/j.mfglet.2020.01.002
22.
YuanT, KangS, JiangX, . Mechanical properties and failure analysis of refill friction stir spot-welded 5052/2A12 joints. Mater Sci Technol. 2022;38(18):1573–1584. doi:10.1080/02670836.2022.2093001
23.
LiuYH, BiJY, YangDY.Microstructure and mechanical properties of refill friction stir spot welded 6005 Al alloy butt joints. Jom. 2022;74(7):2838–2845. doi:10.1007/s11837-022-05341-w
24.
ZhangD, XiongJT, MaYK, . Study of microstructure characteristics and corrosion behavior of 2524 aluminum alloy RFSSW joint. Mater Charact. 2022;190; doi:10.1016/j.matchar.2022.112057
ReimannM, GoebelJ, dos SantosJF.Microstructure and mechanical properties of keyhole repair welds in AA 7075-T651 using refill friction stir spot welding. Mater Des. 2017;132:283–294. doi:10.1016/j.matdes.2017.07.013
27.
ReimannM, GoebelJ, GartnerTM, . Refilling termination hole in AA 2198–T851 by refill friction stir spot welding. J Mater Process Technol. 2017; 245:157–166. doi:10.1016/j.jmatprotec.2017.02.025
28.
HanY, JiangXQ, YuanT, . Material flow and microstructure evolution on the flow path of friction stir lap welded aluminium alloy. Sci Technol Weld Joining. 2023;28(1):72–80. doi:10.1080/13621718.2022.2117531
29.
ChaiP, WangY.Effect of rotational speed on microstructure and mechanical properties of 2060 aluminum alloy RFSSW joint. Met Mater-Int. 2019;25(6):1574–1585. doi:10.1007/s12540-019-00291-6
30.
WangY, ChaiP, MaH, . Formation mechanism and fracture behavior in extra-filling refill friction stir spot weld for Al–Cu–Mg aluminum alloy. J Mater Sci. 2020;55(1):358–374. doi:10.1007/s10853-019-03940-8
31.
ZhaoYQ, LiuHJ, ChenSX, . Effects of sleeve plunge depth on microstructures and mechanical properties of friction spot welded alclad 7B04-T74 aluminum alloy. Mater Des. 2014;62:40–46. doi:10.1016/j.matdes.2014.05.012
32.
ChenSJ, ShiJX, YuanT, . Improvement of refill friction stir spot welds by auxiliary material addition. Mater Sci Technol. 2020;36(3):367–374. doi:10.1080/02670836.2019.1705588
33.
KubitA, TrzepiecinskiT.A fully coupled thermo-mechanical numerical modelling of the refill friction stir spot welding process in Alclad 7075-T6 aluminium alloy sheets. Arch Civ Mech Eng. 2020;20(4):117. doi:10.1007/s43452-020-00127-w